Manufacturing method of surface wood-grain-imitated aluminum alloy building materials

A production method and technology of aluminum alloy materials, applied in the field of production of surface imitation wood grain aluminum alloy building materials, can solve the problems of large randomness and pollution

Active Publication Date: 2017-11-21
LINYI HAOMEN ALUMINUM
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are many ways to make surface wood grain, such as molding with a mold, which is rigid and uniform, such as patent CN1944086A, etc.; or directly print wood grain color on the surface of aluminum alloy or perform electrochemical processing, such as using electrolyte, so that the processed wood The grain effect is good, and the randomness is large, which is very similar to the natural wood grain, but these processing methods are very polluting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of surface wood-grain-imitated aluminum alloy building materials
  • Manufacturing method of surface wood-grain-imitated aluminum alloy building materials
  • Manufacturing method of surface wood-grain-imitated aluminum alloy building materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The present invention firstly provides a physical production method of an aluminum alloy building material with imitation wood grain on the surface, which produces imitation wood grain on the surface of the aluminum alloy material through the production method, and is characterized in that the production method includes using an aluminum alloy Material making stamping blanks, stamping to form wood grain, and flattening process;

[0023] The aluminum alloy material wherein is characterized by content by weight percentage, which includes the following components: 0.30% iron, 0.03% silicon, 0.10% magnesium, and the balance is aluminum and unavoidable impurities; it is characterized in that by weight percentage , the total content of impurities in the aluminum alloy is less than 0.3%. Such materials will have poor fluid continuity during the stamping process. It is not feasible to process very flat aluminum alloy products, but it is just right for decorative plates with rou...

Embodiment 2

[0033] The present invention firstly provides a physical production method of an aluminum alloy building material with imitation wood grain on the surface, which produces imitation wood grain on the surface of the aluminum alloy material through the production method, and is characterized in that the production method includes using an aluminum alloy Material making stamping blanks, stamping to form wood grain, and flattening process;

[0034] The aluminum alloy material is characterized by content by weight percentage, which includes the following components: 0.30-0.60% iron, 0.01-0.03% silicon, 0.10-0.30% magnesium, and the balance is aluminum and unavoidable impurities; It is characterized in that, by weight percentage, the total content of impurities in the aluminum alloy is less than 0.3%.

[0035] Such materials will have poor fluid continuity during the stamping process. It is not feasible to process very flat aluminum alloy products, but it is just right for decorative...

Embodiment 3

[0045] The present invention firstly provides a physical production method of an aluminum alloy building material with imitation wood grain on the surface, which produces imitation wood grain on the surface of the aluminum alloy material through the production method, and is characterized in that the production method includes using an aluminum alloy Material making stamping blanks, stamping to form wood grain, and flattening process;

[0046] The aluminum alloy material is characterized by its content by weight percentage, which includes the following components: 0.30-0.60% iron, 0.01-0.03% silicon, 0.10% magnesium, and the balance is aluminum and unavoidable impurities; it is characterized in that , by weight percentage, the total content of impurities in the aluminum alloy is less than 0.3%. The biggest feature of this embodiment is that the magnesium content has been reduced. This example proves that the grain of the wood is significantly increased by reducing the magnesiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Roughnessaaaaaaaaaa
Roughnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method of surface wood-grain-imitated aluminum alloy building materials. The manufacturing method is actually a physical processing method for manufacturing and generating imitated wood grains on the aluminum alloy material surface; the manufacturing method comprises the steps that a stamping blank is manufactured through an aluminum alloy material, stamping is carried out to form wood grains, and the flat opening process is carried out; the aluminum alloy material comprises the following components including, by weight percentage, 0.30%-0.60% of iron, 0.01%-0.03% of silicon, 0.10%-0.30% of magnesium and the balance aluminum and inevitable impurities; the aluminum alloy material is characterized in that by weight percentage, the total content of the impurities in the aluminum alloy is smaller than 0.3%. By means of the method, the imitated wood grains generated at random each time can be obtained on the surface of the aluminum alloy building materials, and the manufacturing method is low in cost and small in pollution.

Description

technical field [0001] The invention relates to a non-ferrous metal alloy building material, in particular to a method for manufacturing an aluminum alloy building material with a surface imitating wood grain. Background technique [0002] Aluminum is the most widely used metal material among non-ferrous metals, which meets people's needs in various aspects, such as the production of decoration and building materials. At present, there is a great demand for bionics in building materials, that is, to imitate the natural landscape. When making furniture, many manufacturers of aluminum profiles process their surfaces to meet customer needs, especially chemical and electrochemical treatments, so that they produce imitation wood. pattern. [0003] There are many ways to make surface wood grain, such as molding with a mold, which is rigid and uniform, such as patent CN1944086A, etc.; or directly print wood grain color on the surface of aluminum alloy or perform electrochemical pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline