Composite accompanying environment-friendly imitation goose down thermal material and method for producing same

A goose down, environmentally friendly technology, applied in the field of traditional wear and non-woven materials, can solve the problems of easy mildew, easy to harden, easy to feel allergy, etc., to achieve the effect of not easy to drill down, expand the scope of use, and promote development.

Active Publication Date: 2016-07-20
吉祥三宝高科纺织有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are various disadvantages of moisture absorption, mildew, hardening, allergies and poor hand feeling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite accompanying environment-friendly imitation goose down thermal material and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] PLA resin chips enter the screw extruder for melt-spinning, and go through the extruder zone one, extruder zone two, extruder zone three, extruder zone four, extruder zone five and extruder respectively. Melt in the six zones of the machine (the temperature of the six zones of the extruder and the temperature of the extruder outlet are set to 160℃, 165℃, 170℃, 175℃, 180℃, 185℃, 190℃), and then filtered The components intercept and filter the impurities in the slices, and finally the completely melted melt is ejected from the spinneret, and is drawn by the high-speed hot air stream to form PLA melt-blown ultra-fine short fibers on the mesh curtain of the melt-blown equipment 2. Among them, the melt-blown hot air drafting temperature is 200℃, and the spinning speed is 600m / min; the cashmere is opened on the increased conveyor screen near the spinneret and sent to the roller 1 to be carded into a single fiber state, and the speed is 2000r / min roller 1 throws the carded fib...

Embodiment 2

[0031] PLA resin chips enter the screw extruder for melt-spinning, and go through the extruder zone one, extruder zone two, extruder zone three, extruder zone four, extruder zone five and extruder respectively. Melt in the six zones of the machine (the temperature of the six zones of the extruder and the temperature of the extruder outlet are set to 163℃, 168℃, 173℃, 178℃, 183℃, 188℃, 200℃), and then filtered The components intercept and filter the impurities in the slices, and finally the completely melted melt is ejected from the spinneret, and is drawn by the high-speed hot air stream to form PLA melt-blown ultra-fine short fibers on the mesh curtain of the melt-blown equipment 2. Among them, the melt-blown hot air drafting temperature is 230℃, and the spinning speed is 800m / min; the alpaca wool is opened on the increased conveyor screen near the spinneret and sent to the roller 1 to be carded into a single fiber state, and the speed is 2300r / min roller 1 throws the carded ...

Embodiment 3

[0034] PLA resin chips enter the screw extruder for melt-spinning, and go through the extruder zone one, extruder zone two, extruder zone three, extruder zone four, extruder zone five and extruder respectively. Melt in the six zones of the machine (the temperature of the six zones of the extruder and the temperature of the extruder outlet are set to 163℃, 168℃, 173℃, 178℃, 183℃, 188℃, 200℃), and then filtered The components intercept and filter the impurities in the slices, and finally the completely melted melt is ejected from the spinneret, and is drawn by the high-speed hot air stream to form PLA melt-blown ultra-fine short fibers on the mesh curtain of the melt-blown equipment 2. Among them, the melt-blown hot air drafting temperature is 230℃, and the spinning speed is 800m / min; the alpaca wool is opened on the increased conveyor screen near the spinneret and sent to the roller 1 to be carded into a single fiber state, and the speed is 2500r / min roller 1 throws the carded ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Areal densityaaaaaaaaaa
Thicknessaaaaaaaaaa
Fiber finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite accompanying environment-friendly imitation goose down thermal material and a method for producing the same.The composite accompanying environment-friendly imitation goose down thermal material is prepared from PLA (polylactic acid) melt-blown superfine short fibers and a type or a plurality of types of cashmere, camel hair, alpaca wool and rabbit hair fibers.The surface density of the composite accompanying environment-friendly imitation goose down thermal material is 50-300 g / m<2>, the thickness of the composite accompanying environment-friendly imitation goose down thermal material is 3-30 mm, a CLO value of the composite accompanying environment-friendly imitation goose down thermal material is 0.8-3, the warmth retention rate of the composite accompanying environment-friendly imitation goose down thermal material is 50-85%, and a thermal resistance value R of the composite accompanying environment-friendly imitation goose down thermal material is 0.5-3.The composite accompanying environment-friendly imitation goose down thermal material and the method have the advantages that shortcomings of bulkiness, easiness in deformation due to water washing, down piercing and the like of the traditional down feather can be effectively overcome; existing melt-blowing equipment is modified, so that the light, thin, environment-friendly and efficient imitation goose down thermal material can be developed and is wide in service range, and development of the thermal material industry can be effectively promoted.

Description

Technical field [0001] The invention belongs to the field of non-woven materials, and relates to a composite associated environmental protection goose down thermal insulation material and a production method thereof. The thermal insulation material with the goose down structure has a good effect of blocking air flow and good thermal insulation effect. It can be used in various environments and is especially suitable for traditional clothing. Background technique [0002] Traditional thermal insulation materials such as clothing, home textiles, and footwear are always unsatisfactory in terms of the balance of warmth and comfort. There are various shortcomings such as moisture absorption, mildew, hardening, allergies and poor hand feeling. With the improvement of people's living standards, people not only require clothing to meet the traditional cold protection function, but also pay more attention to the decorative beauty of clothing. They require clothing that is novel in style,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/4382D01D5/08D04H1/435D04H1/4266
CPCD01D5/08D04H1/4266D04H1/435D04H1/4382
Inventor 张伟张瑜仇何魏发云路绮雯许鑫
Owner 吉祥三宝高科纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com