Preparation method of alloy ceramic thin film, mobile terminal shell and mobile terminal

A technology of alloy ceramics and mobile terminals, which is applied in the coating process and coating of metal materials, etc., can solve the problems of poor texture, environmental pollution, and cumbersome pretreatment procedures.

Active Publication Date: 2018-05-15
COOLPAD SOFTWARE TECH (SHENZHEN) CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the appearance parts of mobile terminals are basically colored by surface treatment technologies such as anodic oxidation, spray coating, electrophoretic deposition, and vacuum coating, so as to achieve decorative functions. However, the current surface coloring technologies either consume high energy consumption or cause serious environmental pollution. In addition, surface treatment technologies such as anodic oxidation, spray coating, electrophoretic deposition, and vacuum coating are all surface coating technologies. The pretreatment process is cumbersome, the bonding force between the film and the substrate is weak, the wear resistance is relatively poor, and the texture is very bad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of alloy ceramic thin film, mobile terminal shell and mobile terminal
  • Preparation method of alloy ceramic thin film, mobile terminal shell and mobile terminal
  • Preparation method of alloy ceramic thin film, mobile terminal shell and mobile terminal

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] like figure 1As shown, the present invention proposes a method for preparing an alloy ceramic thin film, including: step 102, when the laser beam performs laser laser process on the surface of the alloy plate, blowing a designated reaction gas to the surface of the alloy plate, so that An alloy ceramic thin film is formed on the surface of the alloy plate.

[0030] Specifically, such as figure 2 and image 3 As shown, the alloy plate 1 is selected as the base material, and the alloy plate 1 is processed into the shape of the mobile phone shell, and in order to realize continuous laser coloring of multiple mobile phone shells, multiple mobile phone shells can be rotated according to the computer control program. The body is installed on the assembly line, the assembly line 2 is preferably a rotating disk assembly line, and the mobile phone housing body is located under the laser ablation plasma generator 3, wherein the laser ablation plasma generator 3 emits a laser b...

Embodiment 1

[0047] Select the aluminum alloy with the model number Al7075 as the alloy plate, shape the alloy plate according to the structural design requirements of the mobile phone appearance parts, then polish and clean it, and then make a milky white alloy ceramic film on the surface of the alloy plate, specifically ground, use as figure 2 and image 3 For the shown equipment, the method for preparing the alloy ceramic thin film is as follows: first, oxygen with a purity higher than 3N and nitrogen with a purity higher than 4N are used as the designated reaction gas (wherein, 3N means that the mass purity is 99.9%, and 4N means that the mass purity is 99.9%) 99.99%), and the volume content of oxygen in the mixed gas is not less than 85%, and the flow rate of the mixed gas ranges from 30 milliliters per minute to 40 milliliters per minute; secondly, the chemical composition of the alloy based on Al7075 and the alloy ceramic thin film For the process conditions of the preparation met...

Embodiment 2

[0051] Select titanium alloy with model TC4 or titanium alloy with model TB6 as the alloy plate, shape and process the alloy plate according to the structural design requirements of mobile phone appearance parts, then polish and clean it, and then manufacture on the surface of the alloy plate Royal blue alloy ceramic film, using such as figure 2 and image 3The equipment shown, specifically, the method for preparing the alloy ceramic film is as follows: first, oxygen and acetylene with a purity higher than 3N are used as the designated reaction gas, and the volume content of oxygen in the mixed gas is not less than 95%, and the mixed gas The gas flow rate ranges from 10 ml to 50 ml per minute; clean air can also be used as the designated reaction gas, and the gas flow rate ranges from 10 ml to 50 ml per minute; secondly, based on titanium alloy TC4 or titanium alloy The chemical composition of TB6 and the technological condition of the preparation method of alloy ceramic thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention proposes a method for preparing an alloy ceramic film, a mobile terminal casing and a mobile terminal, wherein the method for preparing the alloy ceramic film includes: when the laser beam is performing laser laser process on the surface of the alloy plate , blowing a designated reaction gas onto the surface of the alloy plate to form an alloy ceramic film on the surface of the alloy plate. Through this technical scheme, the surface of the alloy plate is directly treated with laser and the specified reaction gas is blown, so that the alloy ceramic film formed on the surface of the alloy plate has good hand feeling, high hardness, good wear resistance, and Corrosion, and can achieve a good decorative effect, and the preparation method of the alloy ceramic thin film is simple, does not require the coating technology on the alloy plate, reduces the process flow, thereby effectively protecting the environment.

Description

technical field [0001] The invention relates to the technical field of terminals, in particular to a method for preparing an alloy ceramic film, a mobile terminal shell and a mobile terminal. Background technique [0002] At present, the appearance parts of mobile terminals are basically colored by surface treatment technologies such as anodic oxidation, spray coating, electrophoretic deposition, and vacuum coating, so as to achieve decorative functions. However, the current surface coloring technologies either consume high energy consumption or cause serious environmental pollution. In addition, surface treatment technologies such as anodizing, spraying, electrophoretic deposition, and vacuum coating are all surface coating technologies. The pretreatment process is cumbersome, the bonding force between the film and the substrate is weak, the wear resistance is relatively poor, and the texture is very bad. [0003] Therefore, how to propose a preparation method of an alloy c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C26/00
Inventor 刘兵任斌
Owner COOLPAD SOFTWARE TECH (SHENZHEN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka