Polyester powder furniture coating and preparation method thereof

A technology of furniture coatings and polyester powders, applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of modification not reaching the expected effect, poor compatibility, etc., and achieve increased density and enhanced solvent resistance , Improve the effect of crosslinking density

Inactive Publication Date: 2016-09-28
刘辉
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Vegetable oil is introduced into unsaturated polyester resin through chemical reaction, which easily causes the polymerization reaction of vegetable oil itself, which makes the modification effect limited. Vegetable oil can also modify unsaturated polyester resin by blending method. Due to the poor compatibility of the two, resulting in modification that does not achieve the desired effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A kind of polyester powder furniture coating, it is made up of the raw material of following weight part:

[0021] Lecithin 0.4, 4 vinyl epoxy cyclohexane 0.1, polybenzimidazole 1, triethanolamine monooleate 0.7, diacetone alcohol 2, tung oil 10, sodium hydroxide 0.06, methanol 3, perfluorosulfonic acid resin 0.1 , acetic acid 6, 26% hydrogen peroxide 10, ethyl orthosilicate 10, Y chloropropyltrimethoxysilane 0.1, unsaturated polyester resin 70, methyl ethyl ketone peroxide 0.6, aminoethylpiperazine 0.1, calcite powder 10. Formamide 0.6, tetrabutyl titanate 2, calcium aluminate 3.

[0022] A kind of preparation method of described polyester powder furniture coating, comprises the following steps:

[0023] (1) Add the above-mentioned methanol to tung oil, add sodium hydroxide under stirring condition, react at 37°C for 70 minutes, distill off the methanol, stand to separate layers, and wash the collected upper liquid with sulfuric acid first, and then use hot water Was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact resistanceaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyester powder furniture coating, which is composed of the following raw materials (by weight): 0.4-14 parts of lecithin, 0.1-0.2 part of 1,2-epoxy-4-vinylcyclohexane, 1-2 parts of polybenzimidazole, 0.7-1 part of triethanolamine oleate, 2-3 parts of diacetone alcohol, 10-12 parts of tung oil, 0.06-0.07 part of sodium hydroxide, 3-4 parts of methanol, 0.1-0.2 part of perfluorosulfonate resin, 6-8 parts of acetic acid, 10-15 parts of 26-30% hydrogen peroxide, 10-17 parts of tetraethyl orthosilicate, 0.1-0.2 parts of Y-chloropropyltrimethoxysilane, 70-80 parts of unsaturated polyester resin, 0.6-1 part of methylethyl ketone peroxide, 0.1-0.2 part of aminoethylpiperazine, 10-14 parts of calsite powder, 0.6-1 part of formamide, 2-4 parts of tetrabutyl titanate and 3-4 parts of calcium aluminate.

Description

technical field [0001] The invention relates to the technical field of furniture coatings, in particular to a polyester powder furniture coating and a preparation method thereof. Background technique [0002] Saturated polyester resin is one of the film-forming resins commonly used in the preparation of coatings. However, when the general-purpose unsaturated polyester resin is used to prepare coatings, there are disadvantages such as poor water resistance, solvent resistance, heat resistance, and poor mechanical properties. Modification of ester resin to improve its comprehensive performance At present, polyurethane or polyurethane prepolymer, acrylic resin, epoxy resin, silicone, nanomaterials and vegetable oil are mainly used to modify unsaturated polyester resin in order to improve its preparation. performance when coating. Among them, vegetable oil modified unsaturated polyester resin has attracted more and more attention. Vegetable oil is introduced into unsaturated p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/06C09D7/12C09D5/03
CPCC08L2205/03C09D5/033C09D7/63C09D167/06C08L79/04C08K13/02C08K5/15C08K5/5419C08K2003/265C08K5/10
Inventor 刘辉
Owner 刘辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com