Pure water gravure black ink for printing PVC decorative film and preparation method thereof

A pure water type, printing black technology, applied in the direction of ink, application, household utensils, etc., can solve the problems of inability to achieve decoration and protection, low drying rate of water-based ink, harm to human health, etc., to achieve stable color, clear printing pattern, The effect of reducing pollution

Active Publication Date: 2019-08-16
BEIJING INSTITUTE OF GRAPHIC COMMUNICATION
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, PVC decorative films currently have the following deficiencies: PVC solvent-based inks are often used for printing PVC decorative films. Human body is healthy, so it is better to use water-based ink instead of solvent-based ink to reduce VOCs emissions and be more environmentally friendly
However, there are two problems with the use of water-based inks. One is that the drying rate of water-based inks is low and cannot be dried quickly, which invisibly prolongs the working hours, which is time-consuming and labor-intensive, and also delays the smooth progress of subsequent processes.
The second is that after printing, the peeling strength of PVC and transparent film PVC is poor. When vacuum forming, the two layers of PVC film will be separated, and the purpose of decoration and protection cannot be achieved.
Generally, when PVC is bonded, the temperature is 180-200°C, so the ink is required to maintain good performance under high temperature environment, but it is easy to peel off after using water-based ink.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pure water gravure black ink for printing PVC decorative film and preparation method thereof
  • Pure water gravure black ink for printing PVC decorative film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The preparation method of the pure water type gravure black ink for printing PVC decorative film is as follows:

[0037] 1) Weigh each raw material according to the following quality: carbon black 5kg, water-based PVC glue 50kg, water-based polyurethane resin 20kg, water-based epoxy resin 10kg, deionized water 15kg, acetylenic glycol ethoxylate 1kg, pigment affinity group Copolymer aqueous solution (concentration is 40wt%) 1kg, polysiloxane-polyether copolymer 1kg;

[0038] 2) Weigh the above components and pour them into the mixing device, stir them with a mechanical mixer for 40 minutes, then use a sand mill to disperse them, and grind them until the particle size is below 1 μm. If the particle size does not meet the standard, you need to continue grinding, and finally test the ink The various indicators and performance of the product are filtered and packaged after reaching the standard to obtain the finished product.

Embodiment 2

[0040] The preparation method of the pure water type gravure black ink for printing PVC decorative film is as follows:

[0041] 1) Weigh each raw material according to the following quality: carbon black 20kg, water-based PVC glue (Shanghai Ruitu Chemical Co., Ltd.) 75kg, water-based polyurethane resin 20kg, water-based epoxy resin 10kg, deionized water 20kg, acetylene glycol ethoxylate 1.5kg, 1.5kg of aqueous solution of copolymer containing pigment affinity groups (concentration is 40wt%), 1.2kg of polysiloxane-polyether copolymer;

[0042] 2) Weigh the above components and pour them into the stirring device, stir with a mechanical mixer at a speed of 800rpm for 45 minutes, and then use a sand mill to disperse them. The working pressure of the diaphragm pump is 0.25MPa. If the particle size is below 0.8μm, if the particle size does not meet the standard, it needs to continue grinding, and finally test the various indicators and performance of the ink. After reaching the stan...

Embodiment 3

[0044] The preparation method of the pure water type gravure black ink for printing PVC decorative film is as follows:

[0045] 1) Weigh each raw material according to the following quality: carbon black 8kg, water-based PVC glue (Shanghai Ruitu Chemical Co., Ltd.) 70kg, water-based polyurethane resin 28kg, water-based epoxy resin 25kg, deionized water 20kg, acetylene glycol ethoxylate 1.8kg, 1.8kg of aqueous solution of copolymer containing pigment affinity groups (concentration is 40wt%), 1.4kg of polysiloxane-polyether copolymer;

[0046] 2) Weigh the above components and pour them into the stirring device, stir with a mechanical mixer at 700rpm for 60 minutes, and then sand and disperse them with a sand mill. The working pressure of the diaphragm pump is 0.30MPa. The diameter is between 0.5-0.8 μm. If the particle size does not meet the standard, it needs to continue grinding. Finally, the various indicators and performance of the ink are tested. After reaching the standar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides pure water type gravure black ink for printing a PVC (polyvinyl chloride) decorative film. The pure water type gravure black ink is mainly prepared from the following raw materials in parts by mass: 5-20 parts of carbon black, 50-75 parts of aqueous PVC rubber, 20-30 parts of aqueous polyurethane resin, 10-30 parts of aqueous epoxy resin, 15-35 parts of deionized water, 1-2 parts of an antifoaming agent, 1-2 parts of a dispersing agent and 1-1.5 parts of a surface active agent. A preparation method comprises the following steps: mixing and agitating uniformly all the raw materials, grinding and dispersing an obtained mixture, inspecting the quality of the mixture to be qualified, filtering and packing the mixture, and obtaining the pure water type gravure black ink. The pure water type gravure black ink provided by an embodiment of the invention does not contain any organic solvent in a formula by the mutual cooperation among the aqueous PVC rubber, the aqueous polyurethane resin and the aqueous epoxy resin, is safe and environment-friendly, moreover, enhances a wetting effect on the carbon black, and meanwhile, has favorable wear resistance and film formation performance.

Description

technical field [0001] The invention relates to the field of ink processing, in particular to a pure water gravure black ink for printing PVC decorative films and a preparation method thereof. Background technique [0002] PVC decorative film is a widely used surface decoration material. Firstly, it is printed on PVC, which can have various patterns and embossing patterns. On the double stick laminating machine, the completely dried PVC printed face mask and a layer of PVC transparent film are heated and pressed together. The temperature of the vat of the laminating machine is 180-200°C, and then the laminated film is firmly adsorbed on the surface of the building material through the vacuum suction process, so as to decorate and protect the building material. High-end office furniture, cabinet doors, bathroom cabinet doors, home decoration sets of doors, decorative panels and other building materials can be decorated with it to meet people's different daily needs. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/106C09D11/102C09D11/033C09D11/03
CPCC09D11/03C09D11/033C09D11/102C09D11/106
Inventor 魏先福黄蓓青徐英杰闫继芳
Owner BEIJING INSTITUTE OF GRAPHIC COMMUNICATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products