A kind of deodorant toilet cover and preparation method thereof
A technology for deodorizing toilets and toilet lids, applied in the field of sanitary ware, can solve problems such as inability to remove, poor effect, and reduce the proportion of odors
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0018] A kind of deodorant toilet lid proposed by the present invention, its raw material comprises by weight: 50 parts of corncobs, 40 parts of straw powder, 45 parts of peanut shell powder, 30 parts of tea leaves, 15 parts of pomelo peel, 20 parts of rice bran, 40 parts of Bamboo wood powder, 8 parts of papermaking sludge, 10 parts of modified medical stone powder, 16 parts of porous calcium phosphate, 8 parts of mint, 18 parts of honeysuckle, 5 parts of clove, 5 parts of tourmaline powder, 2 parts of six-ring stone powder, 35 parts of ring Oxygen resin cement;
[0019] Wherein the preparation method of modified medical stone powder is as follows: After mixing 4 parts of medical stone powder, 2 parts of sweet potato starch, and 2 parts of aluminum oxide with water in parts by weight, dry, pulverize and sieve to obtain granular material A; A is heated to 350°C, kept for 1 hour, then heated to 580°C, held for 30 minutes, then heated to 650°C, held for 10 minutes, taken out and...
Embodiment 2
[0022] A kind of deodorant toilet lid proposed by the present invention, its raw material comprises by weight: 60 parts of corncobs, 30 parts of straw powder, 55 parts of peanut shell powder, 20 parts of tea leaves, 25 parts of pomelo peel, 10 parts of rice bran, 45 parts of Bamboo wood powder, 2 parts of papermaking sludge, 15 parts of modified medical stone powder, 8 parts of porous calcium phosphate, 12 parts of mint, 14 parts of honeysuckle, 8 parts of clove, 3 parts of tourmaline powder, 4 parts of six-ring stone powder, 30 parts of ring Oxygen resin cement;
[0023] Wherein the preparation method of the modified medical stone powder is as follows: after mixing 5 parts of medical stone powder, 1.7 parts of sweet potato starch, and 3 parts of aluminum oxide with water in parts by weight, dry, pulverize and sieve to obtain granular material A; A is heated to 320°C, kept for 1.8 hours, then raised to 560°C, kept for 36 minutes, then heated to 630°C, kept for 14 minutes, take...
Embodiment 3
[0026]A kind of deodorant toilet lid proposed by the present invention, its raw material comprises by weight: 58 parts of corn cobs, 33 parts of straw powder, 52 parts of peanut shell powder, 24 parts of tea leaves, 23 parts of pomelo peel, 11 parts of rice bran, 44 parts of Bamboo wood powder, 4 parts of papermaking sludge, 13 parts of modified medical stone powder, 10 parts of porous calcium phosphate, 11 parts of mint, 15 parts of honeysuckle, 7 parts of clove, 3.5 parts of tourmaline powder, 3.4 parts of six-ring stone powder, 31 parts of ring Oxygen resin cement;
[0027] Wherein the preparation method of the modified medical stone powder is as follows: after mixing 6 parts of medical stone powder, 1 part of sweet potato starch, and 4 parts of aluminum oxide with water in parts by weight, dry, pulverize and sieve to obtain granular material A; A is heated to 300°C, kept for 2 hours, then raised to 550°C, kept for 40 minutes, then heated to 620°C, kept for 15 minutes, take...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com