A kind of environment-friendly diatom mud doll and its manufacturing process

A production process and diatom mud technology, applied in the field of environmentally friendly diatom mud dolls, can solve the problems of single functional use, complex production process, poor temperature adaptability, etc., and achieve diversified functions, good chemical stability, and strong flame retardancy. energy effect

Active Publication Date: 2018-10-30
广东涂乐师新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the main components of traditional rubber clay are made of animal fat leftovers, old powder, gypsum powder, wax paint and glue, etc. It has the shortcomings of dark color, poor temperature adaptability, etc. It is easy to stick to hands, causing pollution, and more importantly, its main components contain certain toxins, which have been prohibited for children
The other is clay dolls made of ceramics. This kind of clay dolls are only for decoration and have a single function, but the price is not cheap, and the production process is not only very complicated, but also easy to break or be damaged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1: 1 gram per serving

[0029] An environmentally friendly diatom mud doll is made of the following components in parts by weight: gypsum powder hemihydrate: 900 grams, diatomaceous earth 325 mesh: 100 grams, nano-zinc dioxide: 13 grams and nano-titanium dioxide: 15 grams; The hemihydrate gypsum powder is one of β type hemihydrate powder and α type hemihydrate powder.

[0030] The production process of the environmentally friendly diatom mud doll is as follows: Step 1: first put the above-mentioned parts by weight of hemihydrate gypsum powder, diatomaceous earth 325 mesh, nano-zinc dioxide and nano-titanium dioxide into a mixing tank whose rotation speed is 615 rpm Stir for 6 minutes to obtain a uniformly stirred powder mixture; then, mix the above powder mixture with water and stir for 12 minutes to obtain a muddy mixture, and the weight ratio of the powder mixture to water is 1:0.6.

[0031]Step 2: Vacuum the mud mixture with a vacuum mud refining machine to ...

Embodiment 2

[0040] Example 2: 1 catties per serving

[0041] An environmentally friendly diatom mud doll is made of the following components in parts by weight: hemihydrate gypsum powder: 1000 catties, diatomaceous earth 325 mesh: 166 catties, nano-zinc dioxide: 19 catties and nano-titanium dioxide: 24 catties; The hemihydrate gypsum powder is one of β type hemihydrate powder and α type hemihydrate powder.

[0042] The production process of the environmentally friendly diatom mud doll is as follows: Step 1: first put the above-mentioned parts by weight of hemihydrate gypsum powder, diatomaceous earth 325 mesh, nano-zinc dioxide and nano-titanium dioxide into a mixing tank whose rotation speed is 628 rpm Stir in medium for 10 minutes to obtain a uniformly stirred powder mixture; then, mix the above powder mixture with water and stir for 15 minutes to obtain a muddy mixture, and the weight ratio of the powder mixture to water is 1:0.6.

[0043] Step 2: Vacuum the mud mixture with a vacuum m...

Embodiment 3

[0052] Embodiment three: 1 kilogram per serving

[0053] An environmentally friendly diatom mud doll is made of the following components in parts by weight: gypsum powder hemihydrate: 1050 kg, diatomaceous earth 325 mesh: 187 kg, nano-zinc dioxide: 25 kg and nano-titanium dioxide: 28 kg; The hemihydrate gypsum powder is one of β type hemihydrate powder and α type hemihydrate powder.

[0054] The production process of the environmentally friendly diatom mud doll is as follows: Step 1: first put the above-mentioned parts by weight of hemihydrate gypsum powder, diatomaceous earth 325 mesh, nano-zinc dioxide and nano-titanium dioxide into a mixing tank whose rotation speed is 648 rpm Stir in medium for 14 minutes to obtain a uniformly stirred powdery mixture; then, mix the above powdery mixture with water and stir for 19 minutes to obtain a muddy mixture, and the weight ratio of the powdery mixture to water is 1:0.6.

[0055] Step 2: Vacuum the mud mixture with a vacuum mud refin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly diatom mud doll and a production process thereof. The environment-friendly diatom mud doll is prepared from, by weight, 800-1100 parts of hemihydrate gypsum powder, 80-200 parts of diatomite of 325 mesh, 10-30 parts of nano zinc oxide and 10-30 parts of titanium dioxide. The hemihydrate gypsum powder refers to one of beta type hemihydrate powder and alpha type hemihydrate. The prepared diatom mud doll can effectively remove formaldehyde and harmful substances in the ambient air, and is environmentally friendly, mold proof and bacterial proof; the color does not change even under the irradiation of ultraviolet light, and the original luster and color can be maintained for a long term; the diatom mud doll has good acid and alkali corrosion resistance performance, good water resistance, pollution resistance, wear resistance, steam resistance and aging resistance, good chemical stability and strong flame resistance and is not easy to break, and the function is diversified.

Description

technical field [0001] The invention relates to an environment-friendly diatom mud doll, in particular to an environment-friendly diatom mud doll and a manufacturing process thereof. Background technique [0002] At present, there are roughly two types of clay dolls on the market. One is plasticine designed to improve children's hand-making ability. Children can make various handicrafts, sculptures or paintings through plasticine. However, the main components of traditional rubber clay are made of animal fat leftovers, old powder, gypsum powder, wax paint and glue, etc. It has the shortcomings of dark color, poor temperature adaptability, etc. It is easy to stick to hands and causes pollution. More importantly, its main components contain certain toxins, which have been prohibited for children to use. The other is clay dolls made of ceramics. This kind of clay dolls is only for decoration and has a single function, but the price is not cheap, and the production process is n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B41/50
CPCC04B28/146C04B28/147C04B41/009C04B41/5041C04B2111/00008C04B2111/00017C04B2111/00956C04B14/08C04B14/305C04B14/30C04B41/5024C04B41/5012C04B41/4539
Inventor 陈建平刘妍霞张建友
Owner 广东涂乐师新材料科技有限公司