GRC (glass fiber reinforced cement) product

A technology of products and raw materials, applied in the field of GRC products, can solve the problems of insufficient tensile and bending resistance and impact strength, and achieve the effects of good toughness, extended service life and good environmental protection.

Inactive Publication Date: 2016-06-15
孚姆(江门)新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] GRC (Glass Fiber Reinforced Concrete), also known as GFRC, the Chinese name is glass fiber reinforced cement or glass fiber reinforced concrete. It is a composite material mixed with glass fiber as a reinforcing material and cement mortar as a base material. The existing GRC The product has problems of insufficient tensile strength, bending resistance and impact strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • GRC (glass fiber reinforced cement) product
  • GRC (glass fiber reinforced cement) product
  • GRC (glass fiber reinforced cement) product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Weigh each raw material according to the weight shown in Table 1, first add water, then add color material, start the mixer to stir evenly, then add cement, after stirring for two minutes, add quartz sand, then add mortar, water reducing agent, metakaolin, pozzolan and methyl silicate, stir evenly to prepare cement mortar; use air pressure (6Kg / cm 2 ) chopping the glass fiber inside the concentric and coaxial spray gun, and automatically mixing it with the cement mortar to prepare glass fiber cement mortar with a glass fiber weight percentage of 5%;

[0050] The cement mortar is sprayed from the spray gun to the mold by air pressure to obtain a 3mm thick surface layer. The surface layer is sprayed twice: the first spraying is 1-1.5mm, and the next spraying is 1.5mm after 5-10 minutes. Left and right; Roller compaction is used to expel the air bubbles and increase the density. The spraying method is alternately carried out horizontally and vertically; after about 4 to 5 ...

Embodiment 2

[0053] In the preparation method of the GRC product of this embodiment, the back material layer is three layers, each layer is 3 mm, and the rest is consistent with the embodiment 1, and a GRC product with a thickness of 12 mm is obtained.

Embodiment 3

[0055] In the preparation method of the GRC product of this embodiment, the back material layer is nine layers, each layer is 3 mm, and the rest is consistent with the embodiment 1, and a GRC product with a thickness of 30 mm is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a GRC (glass fiber reinforced cement) product which is prepared from cement, glass fibers, quartz sand, water, rubber paste, a water reducing agent, metakaolin, volcanic ash and methyl silicate. The combination of the water reducing agent, metakaolin, volcanic ash and methyl silicate is used as an enhancer and used as a raw material of the GRC product. The combination of the water reducing agent, metakaolin, volcanic ash and methyl silicate is mixed with the cement, glass fibers and water, so that the water reducing agent, metakaolin, volcanic ash and methyl silicate can generate mutual synergistic actions; and thus, the GRC product has excellent bending resistance and tensile resistance, and the service life of the GRC product is maximally prolonged. When being used in a building, the GRC product has the same service life as the building. Besides, the raw materials used in the GRC product are from reprocessed natural or waste products, and thus, are green and environment-friendly.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a GRC product. Background technique [0002] GRC (Glass Fiber Reinforced Concrete), also known as GFRC, the Chinese name is glass fiber reinforced cement or glass fiber reinforced concrete. It is a composite material mixed with glass fiber as a reinforcing material and cement mortar as a base material. The existing GRC The product has the problems of insufficient tensile strength, bending resistance and impact strength. Contents of the invention [0003] The object of the present invention is to provide a GRC article with very good tensile, flexural and impact strength. [0004] For reaching this purpose, the present invention adopts following technical scheme: [0005] A GRC product is provided, the raw materials of which include: cement, glass fiber, quartz sand, water and mortar, water reducing agent, metakaolin, pozzolan and methyl silicate. [0006] Among t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/27C04B2111/506C04B2201/20C04B2201/50C04B14/42C04B14/06C04B2103/302C04B14/106C04B14/14C04B24/42C04B24/24
Inventor 危学渊
Owner 孚姆(江门)新材料科技有限公司