Environment-friendly diatom ooze decorative wall material

A diatom mud, an environmentally friendly technology, applied in the field of coatings, can solve the problems of short duration of formaldehyde purification, singleness, functionality of harmful substances, etc.

Inactive Publication Date: 2016-10-12
HANGZHOU MAKEDOLLAR ENVIRONMENTAL PROTECTION NEW MATERIAL
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the shortcomings of short formaldehyde purification duration, harmful substances and single function in the prior art, and provides an environmentally friendly diatom mud that does not contain formaldehyde, is non-toxic and harmless, has good antifouling effect and strong cohesive force decorative wall material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly diatom ooze decorative wall material
  • Environment-friendly diatom ooze decorative wall material
  • Environment-friendly diatom ooze decorative wall material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Environmentally friendly diatom mud decorative wall material, calculated in parts by weight, its raw material composition and content are as follows:

[0018]

[0019] Among them, SiO in diatomaceous earth 2 The content is ≥85%, the iron oxide content is 1-1.2%, and the fineness of the quartz sand is 20-100 mesh. The adhesive includes white cement and vinyl acetate and ethylene copolymerized rubber powder, and the mass ratio of white cement to vinyl acetate and ethylene copolymerized rubber powder is 3:1.

[0020] The environment-friendly diatom mud decorative wall material comprises the following steps:

[0021] A) weighing each component by formula;

[0022] B) Stir the diatomite, adhesive, dolomitic rock powder, and attapulgite powder in a powder mixer at 30°C for 15 minutes, then lower the temperature to 25°C, and then mix starch ether, quartz sand, fluorine-containing silicon Add the oxane and zeolite-loaded nano-titanium dioxide into the powder mixer and sti...

Embodiment 2

[0024] Environmentally friendly diatom mud decorative wall material, calculated in parts by weight, its raw material composition and content are as follows:

[0025]

[0026]

[0027] Among them, SiO in diatomaceous earth 2 The content is ≥85%, the iron oxide content is 1-1.2%, and the fineness of the quartz sand is 20-100 mesh. The adhesive includes calcium hydroxide and vinyl acetate and higher fatty acid vinyl ester copolymerized rubber powder, and the mass ratio of calcium hydroxide to vinyl acetate and higher fatty acid vinyl ester copolymerized rubber powder is 3:1.

[0028] The environment-friendly diatom mud decorative wall material comprises the following steps:

[0029] A) weighing each component by formula;

[0030] B) Stir diatomite, adhesive, dolomite powder, attapulgite powder at 40°C in a powder mixer for 10 minutes, then lower the temperature to 20°C, then mix starch ether, quartz sand, fluorine-containing silicon Add the oxane and zeolite-loaded nano-...

Embodiment 3

[0032] Environment-friendly diatom mud decorative wall material, calculated by parts by weight, the composition and content of raw materials are as follows:

[0033]

[0034]

[0035] Among them, SiO in diatomaceous earth 2 The content is ≥85%, the iron oxide content is 1-1.2%, and the fineness of the quartz sand is 20-100 mesh. The adhesive includes calcium hydroxide and acrylate-styrene copolymer powder, and the mass ratio of calcium hydroxide to acrylate-styrene copolymer powder is 3:1.

[0036] The environment-friendly diatom mud decorative wall material comprises the following steps:

[0037] A) weighing each component by formula;

[0038] B) Stir the diatomite, adhesive, dolomitic rock powder, and attapulgite powder in a powder mixer at 36°C for 20 minutes, then lower the temperature to 24°C, and then mix starch ether, quartz sand, fluorine-containing silicon The oxane and zeolite-loaded nano-titanium dioxide were added to the powder mixer and stirred for 36 min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of coatings, and discloses an environment-friendly diatom ooze decorative wall material. The environment-friendly diatom ooze decorative wall material is prepared from components in parts by weight as follows: 20-40 parts of diatomite, 2-35 parts of an adhesive, 6-8 parts of marble quartzite powder, 6-8 parts of attapulgite powder, 8-10 parts of starch ether, 10-25 parts of quartz sand, 6-8 parts of fluorine-containing siloxane and 3-5 parts of zeolite-loaded nanometer titania. The energy-saving and environment-friendly diatom ooze decorative wall material contains no harmful substances and has the advantages of good cohesiveness, high formaldehyde removal efficiency, high antibacterial activity and deodorization performance and excellent self-cleaning and purification durability, and the performance index meets requirements specified in the JC / T2177-2013 standard.

Description

technical field [0001] The invention relates to coatings, in particular to an environment-friendly diatom mud decorative wall material. Background technique [0002] At present, the traditional wall materials represented by latex paint and wallpaper in the building materials market can no longer meet the ever-increasing demands of modern fashion consumers in terms of environmental protection, functionality and individuality. The birth of diatom mud is not accidental, it is the inevitable product of people's advocacy of fashion, function, environmental protection, personality and taste. Diatom mud is a single-celled plankton in the sea hundreds of millions of years ago. It has been melted for hundreds of millions of years. It is a functional decorative wall material with zero pollution. It not only does not contain any harmful substances, but also purifies and removes indoor Harmful gas, which makes diatom mud completely break the inherent disadvantages of wallpaper glued to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B14/04C04B14/06C04B14/08C04B14/10C04B14/30C04B24/26C04B24/38C04B24/42
CPCC04B28/04C04B2111/00017C04B2111/00482C04B24/26C04B14/08C04B14/06C04B14/102C04B24/38C04B24/42C04B14/047C04B14/305
Inventor 王月琴
Owner HANGZHOU MAKEDOLLAR ENVIRONMENTAL PROTECTION NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com