Ultra-thin fabric making method

A production method and fabric technology, applied in the field of textile manufacturing, can solve the problems of inability to make ultra-thin fabrics, fail to meet the requirements of weaving strength, and low yarn strength, and achieve light and smooth texture, soft hand feeling and good skin-friendliness Effect

Inactive Publication Date: 2018-02-23
YUYUE HOME TEXTILE
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional finishing process of spinning and weaving cannot make ultra-thin fabrics, because the N10D nylon filament yarn is fine, which is equivalent to about 530 in the British system
The yarn strength is relatively low, and the single yarn strength is about 60CN, which cannot meet the strength requirements required for weaving.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-thin fabric making method
  • Ultra-thin fabric making method
  • Ultra-thin fabric making method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The example of the invention discloses a method for making an ultra-thin fabric, specifically:

[0020] Fabric gray cloth specification: (v80s+N10D)*(v80s+N10D)126*1401 / 1 plain weave.

[0021] Finished fabric specifications: N10D*N10D 140*1401 / 1 plain weave.

[0022] 1. Specifications and processes

[0023] (1) 1:1 non-elasticity core-spun yarn spinning process:

[0024] Preparation process of vinylon roving: vinylon fiber→cleaning→carding→drawing (3 parallels)→roving;

[0025] N10D (produced by Zhejiang Jiahua Special Nylon Co., Ltd.) nylon filament preparation:

[0026] Vinylon roving spinning process: spun bobbin→winding forming;

[0027] N10D filament spinning process: spun bobbin→winding forming

[0028] The spinning process indicators are shown in the table below:

[0029] project

Spinning frame speed

twist factor

Draft multiple

craft

5000 rpm

350

1.04

[0030] The yarn forming process indicators are shown in the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an ultra-thin fabric making method. The method comprises the steps of 1:1 non-elastic core spun yarn spinning process; weaving, wherein in the weaving process, a warp yarn opening forms an uneven shed, and upper layer warp yarns are made to be not on the same plane; aftertreatment vinylon-dissolving treatment which comprises swelling and dissolving, wherein vinylon-dissolving of a fabric is performed in overflowing equipment, the vinylon-dissolving temperature is 110 DEG C, the time is 25 min, the liquor ratio is about 30:1, and after vinylon-dissolving, the fabric iswashed to be clean with warm water of 40 DEG C and then cleaned with water of normal temperature and dried. The fabric made through the method is light as a thin wing, elegant, transparent, soft in hand feeding, light and smooth in texture, good in skin adaptability, high in yield and low in cost and slightly has silky luster.

Description

technical field [0001] The invention relates to the field of textile manufacturing, and relates to a special process of spinning and finishing, in particular to a method for making an ultra-thin fabric. Background technique [0002] The traditional finishing process of spinning and weaving cannot produce ultra-thin fabrics, because the N10D nylon filament yarn is fine, which is equivalent to about 530 in the British system. The yarn strength is relatively low, and the single yarn strength is about 60CN, which cannot meet the strength requirements required for weaving. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a method for making ultra-thin fabrics. In order to overcome the deficiencies of the prior art, it is considered to reduce the yarn count and improve the yarn strength, and at the same time, it is considered that the fabric is made into a finished yarn To restore the thread co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/36D06B3/10D03D15/283D03D15/47D03D15/50
CPCD02G3/36D06B3/10D10B2331/02D10B2321/06D03D15/47
Inventor 荣振银孙悦玲李强杨佳佳吕强强
Owner YUYUE HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap