Floor Wax and Floor Coating

A floor wax and floor technology, applied in coatings, polyurea/polyurethane coatings, polishing compositions, etc., can solve the problems of floor coatings becoming slippery, affecting slip resistance, reducing gloss and leveling, etc.

Active Publication Date: 2019-01-25
3M CHINA
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] It is known that the formation of black heel marks can be reduced by increasing the lubricant content of the floor wax, but this causes the floor coating to become slippery, affecting its slip resistance
Alternatively, the formation of black heel marks can also be prevented by increasing the hardness of the ground coating, but this limits the selection of ground coating raw materials and reduces its gloss and leveling during coating, etc.
Alternatively, it is also possible to increase the content of plasticizer in the floor wax to improve the anti-black heel print performance, but in this way, dust and other pollutants are easy to penetrate (or blend) into the ground coating along the plasticizer, reducing the resistance of the ground coating. Pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Floor Wax and Floor Coating
  • Floor Wax and Floor Coating
  • Floor Wax and Floor Coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0085] The preparation method of floor wax

[0086] The preparation method of the floor wax in the embodiment of the present invention is not particularly limited, as long as the various components can be finally mixed together uniformly.

[0087] In the actual preparation process, the corresponding emulsion can be used as the raw material of some components. That is to say, some components can be separately dispersed in the medium to form an emulsion, and then different emulsions, additives, remaining medium, etc. are mixed to obtain the floor wax of the embodiment of the present invention.

[0088] It should be understood that if the raw material of a certain component is an emulsion, the solid content in the emulsion is the actual amount of the component in the floor wax, and the medium in the emulsion is a part of the medium of the floor wax. Generally speaking, as The solid content of the raw material emulsion is 15%-40% (mass percentage).

[0089] ground coating

...

specific Embodiment

[0099] Prepare floor wax and floor coating of the present invention and test its performance below, as specific examples.

[0100] 1) Raw material

[0101] The raw materials used in specific examples and comparative examples are as follows:

[0102] Elastomers: Hystrech V29, Hystrech V60, Hycar 29630, Hycar AE960 polyacrylate elastomer emulsions from The Lubrizol Company.

[0103] Other film-forming polymers: Sytran 1942 styrene-acrylic polymer emulsion from Intech; PU 608A polyurethane emulsion from Guanzhi New Materials Co., Ltd.

[0104] Lubricant: Silok 50 silicone rubber emulsion from Silok.

[0105] Wax: Sytran pa1465 wax emulsion from Intech, which is a PE wax emulsion.

[0106] Plasticizer: Acetyl tri-n-butyl citrate (ATBC) from Shanghai Sinopharm Reagent Co., Ltd.

[0107] Film former: Dimethyl phthalate (DMP) from The Dow Chemical Company.

[0108] Wetting agents: Silok 8000 from Silok, Capstone FS60 from Crimson Chemicals.

[0109] Leveling agent: Silok 8066 f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a floor wax and a floor coating, which belong to the technical field of floor coatings. The floor coating has good anti-black shoe heel print performance and anti-skid property at the same time. The floor wax of the present invention comprises a film-forming component and a liquid medium, and the film-forming component is dispersed in the medium, and the film-forming component comprises: a film-forming polymer for forming a floor coating matrix, the The film-forming polymers include elastomers having a maximum tensile elastic strain greater than or equal to 50%; lubricants.

Description

technical field [0001] The invention belongs to the technical field of floor coatings, in particular to a floor wax and a floor coating. Background technique [0002] Floor wax (Floor Finish, also known as floor paint) can be coated on the ground of supermarkets, factories, etc. to form a ground coating, and the ground coating is usually re-formed every few months (such as 3 to 6 months) to To continue to protect the role of the ground. Wherein, "floor wax" is only a customary name for a product in this field, rather than a literal limitation of the product. Therefore, the floor wax does not have to be applied on the floor, and it can also be used on other floors such as floor (such as rubber floor), marble, floor tiles, ceramic tiles, etc. [0003] When a person walks, the black heel will rub against the ground, which may cause the heel to "rub" a black mark on the ground coating, forming a black heel mark (BHM, Black Heel Mark). Among them, "black heel print" is only a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/12C09D125/08C09D175/04C09D133/04C09D123/06C09D7/63C09D7/65