High-strength and wear-resisting boride-based cermet bearing and production method thereof

A ceramic bearing and boride technology are applied in the field of high-strength wear-resistant boride-based metal ceramic bearings and their preparation, which can solve problems such as low market share, and achieve the effects of not easy to wear, simple preparation process and low processing cost.

Inactive Publication Date: 2016-11-09
王莹
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

High-strength wear-resistant boride-based cermet bearings are rare in the domestic market, and those sold in a small...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A high-strength wear-resistant boride-based cermet bearing is made of the following raw materials in parts by weight: the high-strength wear-resistant boride-based cermet bearing is made of the following raw materials in parts by weight: 10 parts of titanium boride, tantalum boride 40 parts, 2 parts of tin powder, 4 parts of iron powder, 13 parts of realgar powder, 10 parts of dickite powder, 10 parts of wolframite powder, 3 parts of graphene, 2 parts of iron citrate, 10 parts of glass fiber, 11 parts of paraffin wax .

[0015] The steps of the preparation method are as follows: first put all raw materials into a high-speed mixer, mix and stir them, then place the uniformly mixed mixture in a mold and press it into a preform, the pressing pressure is 40-50MPa, and then the preform High temperature sintering, the sintering temperature is 900-1200°C, the sintering time is 3-6h, and the temperature can be lowered to room temperature.

Embodiment 2

[0017] A high-strength wear-resistant boride-based cermet bearing is made of the following raw materials in parts by weight: the high-strength wear-resistant boride-based cermet bearing is made of the following raw materials in parts by weight: 20 parts of titanium boride, tantalum boride 50 parts, 8 parts of tin powder, 9 parts of iron powder, 20 parts of realgar powder, 20 parts of dickite powder, 15 parts of wolframite powder, 8 parts of graphene, 6 parts of iron citrate, 15 parts of glass fiber, 15 parts of paraffin wax .

[0018] The steps of the preparation method are as follows: first put all raw materials into a high-speed mixer, mix and stir them, then place the uniformly mixed mixture in a mold and press it into a preform, the pressing pressure is 40-50MPa, and then the preform High temperature sintering, the sintering temperature is 900-1200°C, the sintering time is 3-6h, and the temperature can be lowered to room temperature.

Embodiment 3

[0020] A high-strength wear-resistant boride-based cermet bearing is made of the following raw materials in parts by weight: the high-strength wear-resistant boride-based cermet bearing is made of the following raw materials in parts by weight: 15 parts of titanium boride, tantalum boride 45 parts, tin powder 5 parts, iron powder 6 parts, realgar powder 17 parts, dickite powder 15 parts, wolframite powder 13 parts, graphene 6 parts, iron citrate 4 parts, glass fiber 13 parts, paraffin wax 13 parts .

[0021] The steps of the preparation method are as follows: first put all raw materials into a high-speed mixer, mix and stir them, then place the uniformly mixed mixture in a mold and press it into a preform, the pressing pressure is 40-50MPa, and then the preform High temperature sintering, the sintering temperature is 900-1200°C, the sintering time is 3-6h, and the temperature can be lowered to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength and wear-resisting boride-based cermet bearing and a production method thereof. The high-strength and wear-resisting boride-based cermet bearing is prepared from the following raw materials in parts by weight: 10 to 20 parts of titanium boride, 40 to 50 parts of tantalum boride, 2 to 8 parts of tin powder, 4 to 9 parts of iron powder, 13 to 20 parts of realgar powder, 10 to 20 parts of dickite powder, 10 to 15 parts of wolframite powder, 3 to 8 parts of graphene, 2 to 6 parts of ferric citrate, 10 to 15 parts of glass fibers and 11 to 15 parts of paraffin. Compared with a traditional cermet bearing, the high-strength and wear-resisting boride-based cermet bearing produced by the production method disclosed by the invention has the advantages of better strength, wear resistance and heat resistance; the bearing does not deform under the condition of high temperature, and is not easy to wear; in addition, a preparation technique is simple, the processing cost is low, parameters are easy to control, and the production process is safe and environmentally-friendly; and the high-strength and wear-resisting boride-based cermet bearing and the production method therefor are suitable for large-scale industrial production.

Description

technical field [0001] The invention specifically relates to a high-strength wear-resistant boride-based cermet bearing and a preparation method thereof. Background technique [0002] Cermet English word cermet or ceramet is composed of ceramic (ceramic) and metal (metal). Cermet refers to the composite material of metal and ceramic prepared by powder metallurgy method. Cermet has the advantages of both metal and ceramic. It has low density, high hardness, wear resistance and good thermal conductivity. Brittle. Cermet not only has the toughness, high thermal conductivity and good thermal stability of metal, but also has the characteristics of high temperature resistance, corrosion resistance and wear resistance of ceramics. Cermets have broad application prospects in aerospace, national defense, precision manufacturing and other fields. Boride-based cermets are based on titanium boride, tantalum boride, vanadium boride, chromium boride, zirconium boride, tungsten boride, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C49/00C22C47/14B22F5/10
CPCC22C49/00B22F5/106C22C47/14
Inventor 王莹
Owner 王莹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap