Special impact-resistant aging-resistant material for bumper

An anti-aging and bumper technology, which is applied in the field of chemical polymer materials, can solve the problems of poor impact and corrosion resistance and easy aging, and achieve the effect of not easy to age, good impact and corrosion resistance, and low density

Inactive Publication Date: 2015-05-06
南京中配橡塑制品有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a special impact-resistant and aging-resistant bumper material to solve the problem that the bumper material in the prior art has relatively poor impact and corrosion resistance and is easy to age under wind and sun.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The impact-resistant and aging-resistant bumper special material is composed of the following raw materials in mass fractions:

[0017] 90 parts of polypropylene; 8 parts of EPDM rubber; 3 parts of nano rubber; 5 parts of vulcanizing agent; 6 parts of styrene-butadiene copolymer; 1 part of antioxidant 1010; 18 parts of mineral filler and 1 part of foaming agent share.

Embodiment 2

[0019] The impact-resistant and aging-resistant bumper special material is composed of the following raw materials in mass fractions:

[0020] 95 parts of polypropylene; 8 parts of EPDM rubber; 3 parts of nano rubber; 8 parts of vulcanizing agent; 7 parts of styrene-butadiene copolymer; 2 parts of antioxidant 1010; 20 parts of mineral filler and 2 parts of foaming agent share.

[0021] From the above description, it can be seen that the above-mentioned embodiments of the present invention have achieved the following technical effects:

[0022] The invention provides a special impact-resistant and aging-resistant bumper material, which not only has good impact-resistant and corrosion-resistant properties, but also has good rigidity and strength, and is not easy to age. The density of polypropylene used is small, which is in line with the current development of lightweight automobiles .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special impact-resistant aging-resistant material for a bumper. The special impact-resistant aging-resistant material is prepared from the following raw materials in parts by mass: 88-95 parts of polypropylene, 8-10 parts of ethylene-propylene diene copolymer rubber, 2-3 parts of nanometer rubber, 3-8 parts of a vulcanizing agent, 5-8 parts of a styrene-butadiene copolymer, 0.1-2 parts of an antioxidant 1010, 18-22 parts of a mineral filler and 1-2 parts of a foaming agent. The special material disclosed by the invention has the beneficial effects that the special material has high impact resistance, corrosion resistance, high rigidity and strength and is difficult to age, the used polypropylene is low in density, and the development of automobile lightweight at the present stage is met.

Description

technical field [0001] The invention relates to the technical field of chemical polymer materials, in particular to an impact-resistant and aging-resistant bumper special material. Background technique [0002] In addition to the function of absorbing collision energy and protecting pedestrians, the automobile bumper is mainly used as an exterior decoration, so the requirements for its appearance, impact resistance and corrosion resistance are relatively high. [0003] In recent years, the demand for lightweight automobiles has become higher and higher, and the call for replacing steel with plastic is also increasing. Therefore, the demand for replacing steel with plastic for bumper materials has become increasingly obvious. However, today's bumper materials have relatively high impact and corrosion resistance. Poor, easy to age under wind and sun. Contents of the invention [0004] The purpose of the present invention is to provide a special impact-resistant and aging-re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/16C08L21/00C08L25/10C08J9/04
CPCC08L23/12C08J9/04C08J2323/12C08L2201/08C08L2205/02C08L2205/035C08L23/16C08L21/00C08L25/10C08K5/1345
Inventor 陈永亮
Owner 南京中配橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products