A kind of waterproof roll material and preparation method thereof

A waterproof membrane and membrane layer technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve problems such as hair-like cracks, surface loss, micro-cracks, etc., to improve weather resistance and durability Excellent effect on aging performance, photoaging suppression, and weather resistance

Active Publication Date: 2016-06-15
苏州东方雨虹建筑材料有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at problems such as fading, discoloration, surface loss of luster, even microcracks and hair-like cracks in existing TPO coil products, and provides a waterproof coil and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterproof roll material and preparation method thereof
  • A kind of waterproof roll material and preparation method thereof
  • A kind of waterproof roll material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This embodiment provides a waterproof membrane, which is a three-layer structure, the upper surface and the lower surface are both TPO membrane layers; the middle is a reinforced polyester mesh cloth, the warp fineness of the mesh cloth is 1000D, and the weft yarn The fineness is 1000D, and the total thickness of the product is 1.50mm.

[0045] The components and parts by weight of the upper surface and the lower surface TPO membrane layer are shown in Table 1:

[0046] Components and parts by weight of the TPO membrane layer of Table 1, Example 1

[0047] raw material name

Upper surface TPO layer

Lower surface TPO layer

TPO

100

100

filler

20

25

Reinforcing agent

2

1

light shielding agent

3

1

paint

0

0.5

antioxidant

3.0

2.0

light stabilizer

1.5

1.0

UV absorber

1.5

1.0

[0048] The additives include antioxidants, light stabiliz...

Embodiment 2

[0057] This embodiment provides a waterproof membrane, which is a three-layer structure, the upper surface and the lower surface are both TPO membrane layers; the middle is a reinforced polyester mesh cloth, the warp fineness of the mesh cloth is 1000D, and the weft yarn The fineness is 1000D, and the total thickness of the product is 1.50mm.

[0058] The components and parts by weight of the upper surface and the lower surface TPO membrane layer are shown in Table 3:

[0059] Components and parts by weight of the TPO membrane layer of table 3, embodiment 2

[0060]

[0061] The granulation auxiliary agent includes an antioxidant, a light stabilizer and an ultraviolet absorber, and the particle size of the granulation auxiliary agent is 0.5mm.

[0062] The main antioxidant is IRGANOX245, the auxiliary antioxidant is IRGAFOS168, wherein IRGANOX245:IRGAFOS168=1:1 (mass ratio), the light stabilizer is a combination of high molecular weight light stabilizer Chimassorb2020 and ...

Embodiment 3

[0070] This embodiment provides a waterproof membrane, the preparation method of which is similar to that of embodiment 2, the difference between it and embodiment 2 is that the melt extrusion temperature of the screw extruder is 200°C; the operating temperature of the three-roll calender is 80°C. The components and parts by weight of each layer are shown in Table 5:

[0071] Components and parts by weight of the TPO membrane layer of Table 5 Example 3

[0072]

[0073] The granulation auxiliary agent includes an antioxidant, a light stabilizer and an ultraviolet absorber, and the particle size of the granulation auxiliary agent is 1.0 mm.

[0074] The main antioxidant is IRGANOX245, the auxiliary antioxidant is IRGAFOS168, wherein IRGANOX245:IRGAFOS168=1:2 (mass ratio), the light stabilizer is a combination of high molecular weight light stabilizer Chimassorb2020 and low molecular weight light stabilizer Tinuvin770, of which Chimassorb2020 :Tinuvin770=1:1 (mass ratio), T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a waterproof roll and a preparation method thereof, belongs to the technical field of polymer waterproof rolls, and can solve the problems of color fading, color changing, surface staining, microcracking, hairline crack and the like of a conventional TPO (thermoplastic polyolefin) roll product in the use process. The waterproof roll comprises a TPO roll layer, wherein raw materials of the TPO roll layer comprise polymeric TPO resin and a granular auxiliary; the granular auxiliary comprises an antioxidant, a light stabilizer and an ultraviolet light absorber, and the grain size of the granular auxiliary is 0.5-1.5 mm. The waterproof roll has excellent weather fastness, ageing resistance, waterproof function and fastness and reliability in construction.

Description

technical field [0001] The invention belongs to the technical field of polymer waterproof coiled material, and in particular relates to a waterproof coiled material and a preparation method thereof. Background technique [0002] Since the 1990s, thermoplastic polyolefin (hereinafter referred to as TPO) waterproof membrane has developed into the most common single-layer waterproofing for low-slope roofs due to its excellent mechanical properties, welding construction properties, reflection properties and other comprehensive properties. Coil. In our country, with the acceleration of social and economic development, people put forward higher requirements for waterproof products in the construction field, not only requiring waterproof membranes to have excellent waterproof performance, but also requiring their aesthetics and safety. For this reason, TPO waterproof membrane, which represents the highest technology of single-ply roof waterproof membrane, is in a period of rapid g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B27/18B32B27/20B32B27/32B32B27/12B32B27/36
CPCB32B27/12B32B27/18B32B27/32B32B2307/306B32B2307/50B32B2307/552B32B2307/712B32B2419/06
Inventor 刘国刚李建军刘振华刘志维梁卫业
Owner 苏州东方雨虹建筑材料有限公司