High-fluidity high-temperature nylon material and preparation method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-fluidity, high-temperature technology, applied in the field of nylon materials, can solve the problems of poor high-temperature resistance and fluidity of nylon materials
Inactive Publication Date: 2017-09-08
LUHE SHOUCHUANG PLASTIC HARDWARE PROD
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The technical problem to be solved by the present invention is to provide a high-fluidity high-temperature nylon material and a preparation method, and the present invention can well solve the problems of high-temperature resistance and poor fluidity of existing nylon materials
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] High-fluidity high-temperature nylon material is characterized in that it is mainly made of raw material PA46, glass fiber, stabilizer, nucleating agent, grafted POE and lubricant, wherein the weight percentage of PA46 in the raw material is 40%, glass The weight percentage of fiber in the raw material is 42%, the weight percentage of the stabilizer in the raw material is 3%, the weight percentage of the nucleating agent in the raw material is 2%, and the weight percentage of grafted POE in the raw material Percent composition is 11%, and the weight percent composition of lubricant in raw material is 2%,
[0026] Further, the glass fibers are alkali-free glass fibers.
[0027] Further, the stabilizer is a high temperature resistant hindered amine antioxidant.
[0028] Further, the nucleating agent is aryl sulfonate.
[0029] Further, the grafted POE is maleic anhydride grafted POE.
[0030] Further, the lubricant is stearamide.
[0031] The preparation method of the...
Embodiment 2
[0044] High-fluidity high-temperature nylon material is characterized in that it is mainly made of raw material PA46, glass fiber, stabilizer, nucleating agent, grafted POE and lubricant, wherein the weight percentage of PA46 in the raw material is 85%, glass The weight percentage of fiber in raw material is 12%, the weight percentage of stabilizer in raw material is 0.5%, the weight percentage of nucleating agent in raw material is 0.5%, and the weight percentage of grafted POE in raw material The percentage content is 1.5~11%, and the weight percentage content of the lubricant in the raw material is 0.5~2%,
[0045] Further, the glass fibers are alkali-free glass fibers.
[0046] Further, the stabilizer is a high temperature resistant hindered amine antioxidant.
[0047] Further, the nucleating agent is aryl sulfonate.
[0048] Further, the grafted POE is maleic anhydride grafted POE.
[0049] Further, the lubricant is stearamide.
[0050] The preparation method of the h...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a high-fluidity high-temperature nylon material and a preparation method. Because a stabilizer is added in the material, the high temperature resistance effect of nylon is increased, and a lubricant is used to make the nylon have higher fluidity and mold release performance and easy in molding by processing, in addition, due to the addition of a nucleating agent, the flow performance of products is increased, the molding time of the products is shortened and the tensile, impact and other properties of the products are improved. Glass fiber is matched with grafted POE, thus the toughness of the products is greatly improved, so that the products can be used in a shock-resistant environment. Finally through the stabilizer, nucleating agent, lubricant, glass fiber and grafted POE matching with each other, the fluidity of the products is improved, and meanwhile the high temperature and impact resistance of the products are greatly improved, the molding time of the products is significantly shortened, and the production cost of the products is effectively reduced.
Description
technical field [0001] The invention belongs to the technical field of nylon materials, and in particular relates to high-fluidity high-temperature nylon materials and a preparation method. Background technique [0002] Polyamide (PA), commonly known as nylon, has good comprehensive properties, including mechanical properties, heat resistance, wear resistance, chemical resistance and self-lubricating properties, and has a low coefficient of friction, certain flame retardancy, and is easy to processing. There are many varieties of PA products, including PA6, PA66, PAll, PAl2, PA46, PA610, PA612, PAl010, etc., as well as many new varieties such as semi-aromatic nylon PA6T and special nylon developed in recent years. Because nylon has many characteristics, it is widely used in automobiles, electrical equipment, mechanical parts, transportation equipment, textiles, and papermaking machinery. With the miniaturization of automobiles, the high performance of electronic and electr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More