Chitin/modal/wood fiber multi-fiber blending knitted fabric

A technology of knitted fabrics and wood fibers, which is applied in knitting, weft knitting, textiles and papermaking, etc., and can solve problems such as comfort, stiffness to be further improved, antibacterial performance disappearing, and application limitations

Inactive Publication Date: 2016-07-20
JIANGYIN XIANGFEI APPAREL
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its comfort and stiffness need to be further improved, and its antibacterial properties disappear with repeated washing, so its application as a high-grade fabric is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The invention relates to a chitin / modal / wood fiber multi-fiber blended knitted fabric, which adopts a plain weave weave. Horizontal density: 41.7 longitudinal rows / 10cm; vertical density: 58 rows / 10cm. Needle size: 12G; Yarn: 36 S / 2, 50% modal fiber, 46% wood fiber and 4% chitin fiber siro-spun yarn, gram weight: 245 grams per square meter.

[0013] Product process

[0014] Three kinds of fiber siro spinning→doubling→winding→woven piece→sleeving→flat car→hand sewing→washing→drying→ironing→packing→storage.

[0015] The main technical key to be solved in the development process

[0016] (1) Yarn design

[0017] According to the characteristics of modal fiber, wood fiber and chitin fiber, according to the product cost and the functional effect requirements of the fabric to be achieved, 50% modal fiber plus 46% wood fiber and 4% chitin fiber are preferred to achieve the yarn for fabric and its function requirements.

[0018] (2) Spinning process design

[0019] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
twist factoraaaaaaaaaa
color fastnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a chitin / modal / wood fiber multi-fiber blending knitted fabric. The knitted fabric is characterized in that adopted fabric weave is tabby, and the transverse density is 41.7 columns / 10 cm; the longitudinal density is 58 rows / 10 cm, and the needle size is 12G; yarn is 36S / 2 and formed by 50% of modal fiber siro-spinning yarn, 46% of wood fiber siro-spinning yarn and 4% of chitin fiber siro-spinning yarn, and the gram weight is 245 grams / square meter. The chitin / modal / wood fiber multi-fiber blending knitted fabric can form a gorgeous color effect on the fabric surface, and meanwhile good comfort and great crease resistance are maintained. The knitted fabric has the style and hand feeling of common fabric and further has the softness, comfort, superhigh moisture absorption performance, warm keeping performance, bacteria resistance and bacteriostasis. Therefore, the knitted fabric integrates comfort, bacteria resistance and warm keeping and has wide market prospect.

Description

technical field [0001] The invention relates to a chitin / modal / wood fiber multifiber blended knitted fabric. Background technique [0002] Modal products have good softness and excellent hygroscopicity, but the stiffness of the fabric is poor. Modal has the characteristics of silvery white luster, excellent dyeability and bright color after dyeing, which is enough to make it suitable for outerwear. Because of this, Modal is increasingly becoming a material for outerwear and its upholstery. In order to improve the shortcoming of poor crispness of pure modal and pure wood fiber products, modal can be blended with other fibers to achieve good results. Typically, Modal is blended with pure cotton fibers, supplemented with silver ion antibacterial treatment, to produce functional fabrics. However, its comfort and stiffness need to be further improved, and its antibacterial properties disappear with repeated washing, so its application as a high-grade fabric is limited. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D02G3/04
Inventor 钟俊杰
Owner JIANGYIN XIANGFEI APPAREL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com