Preparation method of absorbable medical suture with good tensile strength
A technology of tensile strength and sutures, which is applied in the field of medical sutures, can solve the problems of difficult adhesion and reproduction of cells, low mechanical strength of chitosan, and easy inflammation, etc., so as to increase hydrophilicity and cell compatibility Sex, improve cell affinity, reduce the effect of rejection
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] A method for preparing absorbable medical sutures with good tensile strength. Take polyethylene glycol monomethyl ether, feed nitrogen gas, heat up to 65°C, keep warm until polyethylene glycol monomethyl ether melts, add zinc lactate, acrylic acid Mix the lactide, heat up to 150°C, keep stirring at a speed of 100r / min for 3h, add dichloromethane to dissolve, add dropwise to ether, filter, and vacuum dry to obtain the intermediate material, wherein the moles of zinc lactate and lactide The ratio is 0.4:100, and the weight ratio of polyethylene glycol monomethyl ether and lactide is 50:144; add carboxymethyl chitosan to water to dissolve, add intermediate materials, stannous chloride, mix well, and pass through nitrogen , heat up to 90°C, keep warm for 35h, filter, add the filtrate dropwise to toluene, filter to obtain a filter cake, and vacuum dry to obtain modified chitosan, wherein the weight volume of carboxymethyl chitosan and water (g / ml ) ratio is 1:100, and the we...
Embodiment 2
[0024] A method for preparing absorbable medical suture with good tensile strength. In the preparation process, polyethylene glycol monomethyl ether is taken, nitrogen gas is passed through, the temperature is raised to 75° C., and the temperature is kept until the polyethylene glycol monomethyl ether melts. Add zinc lactate and lactide and mix well, raise the temperature to 140°C, keep stirring at a speed of 300r / min for 2h, add dichloromethane to dissolve, add dropwise to diethyl ether, filter, and vacuum dry to obtain intermediate materials, in which zinc lactate, The molar ratio of lactide is 0.5:100, and the weight ratio of polyethylene glycol monomethyl ether and lactide is 25:144; add carboxymethyl chitosan to water to dissolve, add intermediate materials, stannous chloride mixed Evenly, nitrogen gas was introduced, the temperature was raised to 120°C, and the temperature was kept for 30h, filtered, and the filtrate was added dropwise to ethyl acetate, filtered to obtain...
Embodiment 3
[0026] A method for preparing absorbable medical suture with good tensile strength. In the preparation process, polyethylene glycol monomethyl ether is taken, nitrogen gas is passed through, the temperature is raised to 67° C., and the temperature is kept until the polyethylene glycol monomethyl ether melts. Add zinc lactate and lactide and mix well, heat up to 147°C, keep stirring at a speed of 150r / min for 2.8h, add dichloromethane to dissolve, add dropwise to ether, filter, and vacuum dry to obtain intermediate materials, in which zinc lactate , The molar ratio of lactide is 0.42:100, the weight ratio of polyethylene glycol monomethyl ether and lactide is 45:144; add carboxymethyl chitosan to dissolve in water, add intermediate material, stannous chloride Mix evenly, feed nitrogen, heat up to 100°C, keep warm for 34 hours, filter, add the filtrate dropwise to toluene, filter to obtain a filter cake, and vacuum dry to obtain modified chitosan, wherein the mixture of carboxyme...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com