Organic porous integral material and preparation method and application thereof

A monolithic material and organic technology, applied in the field of organic porous monolithic materials and their preparation and application, can solve the problems of pH sensitivity, difficult control of free radical polymerization rate, cumbersome process, etc., achieve strong hydrophobicity, simple functional modification method, good permeability

Inactive Publication Date: 2017-12-05
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this silicon-based hybrid monolithic material needs to be prepared through multiple steps, and the process is still relatively cumbersome and sensitive to pH. I

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic porous integral material and preparation method and application thereof
  • Organic porous integral material and preparation method and application thereof
  • Organic porous integral material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] 1) Add 30 mg of DPEPA reagent to a UV transparent centrifuge tube.

[0051] 2) Add 8 mg of functional monomer NDM to the above-mentioned UV transparent centrifuge tube.

[0052] 3) Add 125 μL of n-butanol and 15 μL of ethylene glycol to the above-mentioned UV transparent centrifuge tube.

[0053] 4) Add 0.1 mg of photoinitiator to the above-mentioned ultraviolet transparent centrifuge tube.

[0054] 5) Ultrasonic the above-mentioned centrifuge tube for 5 minutes to mix the various components therein evenly, and remove the dissolved oxygen dissolved therein.

[0055] 6) Introduce 1 μL of the prepolymer solution obtained in step 5) into a 75 μm (inner diameter) UV-transparent capillary tube that has been activated with 3-(trimethoxysilyl)propyl methacrylate in advance with a syringe, and then the capillary Both ends were sealed with silica gel, and then the UV transparent centrifuge tube containing the remaining mixed solution was sealed.

[0056] 7) Place the UV trans...

Embodiment 2

[0059] 1) Add 30 mg of DPEPA reagent to a UV transparent centrifuge tube.

[0060] 2) Add 16 mg of functional monomer NDM to the above-mentioned UV transparent centrifuge tube.

[0061] 3) Add 125 μL of n-butanol and 15 μL of ethylene glycol to the above-mentioned UV transparent centrifuge tube.

[0062] 4) Add 0.1 mg of photoinitiator to the above-mentioned ultraviolet transparent centrifuge tube.

[0063] 5) Ultrasonic the above-mentioned centrifuge tube for 5 minutes to mix the various components therein evenly, and remove the dissolved oxygen dissolved therein.

[0064] 6) Introduce 1 μL of the prepolymer solution obtained in step 5) into a 75 μm (inner diameter) UV-transparent capillary tube that has been activated with 3-(trimethoxysilyl)propyl methacrylate in advance with a syringe, and then the capillary Both ends were sealed with silica gel, and then the UV transparent centrifuge tube containing the remaining mixed solution was sealed.

[0065] 7) Place the UV tran...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of macromolecule, specifically to an organic porous integral material and a preparation method and application thereof. Acrylic ester containing unsaturated double bond, a functional monomer containing mercapto group and an initiator are mixed; a photoinitiator is added; the mixed solution undergoes ultrasonic dissolution in a pore forming agent; a free-radical polymerization reaction is carried out under UV-irradiation to in situ form a porous organic integral material, namely an organic porous integral material with different surface properties and functions. The organic porous integral material has a structured microstructure and ordered porous channels and has good application in chromatographic separation. The preparation method has advantages of simple and fast operation, fast reaction speed and the like. In addition, different organic functional monomers and pore forming agent systems can be selected according to different application requirements, and a series of porous organic integral materials with different physical and chemical properties are prepared.

Description

technical field [0001] The present invention relates to a kind of photoinitiated mercapto-acrylic ester polymerization reaction to prepare organic porous monolithic material and its preparation method and application, specifically dipentaerythritol penta- / hexa-acrylic acid (dipentaerythritol penta- / hexa-acrylic acid) containing unsaturated double bonds -acrylate, DPEPA), mercapto compounds and photoinitiators are ultrasonically dissolved in porogenic solvents, and then undergo radical polymerization under ultraviolet light irradiation to form porous organic monolithic materials in situ, by adjusting the concentration of monomers and porogens The proportion of organic porous monoliths with different surface properties and functions can be prepared. Background technique [0002] Porous monolithic material is a new type of porous micro-separation medium that has received extensive attention in recent years. Compared with traditional packed column separation materials, it has th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F122/14C08F8/34B01D15/08C08J9/14
CPCB01D15/08C08F8/34C08J9/142C08J2203/182C08J2333/08C08F122/1006
Inventor 邹汉法白径遥欧俊杰
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap