Biomimetic collagen bone repair material with multilayer structure and preparation method thereof
A collagen bone and repair material technology, applied in tissue regeneration, medical science, prosthesis, etc., can solve problems such as inability to achieve bone structure, single structure, and low mechanical strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] Embodiment one, a kind of preparation method of the biomimetic collagen bone repair material with multi-layer structure, is characterized in that:
[0040] (1) Take a certain quality of pigskin-derived type I collagen, single-layer graphene oxide solids, and nano-hydroxyapatite solids and dissolve them in 0.1mol / L acetic acid solution, and use an ultrasonic probe to assist stirring for 30 minutes in an ice bath , the conditions of the ultrasonic stirring are: the power is 180w, the stirring intensity is 20-50%, and the content of type I collagen is 3wt%, the content of nano-hydroxyapatite is 3wt%, and the content of graphene oxide is 0.2wt%. The homogeneous A solution;
[0041] (2) Take a certain quality of type I collagen, single-layer graphene oxide solid, and nano-hydroxyapatite solid and dissolve them in 0.1mol / L acetic acid solution, and use an ultrasonic probe to assist stirring for 30 minutes in an ice bath, and the ultrasonic stirring The conditions are: the po...
Embodiment 2
[0047] Embodiment two, a kind of preparation method of biomimetic collagen bone repair material with multilayer structure, is characterized in that:
[0048] (1) Take a certain amount of source type I collagen, single-layer graphene oxide solid and nano-hydroxyapatite solid and dissolve them in 0.1mol / L acetic acid solution, and use an ultrasonic probe to assist stirring for 30min under an ice bath. The conditions of ultrasonic stirring are: the power is 180w, the stirring intensity is 50%, and the content of type I collagen is 2wt%, the content of nano-hydroxyapatite is 2wt%, and the content of graphene oxide is 0.2wt%. solution;
[0049] (2) Take a certain quality of type I collagen, single-layer graphene oxide solid, and nano-hydroxyapatite solid and dissolve them in 0.1mol / L acetic acid solution, and use an ultrasonic probe to assist stirring for 30 minutes in an ice bath, and the ultrasonic stirring The conditions are: the power is 180w, the stirring intensity is 50%, an...
PUM
Property | Measurement | Unit |
---|---|---|
elastic modulus | aaaaa | aaaaa |
elastic modulus | aaaaa | aaaaa |
elastic modulus | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap