Leaching method of uranium and molybdenum associated ore
An associated ore and leaching technology, applied in the field of hydrometallurgy, can solve the problems of low resource utilization and difficulty in solving production costs
Active Publication Date: 2011-03-30
BEIJING RESEARCH INSTITUTE OF CHEMICAL ENGINEERING AND METALLURGY
View PDF0 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The extraction rate can reach 90%, while the leaching rate of molybdenum is only 30%. In addition, it is difficult to solve the problems of high production cost and low resource utilization rate.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] The leaching time was 1 hour, and the continuous stirring mode was taken.
Embodiment 2
[0024] The leaching time was 10 hours, and the continuous stirring mode was taken.
Embodiment 3
[0032] The leaching time was 9 hours.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a method for leaching uranium-molybdenum associated ore. It uses leaching agent and oxidant to extract uranium and molybdenum in the ore; the leaching agent used is a mixture of water, sulfuric acid, soluble inorganic sulfate or inorganic bisulfate, and the hydrogen ion concentration in the leaching agent is 1.5mol / L~ 5.1mol / L, the amount of soluble inorganic sulfate or inorganic bisulfate is 0.1%-2% (weight) of the ore weight; the leaching method is carried out at 20°C-120°C. The leaching rate of uranium-molybdenum associated ore by the method of the invention is high, the production cost is low, and the resource utilization rate is high. The leaching rate of uranium slag can be increased from 40% to more than 70%, and the leaching rate of molybdenum can be increased from less than 30% to more than 75%. .
Description
Technical field of leaching method for uranium and molybdenum associated ore The present invention relates to the hydrometallurgical technology of uranium-molybdenum associated ore leaching, be specifically related to a kind of uranium-molybdenum associated ore leaching method Law. Background technique The countries such as the U.S., France, Niger, Mexico, the former Soviet Union are all comprehensively recovered from the associated ore of uranium and molybdenum Molybdenum, and a lot of research has been done on the comprehensive recovery technology of associated ores. For example, the foreign uranium industry has used pressurized alkali leaching for uranium molybdenum companion The leaching of raw ore has achieved certain results; some easy-to-leach uranium-molybdenum ores can also be treated by atmospheric pressure acid leaching and alkali leaching. domestic uranium The research on molybdenum comprehensive recovery technology began in the late 1960s, and began to b...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B60/02C22B34/34C22B3/04
Inventor 王洪明孟晋黄崇元赵满常叶连升王平康绍辉王凯赵良仁
Owner BEIJING RESEARCH INSTITUTE OF CHEMICAL ENGINEERING AND METALLURGY
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com