Utilizing recycled waste rigid polyurethane foam to make insulation pipe material, insulation pipe and manufacturing method

A technology of rigid foam plastic and manufacturing method, which is applied in the direction of heat preservation and protection of pipes, pipes/pipe joints/pipe fittings through heat insulation, etc., can solve problems such as environmental pollution, waste of resources, etc. Good pore structure

Active Publication Date: 2019-05-07
TIANJIN JUNXING PIPE GRP CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to its excellent performance, it has been widely used, resulting in the pollution of the environment caused by waste rigid polyurethane foam.
[0003] One of the traditional treatment methods is land burial and the other is incineration. No matter which method is used, it will pollute the environment and waste resources at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Utilizing recycled waste rigid polyurethane foam to make insulation pipe material, insulation pipe and manufacturing method
  • Utilizing recycled waste rigid polyurethane foam to make insulation pipe material, insulation pipe and manufacturing method
  • Utilizing recycled waste rigid polyurethane foam to make insulation pipe material, insulation pipe and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0063] The preferred formula is as follows: 90 parts by weight of polyether polyols, 10 parts by weight of waste polyurethane rigid foam fermentation product liquid oligomer polyol mixture, water of 1.5 parts by weight, surfactant of 3 parts by weight, 1.5 parts by weight of reactive amine catalyst, 1 part by weight of conventional amine catalyst, 1.5 parts by weight of crosslinking agent, 30 parts by weight of blowing agent and 145 parts by weight of polymeric MDI system isocyanate.

[0064] The weight ratio of combined polyether polyol to polymeric MDI system isocyanate is: 1:1, preferably 1:1.05. Wherein, combined polyether polyol is by 80-90wt%, preferably 90wt% polyether polyol, 10-20wt% the product liquid oligomer polyol mixture of the reclaimed waste polyurethane rigid foam plastic fermentation fermentation, preferably 10wt% The product liquid oligomer polyol mixture of the reclaimed waste polyurethane rigid foam plastic fermentation fermentation; Wherein, polyether use...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a heat preservation tube material prepared by recycling waste hard polyurethane foamed plastic, a heat preservation tube and a manufacturing method. The heat preservation tube material is prepared from the following components in parts by weight: 80 to 90 parts of polyether polyol, 10 to 20 parts of a liquid oligomer polyhydric alcohol mixture of waste polyurethane hard foamed plastic glycolysis product, 1.0 to 1.5 parts of water, 1.5 to 3.0 parts of a surface active agent, 0.4 to 1.5 parts of a reaction type amine catalyst, 0.3 to 1 part of a conventional amine catalyst, 0 to 1.5 parts of a cross-linking agent, 30 to 50 parts of a foaming agent and 145 to 150 parts of polymerized MDI system isocyanate as a black material. The pollution to the environment is reduced, and cyclic utilization of resources is realized, so that the condition of producing the heat preservation tube by recycling hard polyurethane foam becomes possible, and the production cost is reduced.

Description

technical field [0001] The invention relates to a thermal insulation pipe material, a thermal insulation pipe and a manufacturing method using recycled waste rigid polyurethane foam plastics, which are used in central heating pipe networks. Background technique [0002] With the continuous improvement of people's awareness of environmental protection, especially in today's sustainable development, the rational use of resources has been mentioned as an important strategic height. Rigid polyurethane foam is a thermosetting material with a three-dimensional network structure. Due to its excellent performance, it has been widely used, resulting in the pollution of the environment caused by waste rigid polyurethane foam. [0003] One of the traditional treatment methods is land burial and the other is incineration. No matter which method is used, it will pollute the environment and waste resources at the same time. If the waste polyurethane foam is recycled and reused, the poll...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/76C08G18/48C08G18/32C08J9/04C08J9/08F16L59/02
CPCC08G18/3203C08G18/48C08G18/7664C08G2101/00C08J9/04C08J9/08C08J2203/02C08J2375/08F16L59/028
Inventor 夏成文韩英民吴晓芬苏世爱
Owner TIANJIN JUNXING PIPE GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products