The method of removing film from the edge of coated glass

A coating glass and edge technology, applied in the coating and other directions, can solve the problems of affecting product quality, complicated operation, rising cost, etc., and achieve the effect of simple and feasible operation, reliable quality and beautiful edge.

Active Publication Date: 2019-12-31
信义超薄玻璃(东莞)有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the above-mentioned problems in the existing off-line coated glass film removal process, such as complex operation, film removal affecting product quality, and cost increase, the embodiment of the present invention provides a method for removing film on the edge of coated glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • The method of removing film from the edge of coated glass
  • The method of removing film from the edge of coated glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A method for removing film from the edge of coated glass, comprising the steps of:

[0046]1) Pretreatment of the original glass: the original glass is obtained through pretreatment processes such as cutting, edging, cleaning, drying, and loading;

[0047] 2) Masking treatment: Apply low-temperature pyrolysis ink to the area of ​​the original glass surface that does not need to be coated by screen printing process (such as figure 2 2 regions shown);

[0048] 3) Drying and curing treatment: drying the low-temperature decomposition ink on the original glass at a temperature of 95°C to make it solidify;

[0049] 4) Cleaning and coating treatment: on the surface of the original glass coated with low-temperature pyrolysis ink, use the magnetron sputtering coating method to coat the required film layer (the coated film layer is located at figure 2 Middle 1 area);

[0050] 5) Subsequent processing process: the original glass is made into a finished product through powder ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal decomposition temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method of removing a film from edge of coated glass. The method at least comprises the following steps: 1) carrying out mask coating treatment on a region, without needing to coat the film, of glass to be coated by adopting low-temperature thermal decomposition ink; 2) carrying out drying and solidification treatment on the glass to be coated, which is treated in the first step; 3) carrying out magnetron sputtering coating treatment on the glass to be coated, which is obtained in the second step; and 4) carrying out powder spraying, matching, hot bending, cleaning, laminating, high pressure and packaging treatments on the glass obtained in the third step. A coated glass product prepared by the film removing method is beautiful in side boundary and reliable in quality and is suitable for edge film removing process of automobile glass.

Description

technical field [0001] The invention relates to the technical field of coated glass coating, in particular to a method for removing film from the edge of coated glass. Background technique [0002] Coated glass is widely used in building doors and windows and automobile windows because of its special functions such as sunshade, thermal insulation, and rich colors. However, the film layer prepared by off-line coating technology (such as magnetron sputtering) is not as good as that prepared by online coating The film layer is dense, and the film layer of off-line coating is easily corroded or scratched, resulting in the failure of the functional film, especially for low-emissivity (Low-E) coated glass, whose main functional film is silver, and the silver film is particularly easy to oxidize in the air. In order to avoid the low-emissivity Low-E film of off-line coating from contacting with air, water, etc., after the coating is completed, the coated glass is generally removed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/00
CPCC03C17/002C03C2218/355
Inventor 董清世周枫蔡法清万军鹏高昌龙吕晶
Owner 信义超薄玻璃(东莞)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com