A high-dimensional shape hard alloy forming agent and its mixing process

A technology of cemented carbide and forming agent, which is applied in metal processing equipment, transportation and packaging, etc., can solve the problems of insufficient toughness, cracks, crack removal of forming agent, etc., to improve fluidity, increase uniformity, and reduce viscosity Effect

Active Publication Date: 2018-11-27
厦门金鹭硬质合金有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of processing cemented carbide into tools, it needs to be extruded with a molding agent. The existing extrusion molding agent process can stably produce rods, straight-hole pipes and other products, but the lack of toughness in the production of spiral products leads to extrusion. Cracks during pressing or during drying and removal of forming agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-dimensional shape hard alloy forming agent and its mixing process
  • A high-dimensional shape hard alloy forming agent and its mixing process
  • A high-dimensional shape hard alloy forming agent and its mixing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A high-dimensional shape cemented carbide forming agent of the present invention is composed of the following components in weight percentage, wherein:

[0023]

[0024] A kind of cemented carbide mixing material process based on above-mentioned molding agent of the present invention, comprises the steps:

[0025] A. It is to premix the above molding agent; that is, the paraffin wax of 15% of the total weight of the molding agent, the high melting point paraffin wax of 25% of the total weight of the molding agent, the oleylamine of 1% of the total weight of the molding agent, and the gasoline of 3% of the total weight of the molding agent , 3% soybean oil of forming agent gross weight and 38% n-paraffin of forming agent gross weight are mixed together;

[0026] B. Seal the cemented carbide powder and the pre-mixed forming agent with heat and mix, so that the forming agent and the cemented carbide powder are evenly mixed; take a certain amount of cemented carbide powd...

Embodiment 2

[0036] A kind of high-dimensional shape cemented carbide forming agent and its mixing process of the present invention are different from Embodiment 1 in that the cemented carbide forming agent is composed of the following components by weight percentage, wherein:

[0037]

Embodiment 3

[0039] A kind of high-dimensional shape cemented carbide forming agent and its mixing process of the present invention are different from Embodiment 1 in that the cemented carbide forming agent is composed of the following components by weight percentage, wherein:

[0040]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-dimensional shape hard alloy forming agent and its mixing process, which is composed of the following components in weight percentage, wherein: paraffin wax, 15-25%; high-melting point paraffin wax, 15-25%; oil Amines, 1-4%; gasoline, 1-3%; soybean oil, 3-10%; oleamide, 15-25%; normal alkanes, the balance. The present invention can make the extruded material have suitable plastic deformation ability and high dimensionality by selecting appropriate components and appropriate proportions, and the control precision of the pitch of the front and rear ends of the product is high; the extruded material has high Toughness, able to withstand the torsion during the extrusion process, thereby eliminating extrusion cracks; making the removal of the molding agent stable, and avoiding cracks during the intercalation process.

Description

technical field [0001] The invention relates to the technical field of hard alloy processing, in particular to a high-dimensional hard alloy forming agent and a mixing process thereof. Background technique [0002] Cemented carbide is an alloy material made of hard compounds of refractory metals and bonding metals through powder metallurgy. Cemented carbide has a series of excellent properties such as high hardness, wear resistance, good strength and toughness, heat resistance and corrosion resistance, especially its high hardness and wear resistance, which basically remain unchanged even at a temperature of 500°C , It still has high hardness at 1000 °C. Cemented carbide is widely used as tool material, such as turning tools, milling cutters, planers, drills, boring tools, etc., for cutting cast iron, non-ferrous metals, plastics, chemical fibers, graphite, glass, stone and ordinary steel, and can also be used for cutting Difficult-to-machine materials such as stainless st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00B22F3/20
CPCB22F3/20B22F1/10
Inventor 陈成艺吴其山王年张守全林高安
Owner 厦门金鹭硬质合金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products