Method for rolling titanium-steel clad plate in atmospheric environment

An atmospheric environment, clad plate technology, applied in metal rolling and other directions, can solve the problems that the quality of titanium steel clad plate products cannot be well guaranteed, cannot prevent the mutual diffusion of elements, and the coating metal does not have good ductility, etc. To achieve the effect of good combination effect, eliminate influence and reduce production cost

Active Publication Date: 2018-05-01
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can improve the bonding strength of the interface to a certain extent. However, due to the thin coating, elements such as titanium and iron can penetrate the coating under high temperature or long-term heating conditions and form brittle compounds at the interface, which cannot prevent the interdiffusion of elements. At the same time, due to the lack of good ductility of the coating metal, the problem of uneven interface state will be caused during the rolling process, resulting in the quality of the titanium-steel clad plate prepared by this method cannot be well guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] ① Prepare two steel plates with a size of 200×160×18mm, one titanium plate with a size of 160×120×20mm, one piece of copper foil with the same size as the titanium plate and a thickness of 50μm, and a size of 120×20×40mm and 200×20× There are two 40mm side frames each, wherein the material of the side plates is the same as that of the steel plate; a release agent is applied to the adjacent surfaces of the steel plate and the titanium plate, and the billets are assembled symmetrically in the order of steel plate / titanium plate / copper foil / steel plate, The side plate is arranged around the titanium plate and between two steel plates, and the gap between the steel plate and the side plate and the gap between the side plate and the side plate are welded to form a combined body to obtain a combined blank.

[0038] ②Put the prepared billet into the heating furnace and heat it to 980°C, and keep it warm for 6 hours;

[0039] ③Take out the combined billet that has completed the h...

Embodiment 2

[0042] ①Prepare two steel plates with specifications of 200×160×18mm, a titanium plate with a size of 160×120×20mm, a copper foil with the same size as the titanium plate and a thickness of 100μm, and a size of 120×20×40mm and 200×20× There are two 40mm side frames each, wherein the material of the side plates is the same as that of the steel plate; a release agent is applied to the adjacent surfaces of the steel plate and the titanium plate, and the billets are assembled symmetrically in the order of steel plate / titanium plate / copper foil / steel plate, The side plate is arranged around the titanium plate and between two steel plates, and the gap between the steel plate and the side plate and the gap between the side plate and the side plate are welded to form a combined body to obtain a combined blank.

[0043] ②Put the prepared billet into the heating furnace and heat it to 1000°C, and keep it warm for 6 hours;

[0044] ③Take out the combined billet that has completed the hea...

Embodiment 3

[0047] ①Prepare two steel plates with a size of 200×160×18mm, one titanium plate with a size of 160×120×20mm, one copper foil with the same size as the titanium plate and a thickness of 60μm, and a copper foil with a size of 120×20×40mm and 200×20× There are two 40mm side frames each, wherein the material of the side plates is the same as that of the steel plate; a release agent is applied to the adjacent surfaces of the steel plate and the titanium plate, and the billets are assembled symmetrically in the order of steel plate / titanium plate / copper foil / steel plate, The side plate is arranged around the titanium plate and between two steel plates, and the gap between the steel plate and the side plate and the gap between the side plate and the side plate are welded to form a combined body to obtain a combined blank.

[0048] ②Put the prepared billet into the heating furnace and heat it to 1050°C, and keep it warm for 5 hours;

[0049] ③Take out the combined billet that has com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of titanium clad steel plate preparing and processing, and particularly relates to a method for rolling a titanium clad steel plate in the atmospheric environment. The method comprises the following steps: a. assembling: symmetrically assembling according to the sequence of a steel plate, a titanium plate, a copper plate and a steel plate and welding so as to obtain a combined blank; b. heating: heating the combined blank at 950-1,050 DEG C for 2-6 h; c. rolling: rolling the heated combined blank for at least two times, wherein the total rolling deformation is larger than 90%; d. finishing: separating a titanium-steel interface to obtain the titanium clad steel plate. The method is simple in process, and can solve the problem of interface oxidation during the titanium clad steel plate preparing process; the obtained titanium clad steel plate is good in plate type and good in combining effect, and the combining strength is 200 MPa.

Description

technical field [0001] The invention belongs to the field of preparation and processing of titanium-steel clad plates, and in particular relates to a method for rolling titanium-steel clad plates in an atmospheric environment. Background technique [0002] Titanium has good physical, chemical and mechanical properties, but its smelting technology is complicated and the production cost is high, so the price of titanium is very expensive, which greatly limits the promotion and application of titanium. Combining titanium with other metals (such as steel, copper, aluminum, etc.) -Steel composite materials are widely used in chemical, petroleum and other industrial sectors because of their high strength, excellent corrosion resistance and significant economic benefits. [0003] At present, there are four main production methods of titanium-steel clad plates: explosive clad method, diffusion clad method, explosion-rolling and direct rolling method. The direct rolling method is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/38
CPCB21B1/38B21B2001/386
Inventor 彭琳李军杨柳栾佰峰于辉肖聪
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap