A kind of production process of superabsorbent silk non-woven fabric
A technology of silk non-woven fabric and production process, which is applied in the treatment of non-woven fabrics, textiles, papermaking, and textile materials. It can solve the problems of poor water absorption of non-woven fabrics, and achieve the effect of moisturizing, softness, comfort and improved water absorption.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] Such as figure 1 and figure 2 As shown, the present embodiment provides silk non-woven fabric production process, and this production process comprises successively:
[0040] S1, the hydrophilic step, the hydrophilic step processes the silk fiber by soaking, and then obtains the silk fiber after drying;
[0041] S2. The non-woven fabric forming step, however, in the non-woven fabric forming step, water-absorbent silk fibers are produced through a spunlace process to obtain a highly water-absorbent silk non-woven fabric. In addition, the silk fiber is mixed with viscose, polyester or polypropylene fiber at a weight ratio of 1:0.01 before entering the spunlace process.
[0042] The concrete steps of described soaking method comprise:
[0043] S11. Pour the hydrophilic agent solution prepared according to the weight ratio of 20% amino silicone oil solution and deionized water into the immersion tank. In this example, a hydrophilizing agent solution prepared by adding ...
Embodiment 2
[0049] Such as figure 1 and figure 2 As shown, the present embodiment provides silk non-woven fabric production process, and this production process comprises successively:
[0050] S1, the hydrophilic step, the hydrophilic step processes the silk fiber by soaking, and then obtains the silk fiber after drying;
[0051] S2. The non-woven fabric forming step, however, in the non-woven fabric forming step, water-absorbent silk fibers are produced through a spunlace process to obtain a highly water-absorbent silk non-woven fabric. In addition, the silk fiber is mixed with viscose, polyester or polypropylene fiber at a weight ratio of 1:0.32 before entering the spunlace process.
[0052] The concrete steps of described soaking method comprise:
[0053] S11. Pour the hydrophilic agent solution prepared according to the weight ratio of amino silicone oil solution with a mass concentration of 26% to deionized water of 1:26 into the soaking tank. In this embodiment, use 3000 kg of ...
Embodiment 3
[0059] Such as figure 1 and figure 2 As shown, the present embodiment provides silk non-woven fabric production process, and this production process comprises successively:
[0060] S1, the hydrophilic step, the hydrophilic step processes the silk fiber by soaking, and then obtains the silk fiber after drying;
[0061] S2. The non-woven fabric forming step, however, in the non-woven fabric forming step, water-absorbent silk fibers are produced through a spunlace process to obtain a highly water-absorbent silk non-woven fabric. In addition, the silk fiber is mixed with viscose, polyester or polypropylene fiber at a weight ratio of 1:0.60 before entering the spunlace process.
[0062] The concrete steps of described soaking method comprise:
[0063] S11. Pour the hydrophilic agent solution prepared according to the weight ratio of amino silicone oil solution with a mass concentration of 35% to deionized water of 1:30 into the soaking tank. In this embodiment, use 3000 kg of ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| length | aaaaa | aaaaa |
| length | aaaaa | aaaaa |
| length | aaaaa | aaaaa |