Preparation method of biologically modified composite material

A composite material and biological modification technology, applied in the field of vegetable pest control, can solve problems such as crop quality decline, ecosystem damage, harm to human health, etc., and achieve the effects of increasing porosity, increasing specific surface, and protecting the ecological environment

Pending Publication Date: 2018-01-30
咸阳非金属矿研究设计院有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] One is to solve a series of problems caused by the traditional use of chemical pesticides to prevent crop root rot, such as pesticide residues, soil fertility decline, crop quality decline, environmental pollution, ecosystem damage, and even endanger human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of biologically modified composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Selection of non-metallic minerals: mix bentonite and barite in a ratio of 7:3;

[0026] (2) Drying and crushing: the non-metallic mineral raw materials are crushed to ≤5mm, and the raw materials enter the sorting machine for dry purification, and the non-metallic mineral raw materials with a taste of ≥85% are collected;

[0027] (3) The biosorbent is a mixture of corn stalks and coal ash, the particle size after mixing is controlled at 150 mesh, and the addition amount is 20%;

[0028] (4) Bacillus is selected as the biological bacteria;

[0029] (5) Bake the non-metallic minerals in an oven at 140°C for 10 hours, and bake the adsorbent in an oven at 80°C for 8 hours for sterilization;

[0030] (6) Cultivate the biological bacteria in the growth chamber at 30°C for 40 hours;

[0031] (7) The sterilized non-metallic minerals, adsorbent and biological bacteria are mixed in a ratio of 3:1:1 for biological bacteria immobilization;

[0032] (8) After the bio-control ...

Embodiment 2

[0036] (1) Selection of non-metallic minerals: mix bentonite, barite, and vermiculite in a ratio of 5:3:2;

[0037] (2) Drying and crushing: the non-metallic mineral raw materials are crushed to ≤5mm, and the raw materials enter the sorting machine for dry purification, and the non-metallic mineral raw materials with a taste of ≥85% are collected;

[0038] (3) The biosorbent is a mixture of corn stalks and coal ash, the particle size after mixing is controlled at 200 mesh, and the addition amount is 30%;

[0039] (4) Bacillus and Lactic acid streptococcus are selected as biological bacteria;

[0040] (5) Bake the non-metallic minerals in an oven at 140°C for 9 hours, and bake the adsorbent in an oven at 80°C for 6 hours for sterilization;

[0041] (6) The biological bacteria were cultured in the growth room at 30°C for 45 hours;

[0042] (7) The sterilized non-metallic minerals, adsorbent and biological bacteria are mixed in a ratio of 3:1:1 for biological bacteria immobiliz...

Embodiment 3

[0047] (1) Selection of non-metallic minerals: mix bentonite, barite, vermiculite and medical stone according to the ratio of 4:2:2:2;

[0048] (2) Drying and crushing: the non-metallic mineral raw materials are crushed to ≤5mm, and the raw materials enter the sorting machine for dry purification, and the non-metallic mineral raw materials with a taste of ≥85% are collected;

[0049] (3) The biosorbent is a mixture of corn stalks and coal ash, the particle size after mixing is controlled at 300 mesh, and the addition amount is 25%;

[0050] (4) Bacillus, Lactococcus and Lactococcus are selected as biological bacteria;

[0051] (5) Bake the non-metallic minerals in an oven at 140°C for 8 hours, and bake the adsorbent in an oven at 80°C for 7 hours for sterilization;

[0052] (6) The biological bacteria were cultured in the growth room at 30°C for 48 hours;

[0053] (7) The sterilized non-metallic minerals, adsorbent and biological bacteria are mixed in a ratio of 3:1:1 for biol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a biologically modified composite material. The biologically modified composite material is applied to the field of vegetable plant disease and insect pest prevention and treatment. Nonmetallic minerals are selected as raw materials, and are subjected to process processing of dry process purification, biocontrol bacterium screening, nonmetallic mineral mixture biocontrol bacterium fixation, granulation, drying and the like. The preparation method has the advantages that the raw materials are nonmetallic minerals; no toxicity and harmlessness aregenerated in the production process; no pollutant discharge can be realized; high efficiency, energy saving and environment protection are realized; green and harmless farm products can be produced; the economic value of the farm products is improved; meanwhile, the human body health is facilitated.

Description

technical field [0001] The invention relates to a preparation method of a biomodified composite material, which is used in the field of vegetable pest control. Background technique [0002] In the production of melons, fruits and vegetables, due to years of continuous cropping, blind fertilization, abuse of pesticides, and unreasonable field operations, the soil environment has deteriorated, leading to land compaction, severe pesticide residues, phytotoxicity, and repeated cropping diseases. Decrease, poor air permeability, reduced decomposition and reduction ability, and the yield and quality of fruits and vegetables have dropped significantly. In addition, in some areas, the awareness of environmental protection is weak and the dependence on chemical fertilizers is strong, which leads to the deterioration of the soil and serious water pollution, which leads to an increase in the incidence rate. Now the groundwater above 10 meters in the vast rural areas becomes astringent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C05G3/00C05G3/04C05F17/00C09K17/40C09K101/00C05G3/80
CPCY02W30/40
Inventor 王鸽赵旋杨智荣雷建斌徐光亮马亮陈雄祝李建
Owner 咸阳非金属矿研究设计院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com