Hydrotalcite-lanthanum cyanurate composite environmental protection stabilizer for PVC, and preparation method thereof

A technology of talc lanthanum cyanurate and environmental protection stabilizer is applied in the field of PVC hydrotalcite lanthanum cyanurate composite environmental protection stabilizer and its preparation field, which can solve the problems of poor coloring, cannot be used as the main stabilizer alone, and low thermal stability, etc. Low, improve the effect of thermal stability, improve the effect of heat resistance and mechanical properties

Inactive Publication Date: 2016-02-03
HWASU
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Rare earth heat stabilizers have good thermal stability, but the early thermal stability is not high, and the initial coloring is poor, so they cannot be the main stabilizer alone, so their application and promotion are limited. The applicati...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A PVC hydrotalcite lanthanum cyanurate composite environmental stabilizer, which is prepared from the following components by weight (kg): modified magnesium aluminum hydrotalcite 26, dibutyltin oxide 12, lanthanum cyanurate 7, lauric acid Cerium 7, Trimethyl phosphite 2, Acetyl tri(2-ethylhexyl) citrate 14, Barium stearate 5, Diphenylthiourea 3, Zinc stearate 5, Hexamethylphosphoric triamide 2. Stearic acid 1, vermiculite powder 12.

[0018] The preparation method is as follows:

[0019] (1) Preparation of modified hydrotalcite:

[0020] a. Add a certain amount of Mg(NO3)2·6H2O and Al(NO3)3·9H2O into water to form a salt solution with a total molar concentration of 0.6mol / L, and add a certain amount of NaOH and Na2CO3 into deionized water to form The total molar concentration is 0.6mol / L alkali solution, drop the alkali solution into the salt solution at a speed of 1-2 drops / s, N 2 Stir vigorously under protection, keep the temperature at 38-42°C, keep the pH ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal stabilization timeaaaaaaaaaa
Thermal stabilization timeaaaaaaaaaa
Login to view more

Abstract

The present invention provides a hydrotalcite-lanthanum cyanurate composite environmental protection stabilizer for PVC, wherein the hydrotalcite-lanthanum cyanurate composite environmental protection stabilizer is prepared from the following raw materials by weight: 20-30 parts of modified magnesium aluminum hydrotalcite, 10-12 parts of dibutyl tin oxide, 6-8 parts of lanthanum cyanurate, 6-9 parts of cerium laurate, 1-3 parts of trimethyl phosphite, 13-15 parts of tri(2-ethylhexyl) acetylcitrate, 3-6 parts of barium stearate, 2-4 parts of diphenyl thiourea, 5-6 parts of zinc stearate, 1-2 parts of hexamethylphosphoric triamide, 1-2 parts of stearic acid, and 10-13 parts of vermiculite powder. According to the present invention, the PVC stabilizer has characteristics of good thermal stability, good processing performance, environmental protection, no toxicity, low cost, good plasticity and balance torque reducing during the PVC processing process, and low cost.

Description

technical field [0001] The invention relates to the field of PVC additives, in particular to a PVC hydrotalcite lanthanum cyanurate composite environment-friendly stabilizer and a preparation method thereof. Background technique [0002] With its superior physical properties and low cost, PVC is widely used in chemical industry, materials, machinery, agriculture, daily necessities and other fields, especially in the field of plastics, and is known as one of the five general-purpose plastics. However, PVC has a very important defect, that is, it is easy to decompose and generate HCl gas during thermal processing, and self-catalysis leads to severe degradation of PVC, which affects various properties of PVC products, such as discoloring PVC products or reducing its mechanical properties. In order to overcome this defect of PVC, it is mainly to add an appropriate amount of stabilizer during the thermal processing of PVC. [0003] The only heat stabilizers that are generally in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/06C08K9/04C08K3/26C08K5/57C08K5/3492C08K5/098C08K5/524C08K5/11C08K5/405C08K5/5399C08K5/09C08K3/34
Inventor 王圣茂丘永桂宋开生高旭李毅徐明肖独山孙荣兴
Owner HWASU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap