A kind of preparation method of electrochemical cell

An electrochemical and battery technology, applied in the field of energy storage, can solve the problems of time-consuming, occupying production costs, and complicated procedures, and achieve the effect of simple and reliable procedures and easy low-cost production.

Active Publication Date: 2018-09-11
GUANGDONG ZHUGUANG NEW ENERGY TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For organic electrolyte batteries, it is usually necessary to dry the cells and then inject liquid. After the liquid injection, a slow electrolyte infiltration process is performed, and the formation begins when the electrolyte is fully immersed. The above process is cumbersome and time-consuming. a lot of production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of electrochemical cell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1, different from Comparative Example 1, this embodiment comprises the following steps:

[0031] Cell preparation: Wind the positive electrode sheet, separator, and negative electrode sheet to obtain a bare cell, and then place it in a drying oven with the furnace temperature set at 80°C and preheat with ventilation; when the cell is preheated to 78°C (cell dry When the temperature is required), vacuumize the furnace to 4kpa, and keep the temperature in the furnace at 80°C for drying; when the water content inside the cell is lower than 200ppm, complete the drying;

[0032] Pretreatment: Vacuumize the dried cells to be liquid-filled for 10 hours in an environment of 1000 Pa, and keep the temperature of the cells at 60°C to obtain soaked bare cells;

[0033] Soaking: keep the vacuum, put the bare cell at 60°C in the electrolyte at 25°C, so that the bare cell is sealed by the electrolyte, and then soak until the electrolyte fully infiltrates the diaphragm;

[...

Embodiment 2

[0037] Embodiment 2, different from Embodiment 1, this embodiment includes the following steps:

[0038] Pretreatment: Vacuumize the dried cells to be liquid-filled for 2 hours in an environment of 200 Pa, and keep the temperature of the cells at 60°C to obtain soaked bare cells;

[0039] The rest are the same as in Embodiment 1, and will not be repeated here.

Embodiment 3

[0040] Embodiment 3, different from Embodiment 1, this embodiment includes the following steps:

[0041] Pretreatment: Vacuumize the dried cells to be liquid-filled in an environment of 100 Pa for 1 hour, and keep the temperature of the cells at 60°C to obtain soaked bare cells;

[0042] The rest are the same as in Embodiment 1, and will not be repeated here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of electrochemical batteries, and particularly relates to a preparation method of electrochemical batteries: mainly including four steps of pretreatment, soaking, control of electrolyte retention and preparation of finished batteries. The gas components in the discharge are discharged to reserve space for the electrolyte to infiltrate; then the cell is soaked in the electrolyte so that the cell is surrounded by sufficient electrolyte and is quickly infiltrated by the electrolyte; , to control the amount of electrolyte solution to be squeezed out, so as to obtain the actual amount of electrolyte solution required by the battery cell; finally, the finished battery is prepared. The process is simple and reliable, and is convenient for industrialized low-cost production.

Description

technical field [0001] The invention belongs to the field of energy storage, in particular to a preparation method of an electrochemical battery. Background technique [0002] After entering the 21st century, various electronic device products such as mobile phones, notebooks, wearable devices, etc. emerge in an endless stream, which greatly enriches the lives of the majority of users; at the same time, electric vehicles and various energy storage power stations are also rapidly sprouting, developing, and grow. The above high-tech products have a common feature: high-performance, low-cost batteries are required to act as energy storage components. [0003] Existing batteries mainly include primary batteries and secondary batteries; the so-called primary batteries, that is, batteries that cannot be recharged, mainly include carbon-zinc batteries, alkaline batteries, paste-type zinc-manganese batteries, cardboard zinc-manganese batteries, alkaline Zinc-manganese batteries, b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/058
CPCH01M10/058H01M10/0587Y02E60/10Y02P70/50
Inventor 杨玉洁
Owner GUANGDONG ZHUGUANG NEW ENERGY TECH