Welding technology of aluminum alloy ceiling used for subway compartment

A welding process and technology of aluminum alloy, applied in the field of aluminum alloy, can solve the problems of high comprehensive cost, affecting the qualified rate of products, affecting assembly, etc., and achieve the effect of improving the qualified rate of products, optimizing welding process parameters, and reducing welding man-hours.

Active Publication Date: 2015-05-20
辽宁忠旺铝合金精深加工有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The welding process of the large parts of the aluminum alloy subway roof has high requirements on the assembly of the workpiece and the welding process. A slight deviation may cause serious product deformation, affect subsequent assembly, poor weld quality, and affect the product qualification rate.
In addition, the conventional welding process of large parts of the aluminum alloy subway roof still has problems such as complicated procedures and high overall cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding technology of aluminum alloy ceiling used for subway compartment
  • Welding technology of aluminum alloy ceiling used for subway compartment
  • Welding technology of aluminum alloy ceiling used for subway compartment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] like Figure 1-5 As shown, the car body roof of the subway in this embodiment is welded by five roof panels A1, A2, A3, A4, and A5 and two roof side beams B1 and B2.

[0034] In this embodiment, the roof of the car body is welded in two stages. First, each roof panel is welded, and then the roof side beam and the roof panel assembly are welded, as follows:

[0035] (1) Roof plate welding:

[0036] 1), material selection: select the above-mentioned roof panel as required, and the roof panel is a hollow profile with a single length of 16-20m, a width of 0.3-0.6mm, and a wall thickness of 2-3mm;

[0037] 2) Formal assembly: set the selected five roof panels side by side on the formal welding tool;

[0038] 3) Form-fitting welding: double-machine and double-wire linkage welding is used to weld the roof panels of the formal-fitting assembly. First, welding seams 2 and 3 are welded at the same time, and then welds 1 and 4 are welded at the same time;

[0039] 4) Reverse as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a welding technology of an aluminum alloy ceiling used for a subway compartment. The ceiling is formed by welding five subway roof plates and two subway roof edge beams, and the subway roof plates are hollow profiles, wherein the length of each subway roof plate ranges from 16 m to 20 m, the width of each subway roof plate ranges from 0.3 mm to 0.6 mm, and the wall thickness of each subway roof plate ranges from 2 mm to 3 mm. In the welding process, all the subway roof plates are firstly welded, and then the subway roof edge beams and a subway roof plate assembly are welded; the subway roof plates are welded through double-wire double-machine linkage welding, firstly, forward installation welding is performed, and then reverse installation welding is performed; the subway roof edge beams and the subway roof plate assembly are welded through single-wire double-machine linkage welding, wherein forward installation welding and reverse installation welding are also performed in sequence. The material of welded components, the steps and the technology are improved, the using requirements for the quality and size of product weld joints are completely met, the qualified rate of the product is substantially increased, and meanwhile welding working hours are reduced.

Description

technical field [0001] The invention belongs to the field of aluminum alloys, and relates to an aluminum alloy component for a subway, in particular to a welding process for an aluminum alloy ceiling for a subway carriage. Background technique [0002] The welding process of the large parts of the aluminum alloy subway car roof has high requirements on the assembly of the workpiece and the welding process. A slight deviation may cause serious product deformation, affect subsequent assembly, poor weld quality, and affect the product qualification rate. In addition, the conventional welding process of large parts of the aluminum alloy subway roof still has problems such as complicated procedures and high overall costs. [0003] In order to improve the welding seam quality and overall size requirements of our subway car roof products, improve the product qualification rate, and reduce the manufacturing man-hours, a new subway car roof welding process is hereby redesigned. Con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/02
CPCB23K9/02
Inventor 马青梅韩文宇宋宁高雨
Owner 辽宁忠旺铝合金精深加工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com