A comprehensive utilization method of acid leaching residue of NdFeB waste

A waste acid, NdFeB technology, applied in iron oxide, fibrous fillers, process efficiency improvement, etc., can solve the problems of no comprehensive utilization method, environmental pollution, site occupation, etc.

Inactive Publication Date: 2017-10-31
NANYANG ORIENTAL APPL CHEM RES INST
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no suitable comprehensive utilization method. Some enterprises either sell it as iron-making raw material or store it, which not only occupies the site, but also pollutes the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A comprehensive utilization method of acid leaching residue of NdFeB waste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Raw material composition used: Fe 2 o 3 53.54%; REO1.00%; Co0.65%.

[0041] Mix 100kg of NdFeB waste acid leaching residue with 295kg of acid leaching solution in a neutralization reactor, control the temperature at 70°C for 180 minutes, filter after the reaction, and wash with a small amount of water to obtain 69kg of neutralization residue and 355kg of neutralization solution. The main components of the neutralizing solution are: Fe 2 (SO 4 ) 3 131.3kg; REO 0.4kg; Co 0.62kg;

[0042] Mix and stir 69kg of neutralized residue with 105kg of iron red post-eluate in the acid leaching reactor to form a slurry, then add 106kg of concentrated sulfuric acid with a concentration of 98%, and the reaction time is 240min at 70°C. Filtrate at ℃ and wash with a small amount of water to obtain 295kg of acid leaching solution and 27kg of wet acid leaching residue.

[0043] Add 27kg of acid leaching residue to the reslurry washing tank and add the eluate 135kg, stirred into a ...

Embodiment 2

[0052] Raw material composition used: Fe 2 o 3 67.53%; REO0.85%;

[0053] Mix 1000kg of NdFeB waste acid leaching residue with 3410kg of acid leaching solution in a neutralization reactor, control the temperature at 100°C, and take 360min. After the reaction, filter at 90°C and wash with a small amount of water to obtain neutralization residue 600kg, neutralizing solution 3850kg. The main components of the neutralizing solution are: Fe 2 (SO 4 ) 3 1665kg; REO 3.80kg;

[0054] Mix 600kg of neutralization residue with 1500kg of iron red post-eluate in the acid leaching reactor to form a slurry, then add 1560kg of concentrated sulfuric acid with a concentration of 98%, and the reaction time is 180min at 90°C. Filtrate at ℃ and wash with a small amount of water to obtain 3410kg of acid leaching solution and 250kg of wet acid leaching residue.

[0055] Add 250kg of acid leaching residue to the reslurry washing tank and add the eluate 300kg, stirred into a slurry and then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a comprehensive utilization method of NdFeB waste acid leaching slag. The NdFeB waste acid leaching slag is combined with the NdFeB waste acid leaching slag obtained from the acid leaching and separation process in a neutralization reactor. Mix the acid leaching solution, filter the neutralization slurry to obtain the neutralization solution and the neutralization residue, and the neutralization solution is used as a raw material for preparing iron oxide red; mix the neutralization residue with the acid leaching residue eluate obtained in the acid leaching process and add The acid leaching reaction of sulfuric acid, after filtration, the acid leaching solution and the acid leaching residue are obtained, the acid leaching solution is used for neutralizing the ingredients, and the acid leaching residue is mixed with the late eluate produced in the preparation process of iron oxide red and beaten into pulp. Then filter and wash to dissolve the rare earth sulfate in the acid leaching residue, and send the filtrate obtained after separation to the rare earth extraction process for preparing rare earth products. The comprehensive utilization of iron, trace rare earth and cobalt resources in the acid leaching residue of NdFeB waste has been realized, and the effective separation and enrichment of rare earth and cobalt elements have been realized.

Description

technical field [0001] The invention belongs to the technical field of comprehensive utilization of industrial solid waste, and in particular relates to a comprehensive utilization method of acid leaching slag of NdFeB waste. Background technique [0002] NdFeB waste acid leaching slag is the acid leaching waste slag produced by decomposing NdFeB waste in the process of extracting neodymium from NdFeB waste, and its main component is Fe 2 o 3 , REO, Co, etc. At present, there is no suitable comprehensive utilization method, and some enterprises either sell it as iron-making raw material, or store it, which not only occupies space, but also pollutes the environment. Contents of the invention [0003] In order to comprehensively utilize the valuable resources in the acid leaching residue of NdFeB waste and eliminate environmental pollution, the present invention proposes a method for comprehensive utilization of the acid leaching residue of NdFeB waste. The comprehensive ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/00C22B59/00C22B23/00C01G49/06C09C1/24
CPCC01G49/06C09C1/24C22B7/007C22B23/043C22B59/00Y02P10/20
Inventor 肖景波陈居玲夏娇彬
Owner NANYANG ORIENTAL APPL CHEM RES INST