Water pipe used in pipeline engineering and preparation method thereof

A technology of pipeline engineering and water pipes, which is applied in the field of water pipes in pipeline engineering and its preparation, can solve the problems of flame retardancy, heat resistance and insufficient strength, and achieve good wear resistance, good heat resistance and high elasticity Effect

Inactive Publication Date: 2017-11-07
ANHUI MEILAN LANDSCAPE ENG CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the deficiencies of the existing water pipes in flame retardancy, heat resistance and strength, the object of the present invention is to provide a water pipe used in pipeline engineering and its preparation method, and the prepared water pipe used in pipeline engineering The water pipe has the advantages of good flame retardancy, good heat resistance and high strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A water pipe used in pipeline engineering, comprising the following raw materials in parts by weight: 95 parts of SG-3 type PVC resin, 6 parts of aluminum borate whiskers, 3 parts of calcium acetylacetonate, 18 parts of 1,2-polybutadiene, 5 parts of talcum powder, 2 parts of silica gel, 25 parts of polysulfone resin, 20 parts of polyamide resin, 15 parts of polyurethane rubber, 18 parts of phenolic resin, 2 parts of graphite powder, 3 parts of ceramic fiber, 12 parts of nano silicon carbide , 3 parts of 2,6-di-tert-butyl-p-cresol, 0.7 parts of flame retardant, 3-7 parts of plasticizer, 0.6 part of compatibilizer, 0.5 part of heat stabilizer, 0.6 part of light stabilizer and 0.5 part of curing agent share.

[0042] SG-3 type PVC resin is added to the raw material. SG-3 type PVC resin has the advantages of high strength, high rigidity, good toughness, good heat resistance and low temperature resistance.

[0043] Aluminum borate whiskers are added to the raw materials. Al...

Embodiment 2

[0061] A water pipe used in pipeline engineering, comprising the following raw materials in parts by weight: 90 parts of SG-3 type PVC resin, 4 parts of aluminum borate whiskers, 1 part of calcium acetylacetonate, 12 parts of 1,2-polybutadiene, 3 parts of talcum powder, 1 part of silica gel, 20 parts of polysulfone resin, 15 parts of polyamide resin, 12 parts of polyurethane rubber, 14 parts of phenolic resin, 1 part of graphite powder, 2 parts of ceramic fiber, 6 parts of nano silicon carbide , 2 parts of 2,6-di-tert-butyl-p-cresol, 0.6 parts of flame retardant, 3 parts of plasticizer, 0.3 parts of compatibilizer, 0.3 parts of heat stabilizer, 0.4 parts of light stabilizer and 0.3 parts of curing agent.

[0062] SG-3 type PVC resin is added to the raw material. SG-3 type PVC resin has the advantages of high strength, high rigidity, good toughness, good heat resistance and low temperature resistance.

[0063] Aluminum borate whiskers are added to the raw materials. Aluminum bo...

Embodiment 3

[0081] A water pipe used in pipeline engineering, comprising the following raw materials in parts by weight: 100 parts of SG-3 type PVC resin, 8 parts of aluminum borate whiskers, 5 parts of calcium acetylacetonate, 24 parts of 1,2-polybutadiene, 7 parts of talcum powder, 3 parts of silica gel, 30 parts of polysulfone resin, 25 parts of polyamide resin, 18 parts of polyurethane rubber, 22 parts of phenolic resin, 3 parts of graphite powder, 4 parts of ceramic fiber, 18 parts of nano silicon carbide , 4 parts of 2,6-di-tert-butyl-p-cresol, 0.8 part of flame retardant, 7 parts of plasticizer, 0.9 part of compatibilizer, 0.7 part of heat stabilizer, 0.8 part of light stabilizer and 0.7 part of curing agent.

[0082] SG-3 type PVC resin is added to the raw material. SG-3 type PVC resin has the advantages of high strength, high rigidity, good toughness, good heat resistance and low temperature resistance.

[0083] Aluminum borate whiskers are added to the raw materials. Aluminum bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a water pipe used in pipeline engineering and a preparation method thereof, and relates to the technical field of plastic pipes. The water pipe used in pipeline engineering includes the following raw materials in parts by weight: SG-3 type PVC resin, aluminum borate whiskers, acetyl Calcium acetone, 1,2‑polybutadiene, talc, silica gel, polysulfone resin, polyamide resin, polyurethane rubber, phenolic resin, graphite powder, ceramic fiber, nano silicon carbide, 2,6‑di tert-butyl-p-cresol, flame retardant, plasticizer, compatibilizer, heat stabilizer, light stabilizer and curing agent; the preparation method comprises the following steps: (1) weighing raw materials, (2) mixing, (3) ) Melt molding, cooling and shaping. The invention solves the deficiencies of the existing water pipes in flame retardancy, heat resistance and strength.

Description

technical field [0001] The invention belongs to the technical field of plastic pipes, and in particular relates to a water pipe used in pipeline engineering and a preparation method thereof. Background technique [0002] With the intensification of urbanization, the construction of pipeline engineering is also in full swing. As an important part of pipeline engineering, water pipes are responsible for transporting water bodies. Existing water pipes generally use PVC materials, but the flame retardant performance of PVC water pipes is not high enough, and a large amount of black smoke and toxic gases will be emitted when burning, such as carbon monoxide, benzene, naphthalene and other aromatic compounds, which seriously endanger people's health, and even Threat to people's lives. In addition, the PVC water pipes on the market have poor pressure resistance, and are prone to water leakage, water seepage, rupture, etc., which greatly reduces the service life of PVC pipes and li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L81/06C08L77/00C08L75/04C08L61/06C08L47/00C08K13/04C08K7/08C08K3/38C08K3/34C08K3/36C08K3/04C08K7/04C08K3/22C08K5/098C08K5/12
CPCC08L27/06C08K2003/2227C08K2003/387C08K2201/011C08L2201/02C08L2201/08C08L2203/18C08L2205/035
Inventor 周克斌
Owner ANHUI MEILAN LANDSCAPE ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap