Enhancement type heat isolating reflective coating

A heat-insulating reflection and enhanced technology is applied in the field of coating technology to achieve the effect of increasing the surface area of ​​the coating, enhancing the reflection function and enhancing the anti-aging performance.

Active Publication Date: 2017-12-29
CHONGQING SANXIA PAINTS CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the deficiencies of existing coatings, the invention provides an enhanced heat-shielding reflective coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Enhanced heat-shielding reflective coating, the coating is composed of a bottom layer, a middle layer and a surface layer, in parts by mass,

[0019] The formula of the penetrating anti-rust primer with rust is:

[0020] Epoxy resin: 5 parts;

[0021] Anti-rust pigment: 18 parts;

[0022] Inert filler: 30 parts;

[0023] Modified ketimine: 7 parts;

[0024] Solvent A: 20 parts;

[0025] In this embodiment, the antirust pigment is iron oxide red, composite zinc phosphate, zinc powder, and ferrophosphorus powder, and the mixing mass ratio is 1:1:1:1; the inert filler is precipitated barium sulfate and barite powder, and the mixing mass ratio is 1:1:1:1; The ratio is 1:1; the modified ketimine is made of diethylenetriamine and methyl isobutyl ketone in a certain proportion and reacted under stirring at 110°C for 6 hours, then adding a certain amount of 634 liquid epoxy resin, stirring at 80°C Formed by reacting for 5 hours, solvent A is cyclohexanone.

[0026] The fo...

Embodiment 2

[0043] Enhanced heat-shielding reflective coating, the coating is composed of a bottom layer, a middle layer and a surface layer, in parts by mass,

[0044] The formula of the penetrating anti-rust primer with rust is:

[0045] Epoxy resin: 10 parts;

[0046] Anti-rust pigment: 25 parts;

[0047] Inert filler: 40 parts;

[0048] Modified ketimine: 10 parts;

[0049] Solvent A: 35 parts;

[0050] In this example, the antirust pigment is iron oxide red, composite zinc phosphate, and iron phosphorus powder, and the mixing mass ratio is 1:1:1; the inert filler is precipitated barium sulfate and barite powder, and the mixing mass ratio is 1:1 The synthesis of modified ketimine is the same as described in Example 1, and solvent A is mixed with cyclohexanone, methyl isobutyl ketone, butyl alkyd, and xylene in a mass ratio of 1:1:1:1. become.

[0051] The formulation of the mid-coat paint for enhanced heat-shielding reflective coating is:

[0052] Epoxy resin: 15 parts;

[005...

Embodiment 3

[0067] Enhanced heat-shielding reflective coating, the coating is composed of a bottom layer, a middle layer and a surface layer, in parts by mass,

[0068] The formula of the penetrating anti-rust primer with rust is:

[0069] Epoxy resin: 5 parts;

[0070] Anti-rust pigment: 15 parts;

[0071] Inert filler: 20 parts;

[0072] Modified ketimine: 5 parts;

[0073] Solvent A: 15 parts;

[0074] In this embodiment, the antirust pigment is iron oxide red, composite zinc phosphate, zinc powder, and ferrophosphorus powder, and its mixing mass ratio is 1:2:3; the inert filler is precipitated barium sulfate and barite powder, and its mixing mass ratio is 5:1; the synthesis of modified ketimine is the same as that described in Example 1.

[0075] The formulation of the mid-coat paint for enhanced heat-shielding reflective coating is:

[0076] Epoxy resin: 10 parts;

[0077] Flake filler: 10 parts;

[0078] Hollow glass microspheres: 15 parts;

[0079] Hydroxyl curing agent: 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an enhancement type heat isolating reflective coating. The coating consists of a bottom layer, a middle layer and a face layer; paint of the bottom layer is prepared from, by mass, 5-10 parts of epoxy resin, 15-25 parts of anti-rust pigment, 20-40 parts of inert filler, 5-10 parts of modified ketimine, and 15-35 parts of solvent A; the paint of the middle layer is prepared from, by mass, 10-15 parts of epoxy resin, 10-20 parts of flaky filler, 15-35 parts of hollow glass bead, 10-15 parts of hydroxyl curing agent, and 15-35 parts of solvent B; the paint of the face layer is prepared from, by mass, 40-50 parts of film former resin, 5-15 parts of nanometer metal oxide, 10-15 parts of rutile type titanium dioxide, 15-20 parts of weather fastness curing agent, and 10-20 parts of solvent C. The coating shows the enhancement effect of the heat isolating reflective performance while also has good corrosive resistance.

Description

technical field [0001] The invention belongs to coating technology, in particular to an enhanced heat-insulating reflective coating. Background technique [0002] As a new type of energy-saving material, thermal insulation coating can effectively reflect and block the energy of sunlight, significantly reduce the temperature of building exterior walls, roofs and indoors, and reduce the energy consumption of refrigeration equipment such as air conditioners. The use of heat-insulating coatings can not only improve the working environment but also significantly save energy, and the heat-insulating coatings are convenient for construction and have decorative effects, so they are widely used in the construction field. [0003] With the continuous strengthening of social supervision and inspection on safety and environmental protection issues, coupled with the fact that enterprises consciously improve the effect of energy saving and emission reduction in the operation process of fa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D127/12C09D183/04C09D5/33C09D5/10C09D7/12
CPCC08K7/00C08K7/28C08K2003/0893C08K2003/2227C08K2003/2231C08K2003/2241C08K2003/2244C08K2003/2272C08K2003/3045C08K2003/321C08K2201/011C08K2201/014C08L2201/08C09D5/004C09D5/106C09D127/12C09D163/00C09D183/04C08L83/04C08K3/22C08L27/12
Inventor 邓贤均魏雪峰
Owner CHONGQING SANXIA PAINTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap