Secondary recycling method of silicon rod slicing waste mortar

A waste mortar and secondary recycling technology, which is applied to fine working devices, stone processing equipment, manufacturing tools, etc., can solve the problems of increasing consumption of cutting auxiliary materials, and achieve the effects of simple operation, reduced consumption, and reduced production costs

Inactive Publication Date: 2016-04-27
HUNAN RED SUN PHOTOELECTRICITY SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, mortar is needed when cutting silicon rods, and currently, after cutting with mortar, the mortar will be directly scrapped, which greatly increases the consumption of cutting auxiliary materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Secondary recycling method of silicon rod slicing waste mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.

[0019] Such as figure 1 As shown, the silicon rod slice waste mortar secondary recycling method of the present embodiment includes the following steps:

[0020] S01, first extract the waste mortar after slicing silicon rods, and filter it to filter out broken silicon chips and other large particles and impurities generated during the cutting process;

[0021] S02. Reconstitute the ratio of each component of the filtered waste mortar to achieve the ratio of the components of the new mortar, and ensure that the density of the waste mortar reaches the density required for silicon rod slicing;

[0022] S03. Add a filter screen at the mortar circulation port of the cutting chamber in the silicon rod cutting machine to further filter the waste mortar, and put the waste mortar into the cutting chamber;

[0023] S04. When cutting silicon rods, adjust...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a secondary recycling method of silicon rod slicing waste mortar. The method comprises the following steps: (S01) firstly, waste mortar generated by slicing a silicon rod is extracted and filtered; (S02) all components of the filtered waste mortar are renewedly mixed to reach a component scale value of new mortar; and the density of the waste mortar is guaranteed to reach the density needed by slicing the silicon rod; (S03) a filter screen is added in a cutting chamber mortar circulating port of a silicon rod cutting machine; and the waste mortar is filled in a cutting chamber; and (S04) when the silicon rod is cut, a silicon rod cutting process is adjusted to guarantee the silicon rod slicing quality. The secondary recycling method of the silicon rod slice waste mortar has such advantages as convenience for operation, reduction of slicing accessory consumption and reduction of production cost.

Description

technical field [0001] The invention mainly relates to the technical field of silicon rod cutting, in particular to a method for secondary recycling of silicon rod slicing waste mortar. Background technique [0002] At present, mortar is needed when cutting silicon rods, and currently, after cutting with mortar, the mortar will be directly scrapped, which greatly increases the consumption of cutting auxiliary materials. Contents of the invention [0003] The technical problem to be solved by the present invention is that, aiming at the technical problems existing in the prior art, the present invention provides a method for secondary recycling of silicon rod chip waste mortar which is easy to operate and reduces the consumption of cutting auxiliary materials. [0004] In order to solve the problems of the technologies described above, the technical solution proposed by the present invention is: [0005] A method for secondary recycling of silicon rod chip waste mortar, co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B28D5/00
CPCB28D5/007
Inventor 席德兴
Owner HUNAN RED SUN PHOTOELECTRICITY SCI & TECH