Temperable three-silver LOW-E glass and preparation method thereof

A technology of glass and glass substrate, applied in the field of temperable triple silver LOW-E glass, glass preparation, can solve the problems of poor heat resistance, low light transmittance, large color deviation, etc. Good heat resistance and small color deviation

Active Publication Date: 2015-09-30
中建材佳星玻璃(黑龙江)有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass plays an important role in contemporary production and life. Coated glass is widely used, but the existing coated glass film layer is easy to scratch, has poor heat resistance, low light transmittance, high reflectivity, and high shading coefficient. Large color deviation after tempering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Temperable three-silver LOW-E glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] A temperable triple-silver LOW-E glass, including a glass substrate 1, on the composite surface of the glass substrate 1, there are twenty film layers sequentially and adjacently compounded from the inside to the outside, wherein the first film layer i.e. the innermost layer is SiN x Layer 21, the second film layer is TiO 2 layer 22, the third film layer is ZnO layer 23, the fourth film layer is NiCr layer 24, the fifth film layer is Ag layer 25, the sixth film layer is NiCr layer 26, and the seventh film layer is TiO 2 Layer 27, the eighth film layer is ZnO 2 layer 28, the ninth film layer is NiCr layer 29, the tenth film layer is Ag layer 210, the eleventh film layer is NiCr layer 211, and the twelfth film layer is TiO 2 Layer 212, the thirteenth film layer is ZnO 2 layer 213, the fourteenth film layer is a NiCr layer 214, the fifteenth layer is an Ag layer 215, the sixteenth layer is a NiCr layer 216, and the seventeenth layer is a TiO 2 layer 217, the eighteenth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses temperable three-silver LOW-E glass which comprises a glass substrate, wherein twenty film layers are adjacently compounded on the composite surface of the glass substrate from inside to outside in sequence. The temperable three-silver LOW-E glass is characterized in that the first film layer, namely, the innermost layer, is the SiNx layer, the second film layer is the TiO2 layer, the third film layer is the ZnO layer, the fourth film layer is the NiCr layer, the fifth film layer is the Ag layer, the sixth film layer is the NiCr layer, the seventh film layer is the TiO2 layer, the eighth film layer is the ZnO2 layer, the ninth film layer is the NiCr layer, the tenth film layer is the Ag layer, the eleventh film layer is the NiCr layer, the twelfth film layer is the TiO2 layer, the thirteenth film layer is the ZnO2 layer, the fourteenth film layer is the NiCr layer, the fifteenth film layer is the Ag layer, the sixteenth film layer is the NiCr layer, the seventeenth film layer is the TiO2 layer, the eighteenth film layer is the ZnO layer, the nineteenth film layer is the SiNx layer, and the twentieth layer, namely, the outermost layer, is the SiC layer.

Description

【Technical field】 [0001] The invention relates to a coated glass, more specifically a temperable triple-silver LOW-E glass, and also relates to a method for preparing the glass. 【Background technique】 [0002] Glass plays an important role in contemporary production and life. Coated glass is widely used, but the existing coated glass film layer is easy to scratch, has poor heat resistance, low light transmittance, high reflectivity, and high shading coefficient. After tempering, the color deviation is large. 【Content of invention】 [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a temperable film with strong mechanical scratch resistance, good heat resistance, high transmittance, low reflectivity, small shading coefficient, and small color deviation after tempering. Three silver LOW-E glass. The invention also provides a preparation method of temperable triple-silver LOW-E glass. [0004] The present invention i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/36
Inventor 孙叠文马满江
Owner 中建材佳星玻璃(黑龙江)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap