Rubber composition, crosslinked rubber composition, and tire

A technology of rubber composition and cross-linked rubber, applied in special tires, carbon compounds, tire parts, etc., can solve the problems of reducing cutting resistance and low heat generation, and achieve low heat generation, high wear resistance, high The effect of cut resistance

Inactive Publication Date: 2017-05-10
BRIDGESTONE CORP
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, rubber compositions containing low structure carbon black tend to suffer from poor low heat build-up and reduced cut resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber composition, crosslinked rubber composition, and tire
  • Rubber composition, crosslinked rubber composition, and tire
  • Rubber composition, crosslinked rubber composition, and tire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0075] A more detailed illustration of the invention is provided below by way of examples. However, the present invention is by no means limited by the following Examples.

[0076] (carbon black)

[0077] Carbon Blacks 1-12 having the parameters shown in Table 1 were prepared. Carbon blacks 1, 2, 6-10 and 12 were produced by using fine particle size, high structure HAF carbon black produced by Asahi Carbon Co., Ltd. and by adjusting reaction temperature, air rate, amount of KOH and reaction time. For carbon blacks 3-5 and 11, parameters were changed by adjusting production conditions for fine particle size, low structure HAF carbon black produced by Asahi Carbon Co., Ltd.

[0078] CTAB and 24M4DBP in Table 1 were measured according to JIS K 6217-3 and JIS K 6217-4, respectively. In addition, Dst and ΔD50 were measured by a centrifugal sedimentation method using a disc centrifuge manufactured by Joyce-Loebl. The hydrogen generation amount of carbon black was obtained by mea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The purpose of the present invention is to provide a rubber composition having good low exothermicity, high wear resistance, and high cutting resistance when applied in a tire member such as a tread, and whereby excellent resistance to fatigue cracking can be realized. In order to achieve this purpose, the present invention is the rubber composition including carbon black, the rubber composition is characterized in that the carbon black satisfies relational expressions (1) through (3). (1): 62.5*24M4DBP+Hydrogen generation amount<=8337.5. (2): 24M4DBP+0.25*CTAB>=62.5. (3): Dst+0.75*deltaD50>=152.5

Description

technical field [0001] The present invention relates to rubber compositions, crosslinked rubber compositions and tires. Background technique [0002] Pneumatic tires are generally required to exhibit high performance in a manner that satisfies various performance requirements at the same time. For example, in the case of tire members such as treads, in addition to the requirements for wear resistance, cut resistance, and low heat generation properties, improvement in fatigue crack resistance is desired. [0003] In one example of conventional techniques for improving fatigue cracking resistance, carbon black in which the degree of communication between carbon black particles is small (low-structure carbon black) is compounded into a rubber composition. [0004] However, rubber compositions containing low-structure carbon black tend to suffer from poor low heat build-up and reduced cut resistance. [0005] Examples of techniques for improving fatigue cracking resistance wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L21/00B60C1/00C09C1/50C09C1/48C08K3/04
CPCB60C1/00C08L21/00C08L7/00C01B32/00C08K3/04C08K2201/006C08K3/36C08K5/09C08K5/18C08K3/22C08K5/47C08K3/06C01P2006/12C01P2006/19C01P2006/80C08K2201/003C08K2201/011C09C1/48
Inventor 浜谷悟司
Owner BRIDGESTONE CORP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com