Purification auxiliary material of microcrystalline graphite and production method thereof

A technology of microcrystalline graphite and pure auxiliary materials, applied in the field of microcrystalline graphite purification auxiliary materials and its production, can solve the problems of limited application range, low purification degree of purification auxiliary materials, etc., and achieve the effect of wide application range and simple formula

Inactive Publication Date: 2015-04-08
林前锋
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention proposes a microcrystalline graphite purification auxiliary material and a production method thereof, which solves the defect that the application range of the purification auxiliary material is limited due to the low degree of purification of the purification auxiliary material in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A microcrystalline graphite purification auxiliary material is composed of the following ingredients in weight percentage: 40% of microcrystalline graphite, 20% of hydrochloric acid, 18% of phosphoric acid and 22% of ammonium fluoride. Among them, the concentration of hydrochloric acid is 36%, the density is 1.19; the concentration of phosphoric acid is 85%, the density is 1.69; the density of ammonium fluoride is 1.11.

[0017] A preparation method of microcrystalline graphite purification auxiliary materials, which comprises the following steps: (1) selecting microcrystalline graphite, hydrochloric acid, phosphoric acid and ammonium fluoride according to weight percentage; (2) sequentially mixing microcrystalline graphite with hydrochloric acid, phosphoric acid and fluorinated (3) Place the uniformly mixed mixture in an environment with a temperature of 60° C., dry the mixture, and cool to normal temperature to obtain the microcrystalline graphite purification auxiliar...

Embodiment 2

[0020] A microcrystalline graphite purification auxiliary material is composed of the following ingredients in weight percentage: 50% of microcrystalline graphite, 15% of hydrochloric acid, 12% of phosphoric acid, and 23% of ammonium fluoride. Among them, the concentration of hydrochloric acid is 36%, the density is 1.19; the concentration of phosphoric acid is 85%, the density is 1.69; the density of ammonium fluoride is 1.11.

[0021] The preparation method of the microcrystalline graphite purification auxiliary material comprises the following steps: (1) selecting microcrystalline graphite, hydrochloric acid, phosphoric acid and ammonium fluoride according to weight percentage; (2) sequentially mixing microcrystalline graphite with hydrochloric acid, phosphoric acid and ammonium fluoride Mixing; (3) placing the uniformly mixed mixture in an environment with a temperature of 70° C., drying the mixture, and cooling to normal temperature to obtain the microcrystalline graphite ...

Embodiment 3

[0024] A microcrystalline graphite purification auxiliary material is composed of the following ingredients in weight percentage: 45% of microcrystalline graphite, 25% of hydrochloric acid, 15% of phosphoric acid, and 15% of ammonium fluoride. Among them, the concentration of hydrochloric acid is 36%, the density is 1.19; the concentration of phosphoric acid is 85%, the density is 1.69; the density of ammonium fluoride is 1.11.

[0025] The preparation method of the microcrystalline graphite purification auxiliary material comprises the following steps: (1) selecting microcrystalline graphite, hydrochloric acid, phosphoric acid and ammonium fluoride according to weight percentage; (2) sequentially mixing microcrystalline graphite with hydrochloric acid, phosphoric acid and ammonium fluoride Mixing; (3) placing the uniformly mixed mixture in an environment with a temperature of 80° C., drying the mixture, and cooling to normal temperature to obtain the microcrystalline graphite ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a purification auxiliary material of microcrystalline graphite and a production method thereof. The purification auxiliary material of microcrystalline graphite is composed of the following materials in percentage by weight: 40-50% of microcrystalline graphite, 15-25% of hydrochloric acid, 12-18% of phosphoric acid and 15-30% of ammonium fluoride. The production method of the purification auxiliary material of microcrystalline graphite comprises the following steps: (1) selecting microcrystalline graphite, hydrochloric acid, phosphoric acid and ammonium fluoride according to the percentage by weight; (2) sequentially mixing microcrystalline graphite with hydrochloric acid, phosphoric acid and ammonium fluoride; and (3) placing the uniformly-mixed mixture in an environment at a temperature of 60-100 DEG C, drying the mixture, and cooling to a room temperature, thereby obtaining the purification auxiliary material of microcrystalline graphite. The purification auxiliary material of microcrystalline graphite and the production method thereof disclosed by the invention are simple in formula, achieve the requirement of high purity, and are wide in application range.

Description

technical field [0001] The invention relates to a purification auxiliary material, in particular to a microcrystalline graphite purification auxiliary material and a preparation method thereof. Background technique [0002] Graphite is one of the most important simple substances of carbon, which is formed at high temperature. It is abundant in nature and widely distributed in mineral deposits. Graphite has a typical layered structure, carbon atoms are arranged in layers, each carbon is connected to three adjacent carbons at equal distances, and the carbons in each layer are arranged in a six-point ring. The carbon-carbon distance between the layers is 0.142nm, and the interlayer carbon-carbon distance is 0.340nm. The carbons in the layers are connected by covalent bonds, which also have the properties of some metal bonds, and the interlayers are molecular bonds. This difference in chemical bonds leads to graphite The physical properties have obvious anisotropy and conductiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/04
Inventor 林前锋
Owner 林前锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com