Composition used for preparing compound quartzite jewel board

A composition and quartz stone technology, applied in the field of artificial building decoration materials, can solve the problems of hardness, strength, compactness, smoothness, impermeability, toughness, flame retardancy, anti-ultraviolet aging, limited use range, etc. Strong ultraviolet reflection ability, strong infrared reflection ability, good fire performance

Inactive Publication Date: 2017-05-10
新疆雅美石开发进出口有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current quartz stone plate, because of its low density and low content of silicon dioxide, leads to the hardness, strength, compactness, smoothness, impermeability, toughness, flame retardancy, UV aging resistance and thermal aging of quartz stone plate. , there are still some problems that limit its scope of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition used for preparing compound quartzite jewel board
  • Composition used for preparing compound quartzite jewel board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Raw material preparation:

[0049] Urho pebble A: The deep red Urho pebble produced in Karamay. Pass through a 4-mesh sieve after crushing; weigh 7kg.

[0050] Urho pebble B: The red Urho pebble produced in Karamay, crushed and passed through an 8-mesh sieve. Weigh 14kg.

[0051] Gobi sapphire: the translucent green Gobi sapphire produced in Altay, crushed and passed through a 26-mesh sieve. Weigh 10kg.

[0052] Rose Quartz A: reddish rose quartz produced in Altay, crushed and passed through a 40-mesh sieve. Weigh 17kg.

[0053] Rose Quartz B: reddish rose quartz produced in Altay, crushed and passed through a 70-mesh sieve. Weigh 7kg.

[0054] Quartz powder: quartz powder with a mesh number of 300 mesh. Weigh 24kg.

[0055] Unsaturated polyester resin: use o-phthalic unsaturated polyester resin, weighing 8kg.

[0056] Toner: adopt fruit green toner, weigh 0.0002kg.

[0057] Coupling agent KH-570: Weigh 0.003kg of coupling agent KH-570.

[0058] Curing agent...

Embodiment 2

[0073] Raw material preparation:

[0074] Urho Pebble A: The deep red Urho Pebble produced in Karamay, crushed and passed through a 6-mesh sieve; weigh 9kg;

[0075] Urho Pebble B: Urho pebbles of reddish color produced in Karamay, crushed and passed through a 16-mesh sieve; weigh 16kg;

[0076] Gobi sapphire: the translucent green Gobi sapphire produced in Altay, crushed and passed through a 40-mesh sieve; weigh 12kg;

[0077] Rose Quartz A: reddish rose quartz produced in Altay, crushed and passed through a 70-mesh sieve; weigh 19kg;

[0078] Rose Quartz B: reddish rose quartz produced in Altay, crushed and passed through a 120-mesh sieve; weigh 10kg;

[0079] Quartz powder: quartz powder with a mesh number of 350; weigh 27kg;

[0080] Unsaturated polyester resin: use isophthalic unsaturated polyester resin, weigh 10kg;

[0081] Toner: use phthalocyanine blue toner, weighing 0.00027kg;

[0082] Coupling agent KH-570: Weigh 0.0036kg of coupling agent KH-570;

[0083] Cu...

Embodiment 3

[0098] Raw material preparation:

[0099] Urho pebble A: The deep red Urho pebble produced in Karamay, crushed and passed through a 4-mesh sieve; weigh 8kg;

[0100] Uerhe Pebble B: Urhe pebbles of reddish color produced in Karamay, crushed and passed through a 12-mesh sieve; weigh 15kg;

[0101] Gobi sapphire: the translucent green Gobi sapphire produced in Altay, crushed and passed through a 32-mesh sieve; weigh 11kg;

[0102] Rose quartz A: reddish rose quartz produced in Altay, crushed and passed through a 50-mesh sieve; weigh 18kg;

[0103] Rose Quartz B: reddish rose quartz produced in Altay, crushed and passed through a 100-mesh sieve; weigh 8kg;

[0104] Quartz powder: quartz powder with a mesh number of 325; weigh 25kg;

[0105] Unsaturated polyester resin: adopt p-benzene type unsaturated polyester resin, weigh 9kg;

[0106] Toner: use Luo-green toner, weighing 0.00025kg;

[0107] Coupling agent KH-570: Weigh 0.0032kg of coupling agent KH-570;

[0108] Curing age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composition used for preparing a compound quartzite jewel board, and relates to the technical field of man-made architectural decoration materials. The composition comprises Urho cobbles, gobi sapphire, rosy quartz, quartz powder, unsaturated polyester resin, toner, coupling reagent and curing agent. The composition used for preparing the compound quartzite jewel board adopts Xinjiang unique stone materials as main raw materials and can be smashed into various specifications. In addition, since the stone materials have colors, obtained board materials are colorful and diverse and have a good attractive effect. In addition, the board material prepared from the composition used for preparing the compound quartzite jewel board has better hardness, strength, degree of finish, impermeability, fire resistance, ultraviolet radiation aging resistance and the like than a conventional man-made quartzite board material.

Description

technical field [0001] The invention relates to the technical field of artificial building decoration materials, in particular to a composition for preparing composite quartz stone gemstone plates. Background technique [0002] Composite quartz stone is a new type of material composed of natural quartz stone or quartz sand as the main raw material, organic or inorganic bonding materials through pressure, temperature, vibration and other molding procedures. Due to the use of natural quartz materials, the surface of the stone is more realistic and natural. , stable color, high hardness, excellent chemical resistance and weather resistance. As a new type of material, composite quartz stone can be rationally utilized by using existing stone mine tailings, so that stone, a non-renewable energy source, can be protected to a greater extent. Due to its rich and bright colors, no radiation, wear resistance, pressure resistance, scratch resistance, corrosion resistance, anti-aging, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B111/28C04B111/20
CPCC04B26/18C04B2111/00017C04B2111/20C04B2111/28
Inventor 贾小伟巩银虎陆蓉
Owner 新疆雅美石开发进出口有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap