Flexible LED nail lacquer gel and preparing method thereof

A nail polish and flexible technology, applied in the field of flexible LED nail polish and its preparation, can solve problems such as easy brittleness, excessive adhesion, poor flexibility, etc., achieve moderate adhesion, avoid damage, and avoid organic solvent assistance peeling effect

Inactive Publication Date: 2015-09-23
QINGDAO UNIQUE PRODS DEV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of the existing LED nail polish on the market, such as poor flexibility, brittleness, excessive adhesion, and difficulty in peeling off from the nail, a flexible LED nail polish and its preparation method are provided, which have moderate adhesion and can meet Adhesive effect on nails, and it can be easily peeled off by hand directly, avoiding the use of organic solvents to assist peeling, and effectively avoiding the damage of nail remover to nails

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] 1. According to the following composition ratio (mass percentage content):

[0010] Urethane Acrylate 55%

[0011] Ethoxylated Trimethylolpropane Triacrylate 25%

[0012] Polyester acrylate 14%

[0013] 907 5%

[0014] Polyester modified silicone 1%

[0015] 2. Preparation method

[0016] Step 1 Weigh each component in proportion;

[0017] Step 2 Stir the above-mentioned weighed components evenly, and the speed of the mixer is 1000 rpm;

[0018] Step 3 Let it stand for defoaming and seal it.

[0019] Example 2

[0020] 1. According to the following composition ratio (mass percentage):

[0021] Urethane Acrylate 65%

[0022] Trimethylolpropane Triacrylate 30%

[0023] 184 4%

[0024] Polyether modified silicone 1%

[0025] 2. Preparation method

[0026] Step 1 Weigh each component in proportion;

[0027] Step 2 Stir the above-mentioned weighed components evenly, and the speed of the mixer is 1000 rpm;

[0028] Step 3 After standing still for defoaming, pac...

Embodiment 3

[0030] 1. According to the following composition ratio (mass percentage):

[0031] Polyester acrylate 40%

[0032] Urethane Acrylate 25%

[0033] Ethoxylated Pentaerythritol Tetraacrylate 30%

[0034] TPO 4%

[0035] Polyether modified silicone 1%

[0036] 2. Preparation method

[0037] Step 1 Weigh each component in proportion;

[0038] Step 2 Stir the above-mentioned weighed components evenly, and the speed of the mixer is 1000 rpm;

[0039] Step 3 After standing still for defoaming, package.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ink, in particular to flexible LED nail lacquer gel and a preparing method thereof. The flexible LED nail lacquer gel comprises, by mass, 20-80 percent of acrylic ester low polymer (including urethane acrylate, polyester acrylate, polyether acrylate and the like), 10-15 percent of acrylate monomer, 1-10 percent of photoinitiator and 0.1-5 percent of assistant. The attachment effect on fingernails can be achieved, the gel can be directly stripped off manually very easily, organic solvent auxiliary stripping is avoided, and the nails are effectively prevented from being injured by removing of nail lacquer.

Description

technical field [0001] The invention relates to the technical field of ink, in particular to a flexible LED nail polish and a preparation method thereof. Background technique [0002] Nail polish is a large category of products in the make-up series, which has the function of beautifying and modifying nails. Ordinary nail polish is a nail film-forming agent in which ester-soluble nitrocellulose is dissolved in a certain highly active ester-based solvent system. Left and right nitrocellulose, a small amount of oily solvents, camphor, titanium dioxide, and oil-soluble pigments. Nail polish forms a firm, glossy film on the nails. [0003] At present, there are many LED nail polish products on the market, but they are poor in flexibility, easy to be brittle, and have excessive adhesion, making it difficult to peel off from the nail. Contents of the invention [0004] Aiming at the problems of the existing LED nail polish on the market, such as poor flexibility, brittlen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/891A61K8/87A61K8/86A61K8/85A61K8/81A61Q3/02
Inventor 王红阚生东闫君
Owner QINGDAO UNIQUE PRODS DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com