Process for preparing polyvinyl chloride cable material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polyvinyl chloride cable, a preparation technology, applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of poor quality plasticizers, oil leakage from cables, shortened service life, etc., and improve the tensile strain retention rate of aging fracture , good resistance to volatilization, good charring effect
Inactive Publication Date: 2017-02-15
中广核三角洲(江苏)塑化有限公司
View PDF1 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Ordinary cable materials choose some conventional plasticizers to soften PVC. Due to its own characteristics and production technology, the produced cable materials have a strong smell, are pungent, and have a large amount of smoke, which is harmful to downstream cable production units. Front-line operators caused varying degrees of physical injury
Due to the poor quality of selected plasticizers for some cable materials, problems such as oil leakage and precipitation are caused in the produced cables, which shorten the service life of the products and pollute the environment.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0022] Embodiment: a preparation process for polyvinyl chloride cable material, characterized in that: the polyvinyl chloride cable material is composed of the following components in parts by weight: 80 parts of PVC resin with a polymerization degree of 1300, SG3 type PVC resin 20 parts, 25 parts of dinonyl cyclohexane 1,2 dicarboxylate, 24 parts of octyl acetyl citrate, 5.4 parts of antimony trioxide, 8 parts of zinc borate, 18 parts of filler, 10 parts of aluminum hydroxide, calcium 6 parts of zinc heat stabilizer, 0.3 part of antioxidant 1010, 0.6 part of lubricant, 1 part of processing modifier P551J, 1.8 parts of inorganic silicate deodorant, 9 parts of white carbon black;
[0023] Above-mentioned lubricant is selected from at least one in stearic acid, polyethylene wax, calcium stearate, zinc stearate.
[0024] The above-mentioned filler is one or more mixtures of calcium carbonate, talcum powder and kaolin.
[0025] The processing modifier P551J is produced by Mitsubi...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
degree of polymerization
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to a process for preparing a polyvinyl chloride cable material, and the process comprises the following steps: 1, adding PVC resin with the degree of polymerization of 1300, SG3 type PVC resin, cyclohexane-1,2-dinonyl diformate, acetyl butyl octyl citrate and white carbon black into a high-speed kneading machine for high-speed kneading for 3 to 5 minutes to reach temperature of 90 to 100 DEG C; 2, performing low-speed kneading for 1 minute, simultaneously pouring antimony trioxide, zinc borate, a filler, aluminum hydroxide, a calcium zinc heat stabilizer, antioxidant 1010, a lubricant, processing modifier P551J, an inorganic silicate deodorant and white carbon black, then performing high-speed kneading for 6 minutes, and when the temperature reaches 120 DEG C, fully mixing evenly, pre plasticizing, and discharging; and 3, when in extrusion, screw temperature of double screws being 120 DEG C to 150 C. The process greatly improves the flame retardant property of the material, and the material has good carbon forming effect during combustion, so that secondary combustion and flame propagation of the material can be prevented.
Description
technical field [0001] The invention relates to an environment-friendly cable material, in particular to a preparation process for polyvinyl chloride cable material. Background technique [0002] Polyvinyl chloride (PVC), as the most common plastic product in life, is widely used in the manufacture of various PVC pipes, PVC sheets, PVC films, PVC wallpapers, PVC cable materials, etc. It is the most widely used category among the five general-purpose plastics. [0003] PVC cable material is mainly composed of PVC resin, plasticizer, stabilizer, filler, lubricant and pigment, and is extruded and granulated by a double-stage screw extruder. Among them, the hardness of PVC cable material depends on the proportion of plasticizer in PVC formula to adjust, the more plasticizer content, the softer the cable material. Ordinary cable materials choose some conventional plasticizers to soften PVC. Due to its own characteristics and production technology, the produced cable materials ha...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.