Hydrogen-rich water filter element and preparation method thereof

A hydrogen-rich water and filter element technology, which is applied in separation methods, water treatment parameter control, chemical instruments and methods, etc., can solve the problem of insufficient filter element filtration, achieve anti-oxidation ability, remove active oxygen free radicals, and improve hydrogen The effect of content

Inactive Publication Date: 2017-02-01
朱心江
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for preparing a hydrogen-rich water filter element, so as to solve the problem that the existing filter element is not thoroughly filtered

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogen-rich water filter element and preparation method thereof
  • Hydrogen-rich water filter element and preparation method thereof
  • Hydrogen-rich water filter element and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A filter element for hydrogen-rich water, the active ingredients in the total weight percentage include: 20% magnesium oxide, 15% calcium carbonate, 14% kaolin, 10% magnetic material, 10% tourmaline, 10% mica, titanium oxide 8%, copper oxide 8%, rare earth 5%.

[0028] The active ingredients of the tourmaline include tourmaline 20%, iron tourmaline 60% and magnesium tourmaline 20%.

[0029] The effective components of the magnetic material include: 30% of ferric oxide, 15% of zinc oxide and 55% of silicon dioxide.

[0030] The weight ratio of magnetic material to tourmaline is 1:1.

[0031] In tourmaline, the weight ratio of lithium tourmaline, ferrite and magnesium tourmaline is 1:3:1.

[0032] In the magnetic material, the weight ratio of ferric oxide, zinc oxide and silicon dioxide is 1:0.5:1.83.

[0033] A method for preparing a hydrogen-rich water filter element, comprising the following steps:

[0034] A. First, calcium carbonate, kaolin, tourmaline, and mica ...

Embodiment 2

[0039] A filter element for hydrogen-rich water, the active ingredients in the total weight percentage include: magnesia 21%, calcium carbonate 15%, kaolin 13%, magnetic material 10%, tourmaline 10%, mica 10%, titanium oxide 8%, copper oxide 8%, rare earth 5%.

[0040] The active ingredients of the tourmaline include tourmaline 20%, iron tourmaline 60% and magnesium tourmaline 20%.

[0041] The effective components of the magnetic material include: 30% of ferric oxide, 20% of zinc oxide and 50% of silicon dioxide.

[0042] The weight ratio of magnetic material to tourmaline is 1:1.

[0043] In tourmaline, the weight ratio of lithium tourmaline, ferrite and magnesium tourmaline is 1:3:1.

[0044] In the magnetic material, the weight ratio of ferric oxide, zinc oxide and silicon dioxide is 1:0.5:1.83.

[0045] A method for preparing a hydrogen-rich water filter element, comprising the following steps:

[0046] A. First, calcium carbonate, kaolin, tourmaline, and mica were ba...

Embodiment 3

[0051] A filter element for hydrogen-rich water, the active ingredients in the total weight percentage include: 22% magnesium oxide, 15% calcium carbonate, 12% kaolin, 10% magnetic material, 10% tourmaline, 10% mica, titanium oxide 8%, copper oxide 8%, rare earth 5%.

[0052] The active ingredients of the tourmaline include tourmaline weight percent: 25% of lithium tourmaline, 55% of ferrite tourmaline and 20% of ferrite tourmaline.

[0053] The effective components of the magnetic material include: 35% of ferric oxide, 15% of zinc oxide and 50% of silicon dioxide.

[0054] A method for preparing a hydrogen-rich water filter element, comprising the following steps:

[0055] A. First, calcium carbonate, kaolin, tourmaline, and mica were ball milled on a ball mill for 7 hours to reach a particle size of 60 μm;

[0056] B, Calcium carbonate, kaolin, tourmaline, mica are roasted respectively for 13 hours, and the temperature is 230 ℃, then cooled and pulverized for subsequent us...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hydrogen-rich water filter element and a preparation method thereof. The hydrogen-rich water filter element comprises ingredients by weight: 20 to 30% of magnesium oxide, 15 to 25% of calcium carbonate, 10 to 20% of kaoline, 5 to 10% of magnetic material, 5 to 10% of tourmaline, 5 to 10% of mica, 4 to 8% of titanium oxide, 4 to 8% of copper oxide and 2 to 5% of rare earth. All the raw materials are ball-milled, are placed into a die to be pressed and then are fired to form the hydrogen-rich water filter element. The hydrogen-rich water filter element provided by the invention not only can filter out large-particle macroscopic substances in water, such as rust, silt, eggs and the like, but also can filter foreign odor, peculiar smell, volatile phenols, heavy metal ions and various fungi and germs, and enables the water to reach the health drinking standard; the water filtered by the hydrogen-rich water filter element provided by the invention has oxidation resistance, can effectively remove reactive oxide species, and solves various skin problems.

Description

technical field [0001] The invention relates to the field of drinking water filtration, in particular to a method for preparing a hydrogen-rich water filter element. Background technique [0002] my country is a country with a large population, and the demand for domestic water is very large. Although there are many rivers and lakes in many areas of our country, there are few water resources that can be used as drinking water, and the water pollution is serious. According to statistics, 63 million people in the country drink water with excessive fluoride, 2 million people drink water with excessive arsenic, and about 100 million people in cities There is no guarantee of drinking water safety. "China Water Supply and Sanitation" Issue 01, 2002 "Summary of the Current Situation of Drinking Water in my country" (Zhang Rong, Zhao Dayu) mentioned: With the development of industry, agriculture and cities, a large amount of industrial wastewater and domestic sewage are produced, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D39/20C02F1/00C02F1/68
CPCB01D39/20B01D2239/0407B01D2239/0442B01D2239/045B01D2239/10C02F1/001C02F1/68C02F2101/20C02F2209/10C02F2303/02C02F2303/04
Inventor 朱心江王京东
Owner 朱心江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com