Photonic crystal hydrogel membrane with pH value and ionic strength response, preparation method and application thereof

A technology of photonic crystals and ionic strength, which is applied in the direction of ferrous oxides, analysis of materials through chemical reactions, and material analysis through observation of the influence of chemical indicators, can solve the problem of preparation of photonic crystal hydrogels. Problems such as long cycle, difficult preparation, and inaccurate control of carboxyl content can achieve the effect of easy large-scale preparation, strong reproducibility, and short preparation time

Active Publication Date: 2015-10-07
HUAZHONG UNIV OF SCI & TECH
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above defects or improvement needs of the prior art, the present invention provides a photonic crystal hydrogel film with both pH value and ionic strength response, its preparation method and application, the purpose of which is to use Fe 3 o 4 The formulation of nanoparticles and monomers forms an ordered structure in the photonic crystal film, thereby solving the problem of the long preparation period of the existing photonic crystal hydrogel, the inability to precisely control the carboxyl content, and the difficulty in preparing single-color, large-area, and high-quality hydrogels. Technical issues of photonic crystal hydrogel films with pH and ionic strength responses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photonic crystal hydrogel membrane with pH value and ionic strength response, preparation method and application thereof
  • Photonic crystal hydrogel membrane with pH value and ionic strength response, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The photonic crystal hydrogel film provided by the invention, its preparation method, comprises the following steps:

[0034] (1) Preparation of photonic crystal hydrogel precursor: Fe 3 o 4Nanoparticles, acrylamide, hydroxyethyl methacrylate, methylene bisacrylamide and photoinitiator are uniformly dispersed in the organic solution to obtain a suspension of photonic crystal hydrogel precursor, so that each milliliter of photonic crystal hydrogel precursor Fe in body 3 o 4 Nanoparticles 1mg-50mg, preferably 10mg-30mg, more preferably 10mg-20mg, acrylamide 100mg-600mg, preferably 200mg-400mg, hydroxyethyl methacrylate 10mg-500mg, preferably 20mg-40mg, more preferably 30mg-40mg, Forked bisacrylamide 1mg~20mg, and photoinitiator 0.1mg~1mg. The photoinitiator is a commonly used photoinitiator in the art, preferably 2,2-diethoxyacetophenone. Described organic solvent is preferably conventional dispersing solvents such as methanol, ethanol, ethylene glycol, polyethylene ...

Embodiment 1

[0046] A photonic crystal hydrogel film, prepared according to the following method:

[0047] (1) Preparation of photonic crystal hydrogel precursor: Fe 3 o 4 Nanoparticles, acrylamide, hydroxyethyl methacrylate, methylene bisacrylamide and photoinitiator are uniformly dispersed in ethylene glycol by ultrasonic dispersion method to obtain a suspension of photonic hydrogel crystal precursor, so that each Fe in ml photonic crystal hydrogel precursor 3 o 4 1 mg of nanoparticles, 100 mg of acrylamide, 10 mg of hydroxyethyl methacrylate, 1 mg of methylenebisacrylamide, and 0.1 mg of photoinitiator 2,2-diethoxyacetophenone.

[0048] The Fe 3 o 4 Nanoparticles are prepared as follows: dissolve ferrocene and hydrogen peroxide in 75ml of acetone, and add the solution to a 100mL stainless steel reaction kettle, so that the concentration of ferrocene in the solution is 0.001mg / ml, and the concentration of hydrogen peroxide is 0.01mg / ml; react at 100°C for 10 hours, after the react...

Embodiment 2

[0052] A photonic crystal hydrogel film, prepared according to the following method:

[0053] (1) Preparation of photonic crystal hydrogel precursor: Fe 3 o 4 Nanoparticles, acrylamide, hydroxyethyl methacrylate, methylene bisacrylamide and photoinitiator are uniformly dispersed in glycerin by ultrasonic dispersion method to obtain a suspension of photonic hydrogel crystal precursor, so that each milliliter of photon Fe in crystalline hydrogel precursors 3 o 4 1 mg of nanoparticles, 100 mg of acrylamide, 10 mg of hydroxyethyl methacrylate, 1 mg of methylenebisacrylamide, and 0.1 mg of photoinitiator 2,2-diethoxyacetophenone.

[0054] The Fe 3 o 4 Nanoparticles are prepared as follows: dissolve ferrocene and hydrogen peroxide in 75ml of acetone, and add the solution to a 100mL stainless steel reaction kettle, so that the concentration of ferrocene in the solution is 0.001mg / ml, and the concentration of hydrogen peroxide is 0.01mg / ml; react at 100°C for 10 hours, after th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a photonic crystal hydrogel membrane with pH value and ionic strength response, a preparation method and an application thereof. The photonic crystal hydrogel membrane comprises Fe3O4 nano particles and polyacrylamide-methacrylate acetic acid hydrogel, wherein the Fe3O4 nano particles are uniformly dispersed in the hydrogel and are arranged in a one-dimensional chain shape, and the concentration of the nano particles in the membrane is 1 to 50 mg / mL. The preparation method of the photonic crystal hydrogel membrane comprises the steps of uniformly mixing the Fe3O4 nano particles and hydrogel monomers, so as to generate curing reaction through ultraviolet light, and soaking in a soluble carbonate aqueous solution at last, so as to obtain the required membrane. The preparation method has the advantages of simplicity in operation, strong repeatability and convenience in large-scale preparation, the carboxyl quantity of the obtained membrane is controllable, the membrane is monochromatic, obvious color change occurs under the stimulation of pH value or ionic strength, and naked-eye detection is facilitated.

Description

technical field [0001] The invention belongs to the field of photonic crystal materials, and more specifically relates to a photonic crystal hydrogel film with both pH value and ionic strength response, its preparation method and application. Background technique [0002] Photonic crystals are a periodic structure composed of materials with different refractive indices alternately in space. The most fundamental feature of photonic crystals is that they have a photonic forbidden band, that is, light falling in the forbidden band is prohibited from propagating. Due to their unique optical properties, photonic crystals are widely used in the preparation of various optical devices (such as modulators, sensors, displays, etc.). [0003] Photonic crystals with pH and ionic strength responses are optical materials in which monodisperse nanoparticles are dispersed in pH-responsive polymers. Through the change of pH value and ionic strength of the solution, the volume of the respons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/40C08J5/18C08J3/28C08L33/26C08F220/56C08F220/28C08F222/38C08F2/48C08F2/44C08K3/22C01G49/08G01N21/78
Inventor 朱锦涛贾晓潞沈雷
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com