A kind of adsorbent and its preparation method for simultaneously strengthening the removal of trace phosphorus and organic matter
An adsorbent and organic matter technology, which is applied in the field of adsorbent and its preparation, can solve the problems that organic matter and phosphorus cannot be removed at the same time, and the removal rate of trace phosphorus in water is low, so as to achieve good adsorption and removal effect, improve adsorption capacity, and increase adsorption point. bit effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
specific Embodiment approach 1
[0028] Embodiment 1: In this embodiment, the adsorbent for simultaneously strengthening the removal of trace amounts of phosphorus and organic matter is a lanthanum-polyacrylonitrile-based carbon nanofiber material, which is obtained by uniformly loading nanoscale lanthanum compounds inside and on the surface of carbon nanofibers.
[0029] The composite carbon material prepared by the present invention has an obvious adsorption and removal effect on trace phosphorus, and can still effectively adsorb and remove orthophosphate in water even in the presence of organic matter, and the removal rate of orthophosphate can reach 100%, and can At the same time, organic matter in water is removed.
specific Embodiment approach 2
[0030] Specific embodiment two: this embodiment strengthens the preparation method of the adsorbent that removes trace amount of phosphorus and organic matter at the same time, carries out according to the following steps:
[0031] 1. La(NO 3 ) 3 ·6H 2 Dissolve O in DMF, then add PAN, heat at 50-100°C until PAN is completely dissolved to obtain a DMF solution of PAN, then perform high-voltage electrospinning on the DMF solution of PAN to obtain a spun film, and pass the obtained spun film through After lye treatment, use deionized water to repeatedly rinse until the pH is neutral, and dry;
[0032] 2. Place the dried spinning film in a tube furnace, pre-oxidize it in the air, and then carbonize it under the protection of nitrogen. Soak the carbonized material in alkali solution, rinse it with deionized water after soaking The carbon material is neutralized and dried to obtain the adsorbent.
[0033] In this embodiment, the raw materials for the preparation of a novel adsor...
specific Embodiment approach 3
[0034] Specific embodiment three: the difference between this embodiment and specific embodiment two is: in step one, PAN and La(NO 3 ) 3 ·6H 2 O mass ratio is (1~10):1. Others are the same as in the second embodiment.
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com