Aluminum alloy isothermal precision die forging technology

An aluminum alloy and die forging technology, which is applied in the field of aluminum alloy die forging technology, can solve problems such as insufficient temperature, easy to stick to the die, and excessive forging blanks.

Inactive Publication Date: 2017-06-09
赵敏
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide an aluminum alloy warm precision die forging process to solve the problems that the current aluminum alloy isot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0009] Embodiment 1: The method of this embodiment includes the following steps: Step 1: Determine the size of the forging blank;

[0010] Step 2: Heating the forging mold and the forging blank: install the forging mold on the die base of the forging press and heat it to 380±3°C; after heating for 5 hours, heat the forging blank in a pit furnace at a temperature of 480 ±3°C; at the same time, heat the box furnace and set the temperature at 480°C;

[0011] Step 3: After the material temperature reaches, lift the forging blank from the pit furnace and put it into the No. 1 basket of the box furnace, and continue to keep warm;

[0012] Step 4: Apply graphite lubrication on the mold, then place the forging blank on the mold, and the position of the forging blank should be adjusted;

[0013] Step 5: Press the down button of the forging press console to carry out forging until the mold is completely closed. After holding the pressure for 5 seconds, press the up button of the forgin...

specific Embodiment approach 2

[0016] Embodiment 2: In step 1 of this embodiment, the weight of the blank is determined as the net weight of the forging + 0.08kg, so as to determine the size; avoiding waste. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0017] Specific embodiment three: the forging pressure in step five of this embodiment is 7000-8000KN; The upper mold is coated with more graphite to prevent the upper mold from sticking to the mold, and the forming effect is good. Other steps are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum alloy warm precision die forging process, which relates to an aluminum alloy die forging process. Aiming at the problem that the current aluminum alloy isothermal precision die forging die temperature is not enough, the forging blank is too large to produce waste, the process is unstable, and it is easy to stick to the die. Step 1: Determine the size of the forging blank; Step 2: Heat the forging mold and the forging blank; Step 3: After the material temperature reaches, lift the forging blank from the pit furnace and put it into the No. 1 basket of the box furnace Inside, continue to keep warm; Step 4: Apply graphite lubrication on the mold, and then place the forging blank on the mold; Step 5: Forging. Step 6: Start the push-out button of the ejector rod, eject the formed part, use the material tongs to clamp the forging out, and place it on the table; Step 7: Use the angle grinder to clean the burr on the bottom of the forging, and place it on the table to cool down. The invention is used for isothermal precision die forging of aluminum alloy.

Description

technical field [0001] The invention relates to an aluminum alloy die forging process. Background technique [0002] Isothermal die forging, referred to as isothermal forging, is a die forging in which the die is heated to the deformation temperature of the blank and deformed at a low strain rate. Isothermal forging technology has been maturing since the 1970s, and is widely used in the manufacture of important structural parts of aerospace vehicles, and has achieved very obvious technical and economic benefits. [0003] Isothermal forging technology is mainly used in the aerospace industry for the production of difficult-to-form material forgings with complex shapes, thin webs and high ribs, and high internal quality requirements on the surface of forgings. Not only that, compared with conventional die forging, isothermal die forging technology is also an energy-saving technology. However, isothermal die forging is only suitable for medium and small batch production of fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21J5/02B21J1/06B21J3/00
CPCB21J5/02B21J1/06B21J3/00
Inventor 赵敏
Owner 赵敏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap