A kind of modified biological wax-coated controlled-release fertilizer and preparation method thereof

A controlled-release fertilizer and bio-wax technology, applied in the direction of organic fertilizers, fertilizer mixtures, fertilization devices, etc., can solve the problems of unreachable thickness and slow and controlled release effect, and achieve low price, simple production process and low energy consumption. low effect

Active Publication Date: 2020-01-10
SHANDONG AGRI UNIV FERTILIZER TECH CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using biological wax alone to coat fertilizers cannot reach a certain thickness, nor can it achieve the required slow and controlled release effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment １

[0024] Add 16KG of palm wax into the container for heating and melting, keep at 100°C, add 2KG of polyisobutylene and 2KG of petroleum resin, and keep stirring for 5-10 minutes to prepare the modified biological wax coating agent A.

[0025] Add 10KG palm wax into the container for heating and melting, keep at 100°C, add 2KG polyisobutylene, 2KG petroleum resin, 1KG paraffin, and keep stirring for 5-10 minutes to prepare the modified biological wax coating agent B.

[0026] Add 9KG palm wax into the container for heating and melting, keep at 100°C, add 2KG polyisobutylene, 2KG petroleum resin, 2KG paraffin, and keep stirring for 5-10 minutes to prepare the modified biological wax coating agent C,

[0027] Add 1000KG of 28-12-8 compound fertilizer containing 3-5% humic acid into the drum, turn on the hot air heating system, and heat the fertilizer to 90°C; add the prepared modified biological wax coating agent A, and keep the temperature constant Change, coat for 5-10 minutes; ...

Embodiment 2

[0035] Add 16KG soybean wax into the container for heating and melting, keep at 100°C, add 2KG polyisobutylene, 2KGC5 petroleum resin, and keep stirring for 10-20 minutes to prepare modified biological wax coating agent A.

[0036] Add 14KG soybean wax into the container for heating and melting, keep at 100°C, add 2KG polyisobutylene, 2KGC5 petroleum resin, 2KG paraffin, and keep stirring for 10-20 minutes to prepare the modified biological wax coating agent B.

[0037] Add 12KG soybean wax into the container for heating and melting, keep at 100°C, add 2KG polyisobutylene, 2KGC petroleum resin, 4KG paraffin, and keep stirring for 10-20 minutes to prepare modified biological wax coating agent C,

[0038] Add 1000KG of 24-14-7 compound fertilizer containing 3-5% humic acid into the drum, turn on the hot air heating system, and heat the fertilizer to 90°C; add the prepared modified biological wax coating agent A, and keep the temperature constant Change, coat for 5-10 minutes; af...

Embodiment 3

[0046] Add 16KG of hydrogenated palm oil into a container for heating and melting, keep at 100°C, add 2KG of ethylene-vinyl acetate copolymer, 2KG of petroleum resin, and 2KG of quartz powder and keep stirring for 5-10 minutes to prepare the modified biological wax coating agent A.

[0047] Add 10KG hydrogenated palm oil into the container for heating and melting, keep at 100°C, add 2KG ethylene-vinyl acetate copolymer, 2KG petroleum resin, 1KG paraffin, 2KG quartz powder and keep stirring for 5-10 minutes to prepare the modified biological wax coating Agent B,

[0048] Add 9KG hydrogenated palm oil into the container for heating and melting, keep at 100°C, add 2KG ethylene-vinyl acetate copolymer, 2KG petroleum resin, 2KG paraffin, 2KG quartz powder and keep stirring for 5-10 minutes to prepare the modified biological wax coating Agent C,

[0049] Add 1000KG of 27-8-10 compound fertilizer containing 3-5% humic acid into the drum, turn on the hot air heating system, and heat ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified bio-wax-coated controlled-release fertilizer and a preparation method thereof. The bio-wax is first melted and then modified by adding a modifier to change its melting point and toughness, and then coated as a coating material On the surface of the 2-5mm fertilizer particles, multiple coatings are carried out according to different melting points, and finally the coated controlled-release fertilizer is prepared after cooling; the weight of the coated material accounts for 1% to 10% of the total weight of the fertilizer. Compared with ordinary controlled-release fertilizers, the invention has the advantages of environmentally friendly and non-toxic membrane materials, simple production process, low investment, low energy consumption in the production process, and the like.

Description

technical field [0001] The invention relates to the technical field of slow and controlled release fertilizers and their preparation, in particular to a modified biological wax-coated slow and controlled release fertilizers and a preparation method thereof. Background technique [0002] All countries in the world are aiming at the problems of low utilization rate of ordinary chemical fertilizers, easy loss and environmental pollution during use, and have developed nutrient controlled release or slow release fertilizers. Realize labor-saving and high-efficiency one-time fertilization, and can greatly improve the utilization rate of fertilizer. Slow and controlled release fertilizer is a new type of fertilizer produced to meet the needs of sustainable agricultural development. [0003] At present, the coating materials used for slow and controlled release fertilizers at home and abroad mainly come from petrochemical and other non-renewable raw materials, such as: polyethylene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C05G3/00C05G3/80
CPCC05F11/02
Inventor 丁方军孟庆羽马学文尹秀波陈士更陈卫民吴钦泉于建洪丕征张娟朱军朱福军郭新送路艳艳吴凤林张宏陈光峰
Owner SHANDONG AGRI UNIV FERTILIZER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap