Method for preventing filler of Nixing pottery from disengaging and cracking

A Nixing pottery and filling mud technology, which is applied to clay products, other household utensils, household utensils, etc., can solve the problems of low yield, easy falling off, hindering the development of Qinzhou Nixing pottery filling mud technology, etc., to reduce shedding and Cracking, enhanced electrostatic attraction effect

Inactive Publication Date: 2016-11-09
钦州市永和坭兴陶艺有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the cumbersome process of filling mud in Nixing pottery, and the filling mud and the body of Nixing pottery do not absorb each other during the firing process, it is very easy to fall off, and the yield of finished products is extremely low, only about 20%, which seriously hinders the production of Nixing pottery in Qinzhou. Development of Xingpottery Filling Technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1) Preparing the billet: mixing the east mud and the west mud at a weight ratio of 6:4, grinding, dehydrating, vacuum refining the mud, and aging to make a billet with a moisture content of 20% and a particle size of 6 μm;

[0020] 2) Preparation of filling mud: mix east mud and west mud at a weight ratio of 8:2, grind, dehydrate, vacuum mud, and stale to make filling mud with a moisture content of 25% and a particle size of 6 μm;

[0021] 3) Body forming: the blank is made into a teacup body, the diameter of the teacup is 8cm, and the height is 10cm;

[0022] 4) Trim the green body: trim the green body to meet the design requirements;

[0023] 5) Engraving: Use a carving knife to pick out the soil along the edges of the ink marks on both sides of the body, and remove all the parts with ink marks to form a uniform groove at the bottom;

[0024] 6) Mud filling: Sprinkle a layer of alumina powder evenly in the carved groove, then fill the filling mud into the carved groo...

Embodiment 2

[0028] 1) Preparing the billet: mix the east mud and the west mud at a weight ratio of 6:4, grind, dehydrate, vacuum mud, and stale to make a billet with a moisture content of 22% and a particle size of 5 μm;

[0029] 2) Preparation of filling mud: mix the east mud and west mud at a weight ratio of 7.5:2.5, grind, dehydrate, vacuum mud, and stale to make filling mud with a moisture content of 28% and a particle size of 5 μm;

[0030] 3) Body forming: the blank is made into a green body of a teapot, the diameter of the teapot is 15cm, and the height is 10cm;

[0031] 4) Trim the green body: trim the green body to meet the design requirements;

[0032] 5) Engraving: Use a carving knife to pick out the soil along the edges of the ink on both sides of the body, and remove all the parts with ink to form a uniform groove at the bottom;

[0033] 6) Mud filling: Sprinkle a layer of alumina powder evenly in the carved groove, then fill the filling mud into the carved groove, smooth an...

Embodiment 3

[0037] 1) Preparing the billet: mixing the east mud and the west mud at a weight ratio of 6:4, grinding, dehydrating, vacuum refining the mud, and aging to make a billet with a moisture content of 25% and a particle size of 4 μm;

[0038] 2) Preparation of filling mud: mix east mud and west mud at a weight ratio of 7:3, grind, dehydrate, vacuum mud, and stale to make filling mud with a moisture content of 33% and a particle size of 4 μm;

[0039] 3) Body molding: make the blank into a vase body, the diameter of the vase is 20cm, and the height is 40cm;

[0040] 4) Trim the green body: trim the green body to meet the design requirements;

[0041] 5) Engraving: Use a carving knife to pick out the soil along the edges of the ink marks on both sides of the body, and remove all the parts with ink marks to form a uniform groove at the bottom;

[0042] 6) Mud filling: Sprinkle a layer of alumina powder evenly in the carved groove, then fill the filling mud into the carved groove, smoo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preventing filler of Nixing pottery from disengaging and cracking. The method comprises the steps of blank preparing, blank forming, drawing, carving, filler filling, drying and firing; for the filler filling step, a carved groove is evenly scattered with a layer of alumina powder, and then the carved groove is filled with filling pug; for the drying step, the blank filled with the pug is treated for 1 min to 5 min under the condition of 10 Mpa to 15 Mpa, and then natural air-drying is conducted. Compared with the prior art, according to the method for preventing the filler of the Nixing pottery from disengaging and cracking, alumina particles are added into the carved groove, the electrostatic attraction between the filled pug and a blank body can be greatly increased, and disengaging and cracking of the filled pug in the firing process can be greatly reduced.

Description

technical field [0001] The invention relates to a firing method of Nixing pottery, in particular to a method for preventing Nixing pottery filling mud from falling off and cracking. Background technique [0002] According to historical records, the mud-filling process of Nixing pottery in Qinzhou has been formed since the Qing Dynasty. The traditional mud-filling process of Nixing pottery mainly includes the following steps: 1) Preparation of blanks: The blanks are selected from the east of Qinjiang River, which crosses the urban area of ​​Qinzhou City. The soil in the area is commonly known as Dongni (soft clay with a yellowish-white color and contains a small amount of quartz sand, which plays a role in adjusting plasticity and bonding in the production process of Nixing pottery), and the soil in the west of the Qinjiang River is commonly known as Xini (contains a small amount of K 2 O, NaO, CaO, MgO, Fe 2 o 3 、TiO 2 , MnO 2 , is a kind of purple mudstone with high ir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B37/00C04B33/00C04B33/24
CPCC04B37/045C04B33/02C04B33/24C04B2235/612C04B2237/064
Inventor 刘俭钟昆廷黄晓聪钟恒星
Owner 钦州市永和坭兴陶艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com