Preparing method for synthetic fat dispersed vanadium boride silicon carbide-carbon fiber friction material
A technology of vanadium boride silicon carbide and friction materials, which is applied in ceramic products, applications, household appliances, etc., can solve the problems of safety hazards and friction performance reduction, and achieve the effect of improving wear resistance and high manufacturing cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1
[0019] (1) Set the density to 1.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 900°C. The molar ratio of propane gas: nitrogen is 1:4, the flow rate is controlled at 50ml / min, and the carburizing treatment is performed for 24 hours to obtain a carburized carbon fiber blanket. ;
[0020] (2) Immerse the above-mentioned carburized carbon fiber blanket into a synthetic grease slurry with a particle size of less than 0.3 μm and a content of 5% vanadium boride, place it in an ultrasonic cleaner and fill it with vanadium boride for 50 minutes, take it out and dry it to obtain a filled boride Vanadium carbon fiber blanket, the synthetic fat slurry is an ethanol solution containing 5% synthetic fat;
[0021] (3) Pass the above-mentioned filled vanadium boride carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 900 °C, and the molar ...
Example Embodiment
[0024] Example 2
[0025] (1) Set the density to 0.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixture of propane gas and nitrogen at a temperature of 1000°C. The molar ratio of propane gas: nitrogen is 1:5, the flow rate is controlled at 350ml / min, and the carburizing treatment is performed for 18 hours to obtain a carburized carbon fiber blanket. ;
[0026] (2) Immerse the above-mentioned carburized carbon fiber blanket in a synthetic grease slurry with a particle size of less than 0.3 μm and a content of 12% vanadium boride, place it in an ultrasonic cleaner and fill it with vanadium boride for 40 minutes, take it out and dry it to obtain a filled boride Vanadium carbon fiber blanket, the synthetic fat slurry is an ethanol solution containing 12% synthetic fat;
[0027] (3) Pass the above-mentioned filled vanadium boride carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 1000 °C, and the mola...
Example Embodiment
[0030] Example 3
[0031] (1) Set the density to 0.1g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 1100°C. The molar ratio of propane gas: nitrogen is 1:6, the flow rate is controlled at 600ml / min, and the carburizing treatment is performed for 10 hours to obtain a carburized carbon fiber blanket. ;
[0032] (2) Immerse the above-mentioned carburized carbon fiber blanket in a synthetic grease slurry with a particle size of less than 0.3 μm and a content of 20% vanadium boride, place it in an ultrasonic cleaner and fill it with vanadium boride for 30 minutes, take it out and dry it to obtain a filled boride Vanadium carbon fiber blanket, synthetic fat slurry is an ethanol solution containing 20% synthetic fat;
[0033] (3) Pass the above-mentioned filled vanadium boride carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 1100 ° C. The molar r...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap