A preparation method and application of an energy-saving and environment-friendly building material binder for desulfurization fly ash

A desulfurization fly ash, energy saving and environmental protection technology, applied in the field of new building materials, can solve the problems of cost, difficulty in large-scale promotion of technology, unstudied influence of concrete performance, reduction of strength of cementitious materials, etc., to achieve high adhesion rate, Low operating cost, good adhesive effect

Inactive Publication Date: 2017-12-29
XUZHOU UNIV OF TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Granular adhesives and desulfurized fly ash are used to produce building materials such as water seepage bricks and glass-ceramic, although the utilization rate is high, but due to cost, process and other limitations, it is difficult to be popularized in a large area
[0008] Scholar Wang Chong et al. compounded the finely ground blocky binder with desulfurized fly ash and slag to prepare cementitious materials. The overall strength of cementitious materials showed a decreasing trend
[0009] Scholar Amit Rai et al. crushed air-cooled block binder and desulfurized fly ash into concrete aggregates. The binder and desulfurized fly ash aggregates meet the requirements of the IS 3 83:1990 standard, and suggested that it can be Used in nonstructural concrete, but the effect of this aggregate on concrete properties has not been studied
And the adhesive is flammable and explosive, which will damage the equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of an energy-saving and environment-friendly building material binder for desulfurization fly ash
  • A preparation method and application of an energy-saving and environment-friendly building material binder for desulfurization fly ash
  • A preparation method and application of an energy-saving and environment-friendly building material binder for desulfurization fly ash

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] According to the following steps, a kind of binder for desulfurization fly ash energy-saving and environment-friendly building materials of the present invention is prepared, and in parts by weight:

[0032] Step 1: In the reaction kettle, add 221.432 parts of cationic water and 13..569 parts of fatty alcohol polyethylene oxide ether sulfate sodium salt, start the mixer in the reaction kettle, set the speed at 14.228rpm, start the reaction kettle Heater to raise the temperature to 29.959°C, add 16.813 parts of succinic anhydride, 12.899 parts of N-cyclohexyl p-toluenesulfonamide, and stir evenly, carry out esterification reaction for 6.21 hours; then add N,N- 15.216 parts of dimethyl-p-nitrosoaniline, 18.406 parts of 1-amino-5-hydroxyl-4-[(1-methylpropyl)amino]-8-nitro-9,10-anthraquinone, adjusted The pH value of the solution in the reactor reaches 4.8900;

[0033] Step 2: Take another 15.440 parts of 1-anilino-4-hydroxyanthraquinone, 12.513 parts of p-methylthiobenzyl...

Embodiment 2

[0039] According to the following steps, a kind of binder for desulfurization fly ash energy-saving and environment-friendly building materials of the present invention is prepared, and in parts by weight:

[0040] Step 1: In the reactor, add 446.838 parts of cationic water and 55.930 parts of fatty alcohol polyethylene oxide ether sulfate sodium salt, start the mixer in the reactor, set the speed at 60.306rpm, and start the heater in the reactor , to raise the temperature to 30.994°C, add 125.192 parts of succinic anhydride, 29.545 parts of N-cyclohexyl-p-toluenesulfonamide, and stir evenly, carry out esterification reaction for 17.349 hours; then add N,N-dimethyl -72.49 parts of p-nitrosoaniline, 79.475 parts of 1-amino-5-hydroxyl-4-[(1-methylpropyl)amino]-8-nitro-9,10-anthraquinone, adjusted in the reaction kettle pH of the solution to 8.9457;

[0041] Step 2: Take another 38.578 parts of 1-anilino-4-hydroxyanthraquinone, 57.446 parts of p-methylthiobenzyl alcohol, and 75....

Embodiment 3

[0047] According to the following steps, a kind of binder for desulfurization fly ash energy-saving and environment-friendly building materials of the present invention is prepared, and in parts by weight:

[0048] Step 1: In the reactor, add 222.432 parts of cationic water and 14.838 parts of fatty alcohol polyethylene oxide ether sulfate sodium salt, start the mixer in the reactor, set the speed at 15.569rpm, and start the heater in the reactor , to raise the temperature to 30.930°C, add 17.813 parts of succinic anhydride, 13.192 parts of N-cyclohexyl p-toluenesulfonamide, and stir evenly, carry out esterification reaction for 7.899 hours; then add N,N-dimethyl -16.545 parts of p-nitrosoaniline, 19.216 parts of 1-amino-5-hydroxyl-4-[(1-methylpropyl)amino]-8-nitro-9,10-anthraquinone, adjusted in the reaction kettle The pH of the solution ranges to 5.449;

[0049] Step 2: Take another 16.406 parts of 1-anilino-4-hydroxyanthraquinone, 13.475 parts of p-methylthiobenzyl alcohol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method and application of a desulfurized fly ash energy-saving environmental-friendly building material adhesive. The desulfurized fly ash energy-saving environmental-friendly building material adhesive consists of the following components in parts by weight: cation water, fatty alcohol polyethylene oxide ether sodium sulfate salt, succinic anhydride, N-cyclohexyl para toluene sulfonamide, N,N-dimethyl-p-nitrosoaniline, 1-amino-5-hydroxyl-4-[(1-methyl propyl] amino]-8-nitro-9,10-anthraquinone, 1-phenylamino-4-hydroxyanthraquinone, p-Methylthiobenzyl alcohol, gold nanoparticles, 4,4'-diamido-triphenylmethane, succinic anhydride, 4,4'-(3,3'-dichlorobiphenyl-4,4'-dinitrogen)di(4,5-dihydro-5-oxo-1-phenylpyrazole-3-formic acid) diethyl ester, benzotriazole-1-tri(trimethylamino)-trifluorophosphate, N-(2-benzimidazolyl) methyl carbamate and alpha-bromonaphthalene. The preparation method has the advantages that the adhesive is prevented from saponification, the surface tension of mixtures is reduced, and the mixtures can be relatively solidly adhered to one another; the adhesive has the advantages of stable chemical properties, wide application and high surface cleanliness ratios of molded structures.

Description

technical field [0001] The invention belongs to the field of new building materials, and in particular relates to a preparation method and application of an energy-saving and environment-friendly building material adhesive for desulfurized fly ash. Background technique [0002] The deficiencies of existing technology: [0003] Scholar Li Junhong used granular binder, desulfurized fly ash and tin slag to burn silicate wall material clinker in a vertical kiln, and mixed an appropriate amount of binder in the raw material to burn out Silicate clinker with good stability, normal setting time and high early strength. But the adhesive is toxic and pollutes the environment. [0004] Scholar Li Wenbin et al. used adhesives and desulfurized fly ash, nickel slag, and coal-research stone ingredients to burn clinker in a vertical kiln, and used fly ash as a mixture to produce ordinary silicate new wall materials, which not only can The reduction of environmental pollution can also re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/14C04B22/04C04B24/04C04B24/12C04B24/20
CPCC04B26/14C04B24/121C04B24/20C04B24/04C04B24/12C04B22/04
Inventor 项玮李莹郭莉郭婷婷仇宝进邹吕熙梁峙
Owner XUZHOU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products