Antique ceramics and preparation method thereof
A technology of ceramics and Gexian rice noodles, which is applied to clay products, other household utensils, household utensils, etc., can solve the problems of poor decoration of handicrafts, poor color antiquity, and complicated preparation process, so as to achieve thorough and uniform dispersion of raw materials and strong decoration , The effect of simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] S1. Weigh 30 parts of kaolin, 5 parts of kudzu rice flour, 7 parts of alkaline earth, 5 parts of quartz, 22 parts of bentonite, 1 part of muyu stone powder, 10 parts of serpentine powder, 3 parts of pyrophyllite powder, 4 parts of magnesia powder, 1 part of AS resin, 1 part of bamboo fiber, and after mixing the kaolin, alkaline earth, quartz, bentonite, wood fish stone powder, serpentine powder, pyrophyllite powder, and boaluminite powder, use the mixture: ball: water weight The ratio is 1:1.6:0.7, put it into ball milling equipment, ball mill for 1 hour, put the slurry stale for 24 hours, and then pass through a 100-mesh sieve to obtain mud;
[0022] S2, placing the obtained mud and the kudzu rice flour, AS resin, and bamboo fiber weighed in step S1 in a high-speed mixer and stirring for 5 minutes to obtain a mixed slurry;
[0023] S3. Inject the mixed slurry obtained in step S2 into the mould, demould after 20 minutes, take out the green body, dry, repair the green bo...
Embodiment 2
[0027] S1. Weigh 40 parts of kaolin, 10 parts of kudzu rice flour, 15 parts of alkaline earth, 7 parts of quartz, 30 parts of bentonite, 4 parts of wood fish stone powder, 15 parts of serpentine powder, 6 parts of pyrophyllite powder, 6 parts of magnesia powder, 3 parts of AS resin, 3 parts of bamboo fiber, and after mixing the kaolin, alkaline earth, quartz, bentonite, wood fish stone powder, serpentine powder, pyrophyllite powder and boaluminite powder, the weight of the mixed material: ball: water The ratio is 1: 1.6: 0.9, put it into ball milling equipment, ball mill for 2 hours, put the slurry stale for 36 hours, and pass through a 200-mesh sieve to obtain mud;
[0028] S2, placing the obtained mud and the Gexian rice flour, AS resin, and bamboo fiber weighed in step S1 in a high-speed mixer and stirring for 30 minutes to obtain a mixed slurry;
[0029] S3. Inject the mixed slurry obtained in step S2 into the mould, demould after 30 minutes, take out the green body, dry, ...
Embodiment 3
[0033] S1. Weigh 35 parts of kaolin, 7.5 parts of kudzu rice flour, 11 parts of alkaline earth, 6 parts of quartz, 26 parts of bentonite, 2.5 parts of wood fish stone powder, 12.5 parts of serpentine powder, 4.5 parts of pyrophyllite powder, 5 parts of boronite powder, 2 parts of AS resin, 2 parts of bamboo fiber, and after mixing the kaolin, alkaline earth, quartz, bentonite, wood fish stone powder, serpentine powder, pyrophyllite powder, and boaluminite powder, use the mixture: ball: water weight The ratio is 1:1.6:0.8, put it into ball milling equipment, ball mill for 1.5 hours, stale the slurry for 24-36 hours and pass it through a 150-mesh sieve to obtain mud;
[0034] S2, place the obtained mud and the kudzu rice flour, AS resin, and bamboo fiber weighed in step S1 in a high-speed mixer and stir for 17.5 minutes to obtain a mixed slurry;
[0035] S3. Inject the mixed slurry obtained in step S2 into the mould, demould after 25 minutes, take out the green body, dry, repair...