Rust-proof treatment method for stainless-steel welding joint
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of anti-rust treatment and stainless steel, applied in the direction of metal material coating process, coating, etc., can solve the problems of low production efficiency, difficult processing, and failure to achieve high production efficiency, low processing difficulty, and anti-corrosion performance Improved effect
Inactive Publication Date: 2015-10-07
合肥长兴汽车配件有限公司
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to provide a stainless steel weld anti-rust treatment method, which solves the low production efficiency and high processing difficulty caused by mechanical grinding and polishing in the prior art; the oxide layer on the surface of the weld cannot be completely removed; After applying the anti-rust paste, the appearance is not beautiful, and the effect of completely isolating the oxidation of the weld can not be achieved and other series of problems
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] Embodiment 1, the present embodiment carries out as follows:
[0015] (1) Evenly apply a layer of passivation paste on the surface of the stainless steel weld;
[0016] (2) After the chemical reaction between the passivation paste and the oxide layer on the surface of the weld is completed, the reaction time is controlled within 15 minutes;
[0017] (3), utilize high-pressure water gun to flush to the product after the reaction of above-mentioned step (2);
[0018] (4) The product rinsed in step (3) is blotted dry, and the anti-rust treatment of the weld seam of the product is completed.
Embodiment 2
[0019] Embodiment 2, the present embodiment is carried out according to the following steps:
[0020] (1) Evenly apply a layer of passivation paste on the surface of the stainless steel weld;
[0021] (2) After the chemical reaction between the passivation paste and the oxide layer on the surface of the weld is completed, the reaction time is controlled within 20 minutes;
[0022] (3), utilize high-pressure water gun to flush to the product after the reaction of above-mentioned step (2);
[0023] (4) The product rinsed in step (3) is blotted dry, and the anti-rust treatment of the weld seam of the product is completed.
Embodiment 3
[0024] Embodiment 3, the present embodiment is carried out according to the following steps:
[0025] (1) Evenly apply a layer of passivation paste on the surface of the stainless steel weld;
[0026] (2) After the chemical reaction between the passivation paste and the oxide layer on the surface of the weld is completed, the reaction time is controlled at 17.5 minutes;
[0027] (3), utilize high-pressure water gun to flush to the product after the reaction of above-mentioned step (2);
[0028] (4) The product rinsed in step (3) is blotted dry, and the anti-rust treatment of the weld seam of the product is completed.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a rust-proof treatment method for a stainless-steel welding joint, and relates to the technical field of rust-proof treatment on the stainless-steel welding joint. According to the rust-proof treatment method for the stainless-steel welding joint, a layer of passivation cream is smeared uniformly on the surface of the stainless-steel welding joint, chemical reaction occurs between the passivation cream and an oxide layer on the surface of the welding joint, when the chemical reaction is finished, the welding joint is washed through a water cannon, and rust-proof treatment on the welding joint of the product is finished. According to the rust-proof treatment method for the stainless-steel welding joint, mechanical treatment is not needed by the welding joint on which passivation treatment is conducted already, the processing difficulty is low, the production efficiency is high, and the rust-proof performance of the welding joint can be improved greatly.
Description
technical field [0001] The invention relates to the technical field of antirust treatment of stainless steel welds, in particular to a method for antirust treatment of stainless steel welds. Background technique [0002] The existing technology is to use mechanical grinding and polishing after the welding of stainless steel materials to rub off the oxide layer on the surface of the weld seam, so that the surface of the weld seam is rubbed bright, and finally apply anti-rust paste on the weld seam to isolate the weld seam from the outside world Exposure to air oxidizes. The disadvantage of this anti-rust treatment method is that the production efficiency of mechanical grinding and polishing is low, and the processing is difficult; the oxide layer on the surface of the weld cannot be completely removed; the appearance is not beautiful after the anti-rust paste is applied, and the weld cannot be completely isolated the effect of oxidation. Contents of the invention [0003]...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More