Black TPU (thermoplastic polyurethane) full-shading film and application thereof

A polyurethane and full shading technology, which is applied in the field of polyurethane TPU black full shading film, can solve the problems that the appearance quality is not high enough, the function cannot be fully shading, and cannot be passed through, so as to achieve a uniform and consistent shading effect. Enhance demand, soft touch effect

Inactive Publication Date: 2018-04-03
浙江鸿圣纺织科技有限公司
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Common coated full blackout curtains cannot be passed in terms of environmental protection, and are not ideal products for washing and dry cleaning, and are easy to age and have a short service life.
Coated blackout curtains are coated on one side...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Example 1: A polyurethane TPU black full shading film is made of a masterbatch blown film made of 74% polyurethane TPU, 18% carbon black and 8% chrome black powder, and its thickness is 0.8~ 5 filaments, with a width of 500-3300 cm, the coloring degree of the carbon black is 140%, and the fluidity is 26-28.

Embodiment 2

[0011] Example 2: The polyurethane TPU black full shading film described in Example 1 was applied to the curtain fabric, and was pasted between the curtain fabric surface and the bottom through PUR hot melt adhesive or PU glue. Choose 70g Chunyang Fleece and the required surface cloth, and stick the TPU polyurethane black full shading film in the middle with PUR hot-melt adhesive. The curtains made are soft and drapey. Using polyurethane black full shading film, the double-sided composite curtain fabric with hot melt adhesive can achieve 100% shading, 100% washable and dry cleaning, 100% environmental protection, and can withstand strong sunlight in summer and reduce indoor temperature, keeping warm and moisturizing in winter.

Embodiment 3

[0012] Example 3: The polyurethane TPU black full light-shielding film described in Example 1 was applied to the tent and the sunshade cloth, which has good waterproof performance and can be breathable and watertight. The characteristics of polyurethane black shading film, summer waterproof shading and strong light exposure, TPU black full shading film is made on the product, which has the function of absorbing light, not reflecting but not transmitting light, cooling, and playing the effect of waterproof, heat preservation and moisturizing in winter. Therefore, it is just right to use it on tent shade cloth.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a black TPU (thermoplastic polyurethane) full-shading film and an application thereof. The black TPU full-shading film is prepared from 74% of TPU, 18% of carbon black and 8% of black copper-chromium powder through masterbatch film blowing and has the thickness of 0.8-5 dmm and the width of 500-3,300 cm. The prepared product touches very soft, has good waterproof performance and breathability, can keep warm and moisture and resist stronger sunlight and infrared radiation and is good in shading, resistant to water washing and dry cleaning and environmentally friendly.

Description

technical field [0001] The invention relates to a light-shielding film and its application, in particular to a polyurethane TPU black full light-shielding film and its application. Background technique [0002] At present, all shading products are formed by multiple coatings or woven with black shading silk in the middle. Common coated full blackout curtains cannot be approved in terms of environmental protection, and they are not ideal products for washing and dry cleaning, and they are easy to age and have a short service cycle. Coated full blackout curtains are coated on one side and fabric on the other, and the quality of the appearance is not high enough. Curtain products with black shading silk in the middle of weaving, namely woven shading curtains, have high gram weight, high cost, and cannot achieve full shading. SUMMARY OF THE INVENTION [0003] The technical problem to be solved by the present invention is to provide a polyurethane TPU black full shading film ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K3/04C08K3/22C08L75/04B29C55/28A47H23/10B32B7/12B32B27/40B32B27/06
CPCA47H23/10B29C55/28B32B7/12B32B27/06B32B27/40B32B2307/724B32B2307/7265B32B2437/00B32B2601/00C08J5/18C08J7/06C08J2375/04C08J2375/06C08J2375/08C08K3/04C08K3/22C08L2203/16C08L75/04
Inventor 张文学
Owner 浙江鸿圣纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap